Archives of Foundry Engineering | 2018 | vol.18 | No 1

Download PDF Download RIS Download Bibtex

Abstract

This article discusses results of an analysis of mechanical properties of a sintered material obtained from a mixture of elemental iron, copper and nickel powders ball milled for 60 hours. The powder consolidation was performed by hot pressing in a graphite mould. The hot pressing was carried out for 3 minutes at 900 °C and under a pressure of 35 MPa. The sintered specimens were tested for density, porosity, hardness and tensile strength. Their microstructures and fracture surfaces were also examined using a scanning electron microscope (SEM). The study was conducted in order to determine the suitability of the sintered material for the manufacture of metal-bonded diamond tools. It was important to assess the effects of chemical composition and microstructure of the sintered material on its mechanical properties, which were compared with those of conventional metal bond material produced from a hot-pressed SMS grade cobalt powder. Although the studied material shows slightly lower strength and ductility as compared with cobalt, its hardness and offset yield strength are sufficiently high to meet the criteria for less demanding applications.

Go to article

Authors and Affiliations

J. Lachowski
J.M. Borowiecka-Jamrozek
J. Konstanty
Download PDF Download RIS Download Bibtex

Abstract

This article discusses issues related to continuous casting of brass. The tested material was CuZn39Pb2 brass with the use of continuous casting and different parameters of the process. The position consists of a melting furnace with a graphite refining pot of about 4000 cm3 chuting capacity, a graphite crystallizer of 9,5 mm nominal diameter, a primary and secondary cooling system and an extracting system as well. The analysis was carried out in terms of technological parameters of the process and type of charge. Highlighted: feedrate ingot, number of stops, and technological temperatures. The surface quality of the obtained ingots and the structure were analyzed. The most favorable conditions were indicated and technological recommendations indicated. They have been distinguished for ingots for plasticity and other technologies. Favorable casting conditions are low feed and low temperature. Due to the presence of impurities coming from the charge it is disadvantageous to have Ni greater than 0.053% by mass, and Fe more than 0.075% by mass. It is recommended to maintain a high zinc content in the melt which is associated with non-overheating of the metal during casting and earlier melting.

Go to article

Authors and Affiliations

P. Kwaśniewski
K. Najman
W. Wołczyński
A.W. Bydałek
P. Schlafka
Download PDF Download RIS Download Bibtex

Abstract

Energy conservation is an important step to overcome the energy crisis and prevent environmental pollution. Casting industry is a major consumer of energy among all the industries. The distribution of electrical energy consumed in all the departments of the foundry is presented. Nearly 70% of the energy is consumed especially in the melting department alone. Production of casting involves number of process variables. Even though lot of efforts has been taken to prevent defects, it occurs in the casting due to variables present in the process. This paper focuses the energy saving by improving the casting yield and by reducing the rejections. Furthermore an analysis is made on power consumption for melting in the induction furnace to produce defective castings and improvement in the casting yield. The energy consumed to produce defective castings in all other departments is also presented. This analysis reveals that without any further investment in the foundry, it is possible to save 3248.15 kWh of energy by reducing the rejections as well as by improving the casting yield. The redesign of the feeding system and the reduced major rejection shrinkage in the body casting improved the casting yield from 56% to 72% and also the effective yield from 12.89% to 66.80%.

Go to article

Authors and Affiliations

B. Chokkalingam
V. Raja
M. Dhineshkumar
M. Priya
R. Immanual
Download PDF Download RIS Download Bibtex

Abstract

In the knock-out process, as well as in the preliminary phase of moulding sand reclamation, the issue of energy demand for the process of crushing used sand agglutinations, preferably to single grains, is particularly important. At present, numerical values of moulding sand impact resistance, which would allow energy-related aspects of this process to be forecast, are not known, as such research has not been carried out. It seems that impact resistance tested on very small cross-section samples, which allows us to very precisely reveal some unique features of a moulding sand with organic and inorganic binders, is an important parameter, which so far has not been taken into account for evaluation of mechanical properties of moulding sands. Preliminary attempts to determine impact resistance of moulding sands have been carried out as part of own research of the author. The conducted investigations aimed at determining the relationships between the obtained values of tensile strength and impact resistance of moulding sands. In addition, the effect of holding samples at temperatures of 100oC, 200oC, 300oC on the value of impact resistance was determined, both for sands made with fresh and with reclaimed sand grains.

Go to article

Authors and Affiliations

R. Dańko
G. Dajczer
Download PDF Download RIS Download Bibtex

Abstract

The paper presents a detailed description of one of the newest methods of vacuum saturation of reinforcing preforms in gypsum molds. As an appropriate selection of the infiltration time is a crucial problem during realization of this process, aim of the analysis shown in the paper is to present methods of selection of subatmospheric pressure application time, a sequence of lowering and increasing pressure, as well as examining influence of structure of reinforcing preforms on efficiency of this process. To realize the aim, studies on infiltration of reinforcing preforms made of a corundum sinter of various granulation of sintered particles with a model alloy were conducted. The infiltration process analysis was carried out in two stages. The first stage consisted in investigation of influence of lengthening of sucking off air from the reinforcing preforms on efficiency of this process. In the second stage, an analysis of influence of a two-staged infiltration process on saturation of the studied materials was conducted. Because the studied preforms were of similar porosity, the obtained differences of the saturation level of particular preforms have shown, that the saturation process is influenced mostly by size of pores present in the reinforcement. Because of these differences, each reinforcement type requires individual selection of time and sequence of the saturation process. For reinforcements of higher pore diameter, it is sufficient to simply increase air sucking off time to improve the saturation, while for reinforcement of smaller pore diameter, it is a better solution to apply the two-staged process of sucking off air. Application of the proposed analysis method allows not only obtaining composite castings of higher quality, but also economical optimization of the whole process.

Go to article

Authors and Affiliations

K. Gawdzińska
D. Nagolska
P. Szymański
Download PDF Download RIS Download Bibtex

Abstract

The determination of the form of a probability density function (PDF3) of diameters for nodular particles by using a probability density function (PDF2), which form is empirically estimated from cross-sections of these nodules in a metallographic specimen, can be regarded as a special case of Wicksell's corpuscle problem (WCP). The estimation of the PDF3 for the nodular particles provides information about the kinetics of these particles nucleation, and so about the kinetics of their growth. This information is essential for building more accurate mathematical models of the alloy crystallization. In the paper there are presented two derivations of the methods used for the estimation of the PDF3 form. The first method bases on diameters received from a planar cross-section. The second one uses also data from the planar cross-section but not the diameters only chords. Both methods provide practical rules for the analysis of the empirical diameters’ and chord’s size distribution and allow to estimate the mean value of the external surface area of the particles.

Go to article

Authors and Affiliations

D. Gurgul
A. Burbelko
T. Wiktor
Download PDF Download RIS Download Bibtex

Abstract

The article presents an example of analysis of the influence of selected parameters deriving from data acquisition in foundries on the occurrence of Gas porosity defects (detected by Visual testing) in castings of ductile cast iron. The possibilities as well as related effectiveness of prediction of this kind of defects were assessed. The need to rationally limit the number of possible parameters affecting this kind of porosity was indicated. Authors also benefited from expert group's expertise in evaluating possible causes associated with the creation of the aforementioned defect. A ranking of these parameters was created and their impact on the occurrence of the defect was determined. The classic statistical tools were used. The possibility of unexpected links between parameters in case of uncritical use of these typical statistical tools was indicated. It was emphasized also that the acquisition realized in production conditions must be subject to a specific procedure ordering chronology and frequency of data measurements as well improving the casting quality control. Failure to meet these conditions will significantly affect the difficulties in implementing and correcting analysis results, from which INput/OUTput data is expected to be the basis for modelling for quality control.

Go to article

Authors and Affiliations

Z. Ignaszak
R. Sika
M. Rogalewicz
Download PDF Download RIS Download Bibtex

Abstract

Measurements of the hardening process course of the selected self-hardening moulding sands with the reclaimed material additions to the matrix, are presented in the hereby paper. Moulding sands were produced on the „Szczakowa” sand (of the Sibelco Company) as the matrix of the main fraction FG 0,40/0,32/0,20, while the reclaim was added to it in amounts of 20, 50 and 70%. Regeneration was performed with a horizontal mechanical regenerator capacity of 10 t/h. In addition, two moulding sands, one on the fresh sand matrix another on the reclaimed matrix, were prepared for comparison. Highly-fluid urea-furfuryl resin was used as a binder, while paratoluensulphonic acid as a hardener. During investigations the hardening process course was determined, it means the wave velocity change in time: cL = f(t). The hardening process kinetics was also assessed (dClx/dt = f(t)). Investigations were carried out on the research stand for ultrasound tests. In addition strength tests were performed.

Go to article

Authors and Affiliations

Ł. Jamrozowicz
J. Kolczyk
P. Wojtuń
Download PDF Download RIS Download Bibtex

Abstract

The problem of production flow in steel casting foundry is analysed in this paper. Because of increased demand and market competition, a reorganisation of the foundry process is required, including the elimination of manual labour and the implementation of automation and robotisation of certain processes. The problem is how to determine the real difference in work efficiency between human workers and robots. We show an analysis of the production efficiency of steel casting foundry operated by either human operators or industrial robots. This is a problem from the field of Operations Research for which the Discrete Event Simulation (DES) method is used. Three models are developed, including the foundry before and after automation when taking into consideration parameters of the availability of machines, operators and robots. We apply the OEE (Overall Equipment Effectiveness) indicator to present how the availability, performance and quality parameters influence the foundry’s productivity. In addition, stability of the simulation model was analysed. This approach allows for a better representation of real production processes and the obtained results can be used for further economic analysis.

Go to article

Authors and Affiliations

A. Kampa
G. Gołda
Download PDF Download RIS Download Bibtex

Abstract

High prices of tin and its limited resources, as well as several valuable properties characterising Cu-Sn alloys, cause searching for materials of similar or better properties at lower production costs. The influence of various nickel additions to CuSn10 casting bronze and to CuSn8 bronze of a decreased tin content was tested. Investigations comprised melting processes and casting of tin bronzes containing various nickel additions (up to 5%). The applied variable conditions of solidification and cooling of castings (metal and ceramic moulds) allowed to assess these alloys sensitivity in forming macro and microstructures. In order to determine the direction of changes in the analysed Cu-Sn-Ni alloys, the metallographic and strength tests were performed. In addition, the solidification character was analysed on the basis of the thermal analysis tests. The obtained results indicated the influence of nickel in the solidification and cooling ways of the analysed alloys (significantly increased temperatures of the solidification beginning along with increased nickel fractions in Cu-Sn alloys) as well as in the microstructure pattern (clearly visible grain size changes). The hardness and tensile strength values were also changed. It was found, that decreasing of the tin content in the analysed bronzes to which approximately 3% of nickel was added, was possible, while maintaining the same ultimate tensile strength (UTS) and hardness (HB) and improved plasticity (A5).

Go to article

Authors and Affiliations

M. Perek-Nowak
J. Kozana
M. Piękoś
A. Garbacz-Klempka
E. Czekaj
Download PDF Download RIS Download Bibtex

Abstract

The paper proposes a new electropulse apparatus for processing natural raw materials. The temperature of the crushing-and-reducing assembly of an electropulse plant is found. The results of ore crushing are presented and optimal engineering factors are offered. The elemental analysis of the test material is obtained. It is reported that the electropulse processing at the reduction stage made for significant increase in the content of non-ferrous and rare metals.

Go to article

Authors and Affiliations

B.R. Nussupbekov
A.K. Khassenov
D.Zh. Karabekova
I.P. Kurytnik
A.Sh. Kazhikenova
Download PDF Download RIS Download Bibtex

Abstract

The thermal reclamation process as a utilisation method of spent moulding and core sands is more costly than other reclamation methods, but in the majority of cases it simultaneously provides the best cleaning of mineral matrices from organic binders. Thus, the application of the thermal analysis methods (TG-DSC), by determining the temperature range within which a degradation followed by a destruction of bounded organic binders in moulding sands, can contribute to the optimisation of the thermal reclamation process and to the limiting its realisation costs. The thermal analysis results of furan resin, one of the most often applied binder in foundry practice, are presented in the hereby paper. The influence of the heating rate of the sample - placed in the thermal analyser - on its degradation and destruction process under oxygen-free (argon) and oxygen (air) conditions, were compared. The recorded TG and DSC curves were used for analysing these processes as the temperature as well as the time function. The obtained results were analysed with regard to determining the required temperature of the thermal reclamation of the investigated organic binder. The usefulness of the developed methodology was found out, however under conditions of meeting several essential requirements concerning the repeatability of performed analyses.

Go to article

Authors and Affiliations

M. Łucarz
Download PDF Download RIS Download Bibtex

Abstract

Bimetallic AZ91/AlSi17 samples were produced by compound casting. The casting process involved pouring the AZ91 magnesium alloy heated to 650oC onto a solid AlSi17 aluminum alloy insert placed in a steel mould. Prior to casting, the mould with the insert inside was heated to about 370oC. The bonding zone formed between AZ91 and AlSi17 had a thickness of about 200 μm; it was characterized by a non-homogeneous microstructure. Two different areas were distinguished in this zone: the area adjacent to the AZ91 and the area close to the AlSi17. In the area closest to the AZ91 alloy, a eutectic composed of an Mg17Al12 intermetallic phase and a solid solution of Al in Mg was observed. In bonding zone at a certain distance from the AZ91 alloy an Mg2Si phase co-occurred with the eutectic. In the area adjacent to the AlSi17 alloy, the structure consisted of Al3Mg2, Mg17Al12 and Mg2Si. The fine Mg2Si phase particles were distributed over the entire Mg-Al intermetallic phase matrix. The microhardness of the bonding zone was much higher than those of the materials joined; the microhardness values were in the range 203-298 HV. The shear strength of the AZ91/AlSi17 joint varied from 32.5 to 36 MPa.

Go to article

Authors and Affiliations

R. Mola
T. Bucki
Download PDF Download RIS Download Bibtex

Abstract

The present paper is a presentation of results of a study on morphology, chemical composition, material properties (HVIT, HIT, EIT), and nanoindentation elastic and plastic work for carbide precipitates in chromium cast iron containing 24% Cr. It has been found that the carbides differ in chemical composition, as well as in morphology and values characterizing their material properties. The carbides containing the most chromium which had the shape of thick and long needles were characterized with highest values of the analyzed material properties.

Go to article

Authors and Affiliations

A.W. Orłowicz
M. Mróz
M. Tupaj
A. Trytek
M. Jacek
M. Radoń
Download PDF Download RIS Download Bibtex

Abstract

This paper presents initial findings from research into the possibility of using gypsum binders in quartz moulding sand that could be used in the production of casting moulds and cores. For the purposes of the research two commercial types of gypsum were used as binders: building gypsum and gypsum putty. Dry components of moulding sand i.e. medium quartz sand and gypsum were mixed in proportion of 89/11 parts by weight. In order to achieve bonding properties for the binders, 5 parts by weight of water was added to the mixture of dry components. After 24 hours of adding water and mixing all the components, the moulding sand, naturally hardened, was subjected to high temperature. The moulding sand thus produced, i.e. with cheap and environmentally-friendly gypsum binders, was eventually analysed after heating (at temperatures of 300oC, 650oC and 950oC) and cooling in order to determine changes in the following parameters: LOI – loss on ignition, chemical composition and pH. Moreover, investigated were bonding bridges, before and after the moulding sand was roasted. The research results revealed differences in the structure of bonding bridges and the occurrence of automatic adhesive destruction for both types of gypsum binders. For two types of moulding sands under the investigation of the LOI exceeded 2.59wt.% (with building gypsum) or 2.84wt.% (with putty gypsum) and pH increased to ca. 12 as a result of increasing roasting temperature from 300oC to 650oC. Next, roasting at 950oC decrease value of LOI in both types of moulding sands. Moulding sand with builoding gypsum roasted at 950oC revealed a return to the value of pH parameter measured prior to annealing.

Go to article

Authors and Affiliations

M. Stachowicz
P. Paduchowicz
K. Granat
Download PDF Download RIS Download Bibtex

Abstract

The article presents the study results of Sn-Zn lead-free solders with the various Zn content. The results concern the hypoeutectic, eutectic and hypereutectic alloys containing respectively 4.5% Zn, 9% Zn and 13.5% Zn. Moreover, these alloys contain the constant Ag (1%) addition. The aim of the study was to determine the microstructural conditionings of their fatigue life. In particular it was focused on answer the question what meaning can be assigned to the Ag addition in the chemical composition of binary Sn-Zn alloys. The research includes a qualitative and quantitative assessments of the alloy microstructures, that have been carried out in the field of light microscopy (LM). In order to determine some geometrical parameters of the microstructure of alloys the combinatorial method based on the phase quanta theory was applied. Moreover, for the identification necessities the chemical analyses in the micro-areas by SEM/EDS technics were also performed. Based on the SEM/EDS results the phases and intermetallic compounds existing in the examined lead-free solders were identified. The mechanical characteristics were determined by means of the modified low cycle test (MLCF). Based on this method and on the results obtained every time from only one sample the dozen of essential mechanical parameters were evaluated. The research results were the basis of analyzes concerning the effects of microstructural geometrical parameters of lead-free alloys studied on their fatigue life at ambient temperature.

Go to article

Authors and Affiliations

M. Maj
A. Wojciechowski
K. Pietrzak
A. Klasik
N. Sobczak
Download PDF Download RIS Download Bibtex

Abstract

The article presents the investigation results of the crystallization (performed by means of the TDA method) and the microstructure of complex aluminium bronzes with the content of 6% Al, 4% Fe and 4% Ni, as well as Si additions in the scope of 1–2% and Cr additions in the scope of 0.1–0.3%, which have not been simultaneously applied before. For the examined bronze, the following tests were performed: hardness HB, impact strength (KU2). For bronze CuAl6Fe4Ni4Si2Cr0.3, characterizing in the highest hardness, wear tests were conducted with dry friction and the dry friction coefficient. The investigations carried out by means of the X-ray phase analysis demonstrated the following phases in the microstructure of this bronze: αCu, γ2 and complex intermetallic phases based on iron silicide type Fe3Si (M3Si M={Fe,Cr,…}). Compared to the normalized aluminium bronzes (μ=0.18–0.23), the examined bronze characterizes in relatively low wear and lower friction coefficient during dry friction (μ=0.147±0.016).

Go to article

Authors and Affiliations

B.P. Pisarek
B. Kowalski
H. Atapek
Ş. Polat
T. Tüfekçi
Download PDF Download RIS Download Bibtex

Abstract

The paper presents an innovative method of creating the layered castings. The innovation relies on application the 3D printing insert obtaining in SLM (selective laser melting) method. This type of scaffold insert made from pure Ti powder, was placed into mould cavity directly before pouring by grey cast iron. In result of used method was obtained grey cast iron casting with surface layer reinforced by titanium carbides. In range of studies were carried out metallographic researches using light microscope and scanning electron microscope, microhardness measurements and abrasive wear resistance. On the basis of obtaining results was stated that there is a possibility of reinforcing surface layer of the grey cast iron casting by using 3D printing scaffold insert in the method of mould cavity preparation. Moreover there was a local increase in hardness and abrasive wear resistance in spite of the precipitation of titanium carbides in surface layer of grey cast iron. While the usable properties of composite surface layer obtained in result of use of the method presented in the paper, strongly depend of dimensions of scaffold insert, mainly parameters Re and Ri.

Go to article

Authors and Affiliations

A. Dulska
J. Szajnar
N. Przyszlak
T. Wróbel
Download PDF Download RIS Download Bibtex

Abstract

Castability of thin-walled castings is sensitive to variation in casting parameters. The variation in casting parameters can lead to undesired casting conditions which result in defect formation. Variation in rejection rate due to casting defect from one batch to other is common problem in foundries and the cause of this variation usually remain unknown due to complexity of the process. In this work, variation in casting parameters resulting from human involvement in the process is investigated. Casting practices of different groups of casting operators were evaluated and resulting variations in casting parameters were discussed. The effect of these variations was evaluated by comparing the rejection statistics for each group. In order to minimize process variation, optimized casting practices were implemented by developing specific process instructions for the operators. The significance of variation in casting parameters in terms of their impact on foundry rejections was evaluated by comparing the number of rejected components before and after implementation of optimized casting practices. It was concluded that variation in casting parameters due to variation in casting practices of different groups has significant impact on casting quality. Variation in mould temperature, melt temperature and pouring rate due to variation in handling time and practice resulted in varying quality of component from one batch to other. By implementing the optimized casting instruction, both quality and process reliability were improved significantly.

Go to article

Authors and Affiliations

M. Raza
P. Silva
M. Irwin
B. Fagerström
A.E.W. Jarfors
Download PDF Download RIS Download Bibtex

Abstract

The results of investigations of three commercial binders applied in the Alphaset technology marked as: Sample E , Sample T and Sample S are presented in the hereby paper. These samples were subjected to the pyrolysis process at a temperature of 900°C (inert atmosphere, He 99.9999). The gas chromatograph coupled with the mass spectrometer and pyrolizer (Py-GC/MS) were used in the study. The identification of gases emitted during the thermal decomposition was performed on the basis of the mass spectral library. The obtained results indicate a certain diversification of emitted gases. Among the pyrolysis products the following harmful substances were identified: furfuryl alcohol, formaldehyde, phenol and also substances from the BTEX (benzene, toluene and ethylobezneze and xylenes) PAHs (Polycyclic Aromatic Hydrocarbons) and VOC groups (Volatile Organic Compounds). Therefore, from the environment protection point of view performing systematic investigations concerning the harmfulness of binders applied in the moulding and core sands technology, is essential.

Go to article

Authors and Affiliations

A. Roczniak
M. Holtzer
A. Kmita
Download PDF Download RIS Download Bibtex

Abstract

In this paper, the mathematical model and numerical simulations of the molten steel flow by the submerged entry nozzle and the filling process of the continuous casting mould cavity are presented. In the mathematical model, the temperature fields were obtained by solving the energy equation, while the velocity fields were calculated by solving the momentum equations and the continuity equation. These equations contain the turbulent viscosity which is found by solving two additional transport equations for the turbulent kinetic energy and its rate of dissipation. In the numerical simulations, coupling of the thermal and fluid flow phenomena by changes in the thermophysical parameters of alloy depending on the temperature has been taken into consideration. This problem (2D) was solved by using the finite element method. Numerical simulations of filling the continuous casting mould cavity were performed for two variants of liquid metal pouring. The effect of the cases of pouring the continuous casting mould on the velocity fields and the solid phase growth kinetics in the process of filling the continuous casting mould was evaluated as these magnitudes have an influence on the high quality of the continuous cast steel slab.

Go to article

Authors and Affiliations

L. Sowa
T. Skrzypczak
P. Kwiatoń
Download PDF Download RIS Download Bibtex

Abstract

Cast high-manganese Hadfield steel is commonly used for machine components operating under dynamic load conditions. Their high fracture toughness and abrasive wear resistance is the result of an austenitic structure, which - while being ductile - at the same time tends to surface harden under the effect of cold work. Absence of dynamic loads (e.g. in the case of sand abrasion) causes rapid and premature wear of parts. In order to improve the abrasive wear resistance of cast high-manganese steel for operation under the conditions free from dynamic loads, primary titanium carbides are produced in this cast steel during melting process to obtain in castings, after melt solidification, the microstructure consisting of an austenitic matrix and primary carbides uniformly distributed therein. After heat treatment, the microhardness of the austenitic matrix of such cast steel is up to 580 μHV20 and the resulting carbides may reach even 4000 μHV20. The impact strength of this cast steel varies from 57 to 129 and it decreases with titanium content. Compared to common cast Hadfield steel, the abrasive wear resistance determined in Miller test is at least twice as high for the 0.4% Ti alloy and continues growing with titanium content.

Go to article

Authors and Affiliations

R. Zapała
G. Tęcza
Download PDF Download RIS Download Bibtex

Abstract

Fe - 4,25% C alloy was directionally solidified with a constant temperature gradient of G = 33,5 K/mm and growth rate of v = 83,3 μm/s (300 mm/h) using a vacuum Bridgman-type crystal growing facility with liquid metal cooling technique. To reveal more detailed microstructure, the deep etching was made. This was obtained in the process of electrolytic dissolution. The microstructure of the sample was examined on the longitudinal and transverse sections using an Optical Microscope and Scanning Electron Microscope. Using the Electron Backscattered Diffraction technique, phase map and analysis of phase were made. In this paper the analysis of Fe-C alloy eutectic microstructure is presented. Regular eutectic structure was obtained. The fracture surfaces show lamellar structure. Microscopic observation after electrolytic extraction indicates that the grains of longitudinal shape of eutectic cementite have been obtained. These grains are characterized by layered construction with many rounded discontinuities.

Go to article

Authors and Affiliations

M. Trepczyńska-Łent
Download PDF Download RIS Download Bibtex

Abstract

In this paper, the authors investigated the size distribution of titanium oxide (TiO2), titanium nitride (TiN) and titanium carbide (TiC) inclusions in a titanium deoxidized 4130 steel and compared it with the 4130 base alloy composition inclusions. TiN and TiC inclusions are of particular interest due to their role as heterogeneous nuclei for various phase reactions in steels. Two types of samples were prepared, a polished sample and a filtered sample. Electrolytic dissolution was employed to make the filter paper samples. The size range of titanium inclusions was found to be more than that of the non-metallic inclusions from 4130 base alloy heat. Titanium inclusions from the filter and polished samples were round in shape. TiC and TiN inclusions were not found in the electrolytic extraction samples. Inclusions and their chemistries were analyzed using scanning electron microscope and energy dispersive spectrometer. The inclusion size range was larger for the titanium deoxidized samples than the base alloy. However, in both steels the majority of inclusions had a size smaller than 10 μm.

Go to article

Authors and Affiliations

R.B. Tuttle
S. Kottala
Download PDF Download RIS Download Bibtex

Abstract

Al-4.5Cu alloys are widely used in aerospace industries due to their low weight and high mechanical properties. This group of aluminium alloys is known as 2xx series and exhibits the highest mechanical properties however this alloy is known to suffer from feedability and high tendency for hot tearing. Al-Si alloys (3xx) have improved fluidity and better feedability particularly by several modifications such as Ti, B or Sr. Eutectic temperature is decreased and mechanical properties can be enhanced. Yet, the strength values of this alloy group cannot reach the values of 2xx series. Therefore, in this study, the effect of Ag addition on the fluidity of Al-4.5Cu alloy has been investigated. Standard size spiral mould was used. The casting temperature was selected to be 770oC. Five castings were made and Weibull statistical approach was used to evaluate the results. In addition, coating of the die with BN was also investigated. It was found that Ag addition and BN coating of the die revealed the most reproducible, reliable and high fluidity values.

Go to article

Authors and Affiliations

K. Yildirim
M. Helvaci
Ö. Gürsoy
E. Erzi
C. Kahruman
D. Dispinar
Download PDF Download RIS Download Bibtex

Abstract

The results of castability and structures researches of two nickel base alloys - Ceranium CN and Magnum AN applied on casting of the crowns and dental bridges are presented. Studies were carried out on the alloys cast under the centrifugal force to the moulds made by the lost wax method using production line of ROKO. Having regard to a specific technology of casting and possibility of ROKO production line, to the estimation of alloys castability a spiral test was adjusted with a 0,8 mm and a 2,5 mm diameter of test casting. Measuriements executed on a 20 test castings allowed to establish, that castability of Magnum AN alloy was 65 % greater than castability of Ceranium NC alloy. The results of thermodynamics calculations of the equilibrium and nonequilibrium crystallization (Scheil model) of the investigated alloys are presented too. The characteristic temperatures of phase transformation and forecast phase composition of alloys for both kind of crystallization were calculated. It is established after structural supervisions, that the investigated alloys crystallize in dendryte form and in centrifugal casting conditions have cooling rate sensivity and inclination to texture structure forming in outmost layer of casting. Phase composition of alloys corresponds to the results of thermodynamics calculations of the nonequilibrium crystallization conditions.

Go to article

Authors and Affiliations

Z. Konopka
M. Łągiewka
A. Zyska
P. Kordas
Download PDF Download RIS Download Bibtex

Abstract

The article presents the results of selected energy parameters calculations, carried out for the recorded values of instantaneous voltages and currents in the three-phase power supply of the model vibratory unit. The parameters were the values of active and apparent power taken from the drive consisting of two electric motors supplied by the inverter for selected frequency settings and directly from the power grid. In addition, calculations of tgφ power factor values were made to evaluate the compensation of reactive power consumption in the tested power systems. Measurements and calculations lead to the conclusion that if the frequency of the inverter output voltage rises, the active and apparent power consumed by the model vibratory drive unit increases. The active and apparent power for setting the output frequency of the inverter from 50 Hz was less than the active and apparent power taken by the model vibratory unit that was powered directly from the power grid. The power factor tgφ in the power supply system was approximately 6, except one case (f = 30 Hz).

Go to article

Authors and Affiliations

E. Ziółkowski
M. Skrzyński
Download PDF Download RIS Download Bibtex

Abstract

In many foundries, the requirements placed on castings production have risen mainly over the few years. Further trends in recent years have been the ever increasing level of automation and introduction of new alloys, especially composites. On the other hand, the foundry environment has become increasingly difficult because is used many organic binders. Environmental regulations will be further tightened up. These processes are pursued at national, European and global level. Conformity with emission limits is becoming increasingly difficult. The problem is emission of aromatic hydrocarbons, phenol, odours and other harmful compounds to environment. The main purpose of many companies is reduction of this toxins. The new cold-box systems (based on phenolic resins) try to reduce the emission by introducing into the resin structure silicate modifiers. Research presented of this article evaluate the effectiveness of these methods. The results show comparison of two resins ("without" and "with" silicate modifier) for assessment of emission of harmful aromatic hydrocarbons and phenol.

Go to article

Authors and Affiliations

S. Żymankowska-Kumon
B. Grabowska
A. Bobrowski
D. Drożyński
K. Kaczmarska
Download PDF Download RIS Download Bibtex

Abstract

The constant growth of foundry modernization, mechanization and automation is followed with growing requirements for the quality and parameters of both moulding and core sands. Due to this changes it is necessary to widen the requirements for the parameters used for their quality evaluation by widening the testing of the moulding and core sands with the measurement of their resistance to mechanical deformation (further called elasticity). Following article covers measurements of this parameter in chosen moulding and core sands with different types of binders. It focuses on the differences in elasticity, bending strength and type of bond destruction (adhesive/cohesive) between different mixtures, and its connection to the applied bonding agent. Moulding and cores sands on which the most focus is placed on are primarily the self-hardening moulding sands with organic and inorganic binders, belonging to the group of universal applications (used as both moulding and core sands) and mixtures used in cold-box technology.

Go to article

Authors and Affiliations

St.M. Dobosz
A. Grabarczyk
K. Major-Gabryś
J. Kusiński
Download PDF Download RIS Download Bibtex

Abstract

This paper shows how it is possible to obtain an ausferrite in compacted graphite iron (CGI) without heat treatment of castings. Vermicular graphite in cast iron was obtained using Inmold technology. Molybdenum was used as alloying additive at a concentration from 1.6 to 1.7% and copper at a concentration from 1 to 3%. It was shown that ausferrite could be obtained in CGI through the addition of molybdenum and copper in castings with a wall thickness of 3, 6, 12 and 24 mm. Thereby the expensive heat treatment of castings was eliminated. The investigation focuses on the influence of copper on the crystallization temperature of the graphite eutectic mixture in cast iron with the compacted graphite. It has been shown that copper increases the eutectic crystallization temperature in CGI. It presents how this element influences ausferrite microhardness as well as the hardness of the tested iron alloy. It has been shown that above-mentioned properties increases with increasing the copper concentration.

Go to article

Authors and Affiliations

G. Gumienny
B. Kacprzyk
Download PDF Download RIS Download Bibtex

Abstract

The impact of casting conditions on microstructure a and mechanical properties was described, especially for cast products from AlSi9Cu3 alloy. Particular attention was paid to the parameters of dendritic structure: DAS 1 and DAS 2. Selected mechanical properties (by static tension test) of test castings made using basic technologies of casting: GSC - gravity sand casting, GDC - gravity die-casting and HPDC - high-pressure die-casting, are presented for cast-on test bars and cast separately. Casts were made of the same alloy AlSi9Cu3. Fractures and the zone near the fracture (after static tension test) was subjected to VT - visual tests, PT - penetration tests and metallographic tests. The condition of porosity (fracture zone) was also assessed. The analysis of virtual results was performed using the NovaFlow & Solid system together with the database and they were compared to experimental tests. This way of validation was applied in order to assess the correlation between the local rate of cooling and the size of DAS for GSC, GDC and HPDC technologies. Finally, the correlation between the parameters of structure and mechanical properties with regard to the impact of porosity was signalized.

Go to article

Authors and Affiliations

J. Hajkowski
Z. Ignaszak
Download PDF Download RIS Download Bibtex

Abstract

The paper presents the effect of pre-heat treatment on the mechanical properties of ductile cast iron with elevated content of Cu and Mo elements. Austempered Ductile Iron is a material with non-standard properties, combining high tensile strength and abrasion resistance with very good plasticity. In addition, it is prone to strain hardening and have good machining abilities. The study was conducted for five designed heat treatment cycles. The variables were the time and temperature of the pre-heat treatment, followed by one of two standard heat treatments for ADI cast iron. The aim of the authors was fragmentation of the grains of perlite during the initial heat treatment. It is presumed, that subsequent heat treatment will cause further refinement of the microstructure than would be the case without initial heat treatment. Diffusion is much faster than in case of ferritic matrix of cast iron. The results will be used to evaluate material for the production of parts of equipment that must operate under extreme load conditions.

Go to article

Authors and Affiliations

P. Nawrocki
K. Łukasik
K. Wasiluk
D. Myszka
Download PDF Download RIS Download Bibtex

Abstract

As-cast Mg-6Li-0.3Zn-0.6Y and Mg-6Li-1.2Zn-1.2Y (wt%) alloys were prepared and extruded at 260 oC with an extrusion ratio of 25. The microstructure and mechanical behavior of as-cast and extruded alloys are reported and discussed. The results show that Mg-6Li-1.2Zn- 1.2Y alloy is composed of α-Mg, β-Li, and W-Mg3Zn3Y2 phases while Mg-6Li-0.3Zn-0.6Y alloy contains α-Mg, β-Li, W-Mg3Zn3Y2 phase and X-Mg12ZnY. After hot extrusion, the microstructure of specimens is refined and the average grains size of extruded alloys is 15 μm. Dynamic recrystallization occurs during the extrusion, leading to grain refinement of test alloys. Both the strength and elongation of test alloys are improved by extrusion. The extruded Mg-6Li-0.3Zn-0.6Y alloy possesses an ultimate strength of 225 MPa with an elongation of 18% while the strength and elongation of Mg-6Li-1.2Zn-1.2Y alloy are 206 MPa and 28%, respectively. The X-phase in Mg-6Li-0.3Zn- 0.6Y is beneficial to the improvement of strength, but will lead to the decrease of ductility.

Go to article

Authors and Affiliations

J-f. Su
Y. Yang
X-s. Fu
Q-y. Ma
F-j. Ren
X-d. Peng
Download PDF Download RIS Download Bibtex

Abstract

Characteristics of the microstructure of corrosion-resistant cast 24Cr-5Ni-2.5Mo duplex steel after introduction of 0.98, 1.67 and 4.3% Si were described. Based on the test results it has been found that silicon addition introduced to the corrosion-resistant cast two-phase duplex steel significantly reduces austenite content in the alloy matrix. Increasing silicon content in the test alloy to 4.3% has resulted, in addition to the elimination of austenite, also in the precipitation of Si-containing intermetallic phases at the grain boundaries and inside the grains. The precipitates were characterized by varying content of Cr and Mo, indicating the presence in the structure of more than one type of the brittle phase characteristic for this group of materials. The simulation using Thermo-Calc software has confirmed the presence of ferrite in all tested alloys. In the material containing 4.3% Si, the Cr and Si enriched precipitates, such as G phase and Cr3Si were additionally observed to occur.

Go to article

Authors and Affiliations

J. Kowalska
M. Witkowska
B. Kalandyk
R. Zapała
Download PDF Download RIS Download Bibtex

Abstract

The effectiveness of cast iron spheroidization with FeSiMg master alloy by the traditional method and using a reaction chamber placed in the cavity of foundry mould was compared. The method of cast iron treatment in mould cavity using a reaction chamber is an innovative technology developed by the Foundry Research Institute in Krakow. The effectiveness of the spheroidization process carried out by both methods was checked on a series of test castings. The article also presents the results of metallographic examinations and mechanical testing, including the discussion of magnesium yield and its assimilation rate.

Go to article

Authors and Affiliations

J. Kamińska
M. Angrecki
Z. Stefański
A. Palma
E. Pamuła
Download PDF Download RIS Download Bibtex

Abstract

The article presents results of research on the influence of variable parameters of horizontal continuous casting on the structure of AlCu4MgSi (EN AW-2017A) alloy ingots. The special character of the process allows for a continuous change of some of its parameters, namely, of the casting speed and of the rate of the cooling fluid flow thorough the crystallizer. These parameters have a significant impact on the crystallization process of the liquid metal. Depending on the cooling rate, intensity of the convection inside the solidifying alloy, and its chemical composition, there may arise some differences in the structure of the cast. In this study, ingots obtained at different casting speeds have been analyzed. The research methodology, based on light microscopy and electron microscopy (SEM), as well as energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), allowed for a thorough examination of the structure of the studied materials. The results were shown that an increase in the ingot casting speed leads to an increase in the average grain surface area.

Go to article

Authors and Affiliations

T. Wróbel
P.M. Nuckowski
Download PDF Download RIS Download Bibtex

Abstract

The paper presents the results of the application of a statistical analysis to evaluate the effect of the chemical composition of the die casting Al-Si alloys on its basic mechanical properties. The examinations were performed on the hypoeutectic Al-Si alloy type EN AC-46000 and, created on its basis, a multi-component Al-Si alloy containing high-melting additions Cr, Mo, W and V. The additions were introduced into the base Al-Si alloy in different combinations and amounts (from 0,05% to 0,50%). The tensile strength Rm; the proof stress Rp0,2; the unit elongation A and the hardness HB of the examined Al-Si alloys were determined. The data analysis and the selection of Al-Si alloy samples without the Cr, Mo, W and V additions were presented; a database containing the independent variables (Al-Si alloy's chemical composition) and dependent variables (Rm; Rp0,2; A and HB) for all the considered variants of Al-Si alloy composition was constructed. Additionally, an analysis was made of the effect of the Al-Si alloy's component elements on the obtained mechanical properties, with a special consideration of the high-melting additions Cr, Mo, V and W. For the optimization of the content of these additions in the Al-Si alloy, the dependent variables were standardized and treated jointly. The statistical tools were mainly the multivariate backward stepwise regression and linear correlation analysis and the analysis of variance ANOVA. The statistical analysis showed that the most advantageous effect on the jointly treated mechanical properties is obtained with the amount of the Cr, Mo, V and W additions of 0,05 to 0,10%.

Go to article

Authors and Affiliations

J. Szymszal
G. Gumienny
T. Szymczak
Download PDF Download RIS Download Bibtex

Abstract

Access to up-to-date information on technology, innovation, source publications, and the materials and services offered in a particular industry is very important for both industrial plants and departmental research centres. It should be noted that obtaining such information using publicly available search engines such as Google, Yahoo!, Bing, Bindu (mainly used in China) is only apparently easy because, due to their versatility, they deliver results with great redundancy. This leads to the need to analyze large data sets by linguistic methods or "manually", which is very tedious and time consuming. In this situation, it was considered reasonable to undertake studies aimed at acquiring relatively simple IT tools, i.e. crawlers, which allow their users to selectively search for information in a particular problem area, which in this particular case is casting. The intention of this work was to collect and analyze the experimental material that would allow describing the characteristics of the above solutions from the point of view of the range of their application, the quality of the results achieved, and possible limitations and preferences taking into account user needs [1, 2].

Go to article

Authors and Affiliations

S. Kluska-Nawarecka
D. Wilk-Kołodziejczyk
Z. Stefański
A. Smolarek
Download PDF Download RIS Download Bibtex

Abstract

The research was concerned with the influence of chemical composition of austenitic steels on their mechanical properties. Resulting properties of castings from austenitic steels are significantly influenced by the solidification time that affects the size of the primary grain as well as the layout of elements within the dendrite and its parts with regard to the last solidification points in the interdendritic melt. During solidification an intensive segregation of all admixtures occurs in the melt, which causes a whole range of serious metallurgical defects and it has also a significant influence on subsequent precipitation of carbides and intermetallic phases. Chemical heterogeneity then affects the structure and mechanical properties of the casting. In a planned experiment, we cast melted steels containing 18 to 28 % Cr and 8 to 28 % Ni with variable carbon and nitrogen contents. Testing the tensile strength of the cast specimens we could determine the Rp0.2, Rm, and A5 values. The dependence of the mechanical properties on the chemical content was described by regression equations. The planned experiment results allow us to control the chemical content for the given austenitic steel quality to achieve the required values of the mechanical properties.

Go to article

Authors and Affiliations

A. Záděra
V. Kaňa
B. Maroš
P. Blažík
J. Čech
Download PDF Download RIS Download Bibtex

Abstract

Gas emission from casting moulds, cores and coatings applied for sand and permanent moulds is one of the fundamental reasons of casting defects occurrence. In the previous studies, gas emission was measured in two ways: normalized, in which the evolving gas volume was measured during heating of the moulding sand sample in a sealed flask, or by measuring the amount of gas from sand core (sample) which is produced during the pouring of liquid metal. After the pouring process the sand mould is heated very unequally, the most heated areas are layers adjacent to the liquid metal. The emission of gas is significantly larger from the surface layer than from the remaining ones. New, original method of measuring kinetics of gas emission from very thin layers of sand moulds heated by liquid metal developed by the authors is presented in the hereby paper. Description of this new method and the investigation results of kinetics of gas emission from moulding sand with furan and alkyd resin are shown. Liquid grey cast iron and Al-Si alloy were used as a heat source in the sand moulds. Comparison of the kinetics of gas emission of these two kinds of moulding sands filled with two different alloys was made. The momentary metal temperature in sand mould was assigned to the kinetics of gas emission, what creates a full view of the possibility of formation of casting defects of the gaseous origin. Moulding sand with alkyd resin is characterized by larger gas emission; however gases are emitted slower than in the case of moulding sands with furan resin. This new investigation method has a high repeatability and is the only one which gives a full view of phenomenon’s in the surface layer which determines quality of the casings. The obtained results are presented on several graphs and analyzed in detail. They have a great application value and can be used in the production of iron as well as light metal alloy castings.

Go to article

Authors and Affiliations

J. Zych
J. Mocek
N. Kaźnica

Instructions for authors

Submission


To submit the article, please use the Editorial System provided here:

https://www.editorialsystem.com/afe


Papers submitted in any other way will not be accepted.



The Journal does not have submission charges.


The APC Article Processing Charge is 110 euros (500zł for Polish authors). In some cases, the APC is paid as a part of the scientific conference fee, for which the AFE journal is a supportive one. If not, it is payable after the acceptance of the final article by direct money transfer.


Bank account details:


Account holder: Stowarzyszenie Wychowankow Politechniki Slaskiej Kolo Odlewnikow
Account holder address: ul. Towarowa 7, 44-100 Gliwice, Poland
Account numbers: BIC BPKOPLPW IBAN PL17 1020 2401 0000 0202 0183 3748


Instructions for the preparation of an Archives of Foundry Engineering Paper

Publication Ethics Policy


Publication Ethics Policy

The standards of expected ethical behavior for all parties involved in publishing in the Archives of Foundry Engineering journal: the author, the journal editor and editorial board, the peer reviewers and the publisher are listed below.

All the articles submitted for publication in Archives of Foundry Engineering are peer reviewed for authenticity, ethical issues and usefulness as per Review Procedure document.

Duties of Editors
1. Monitoring the ethical standards: Editorial Board monitors the ethical standards of the submitted manuscripts and takes all possible measures against any publication malpractices.
2. Fair play: Submitted manuscripts are evaluated for their scientific content without regard to race, gender, sexual orientation, religious beliefs, citizenship, political ideology or any other issues that is a personal or human right.
3. Publication decisions: The Editor in Chief is responsible for deciding which of the submitted articles should or should not be published. The decision to accept or reject the article is based on its importance, originality, clarity, and its relevance to the scope of the journal and is made after the review process.
4. Confidentiality: The Editor in Chief and the members of the Editorial Board t ensure that all materials submitted to the journal remain confidential during the review process. They must not disclose any information about a submitted manuscript to anyone other than the parties involved in the publishing process i.e., authors, reviewers, potential reviewers, other editorial advisers, and the publisher.
5. Disclosure and conflict of interest: Unpublished materials disclosed in the submitted manuscript must not be used by the Editor and the Editorial Board in their own research without written consent of authors. Editors always precludes business needs from compromising intellectual and ethical standards.
6. Maintain the integrity of the academic record: The editors will guard the integrity of the published academic record by issuing corrections and retractions when needed and pursuing suspected or alleged research and publication misconduct. Plagiarism and fraudulent data is not acceptable. Editorial Board always be willing to publish corrections, clarifications, retractions and apologies when needed.

Retractions of the articles: the Editor in Chief will consider retracting a publication if:
- there are clear evidences that the findings are unreliable, either as a result of misconduct (e.g. data fabrication) or honest error (e.g. miscalculation or experimental error)
- the findings have previously been published elsewhere without proper cross-referencing, permission or justification (cases of redundant publication)
- it constitutes plagiarism or reports unethical research.
Notice of the retraction will be linked to the retracted article (by including the title and authors in the retraction heading), clearly identifies the retracted article and state who is retracting the article. Retraction notices should always mention the reason(s) for retraction to distinguish honest error from misconduct.
Retracted articles will not be removed from printed copies of the journal nor from electronic archives but their retracted status will be indicated as clearly as possible.

Duties of Authors
1. Reporting standards: Authors of original research should present an accurate account of the work performed as well as an objective discussion of its significance. Underlying data should be represented accurately in the paper. The paper should contain sufficient details and references to permit others to replicate the work. The fabrication of results and making of fraudulent or inaccurate statements constitute unethical behavior and will cause rejection or retraction of a manuscript or a published article.
2. Originality and plagiarism: Authors should ensure that they have written entirely original works, and if the authors have used the work and/or words of others they need to be cited or quoted. Plagiarism and fraudulent data is not acceptable.
3. Data access retention: Authors may be asked to provide the raw data for editorial review, should be prepared to provide public access to such data, and should be prepared to retain such data for a reasonable time after publication of their paper.
4. Multiple or concurrent publication: Authors should not in general publish a manuscript describing essentially the same research in more than one journal. Submitting the same manuscript to more than one journal concurrently constitutes unethical publishing behavior and is unacceptable.
5. Authorship of the manuscript: Authorship should be limited to those who have made a significant contribution to the conception, design, execution, or interpretation of the report study. All those who have made contributions should be listed as co-authors. The corresponding author should ensure that all appropriate co-authors and no inappropriate co-authors are included in the paper, and that all co-authors have seen and approved the final version of the paper and have agreed to its submission for publication.
6. Acknowledgement of sources: The proper acknowledgment of the work of others must always be given. The authors should cite publications that have been influential in determining the scope of the reported work.
7. Fundamental errors in published works: When the author discovers a significant error or inaccuracy in his/her own published work, it is the author’s obligation to promptly notify the journal editor or publisher and cooperate with the editor to retract or correct the paper.

Duties of Reviewers
1. Contribution to editorial decisions: Peer reviews assist the editor in making editorial decisions and may also help authors to improve their manuscript.
2. Promptness: Any selected reviewer who feels unqualified to review the research reported in a manuscript or knows that its timely review will be impossible should notify the editor and excuse himself/herself from the review process.
3. Confidentiality: All manuscript received for review must be treated as confidential documents. They must not be shown to or discussed with others except those authorized by the editor.
4. Standards of objectivity: Reviews should be conducted objectively. Personal criticism of the author is inappropriate. Reviewers should express their views clearly with appropriate supporting arguments.
5. Acknowledgement of sources: Reviewers should identify the relevant published work that has not been cited by authors. Any substantial similarity or overlap between the manuscript under consideration and any other published paper should be reported to the editor.
6. Disclosure and conflict of Interest: Privileged information or ideas obtained through peer review must be kept confidential and not used for personal advantage. Reviewers should not consider evaluating manuscripts in which they have conflicts of interest resulting from competitive, collaborative, or other relations with any of the authors, companies, or institutions involved in writing a paper.

Peer-review Procedure


Review Procedure


The Review Procedure for articles submitted to the Archives of Foundry Engineering agrees with the recommendations of the Ministry of Science and Higher Education published in a booklet: ‘Dobre praktyki w procedurach recenzyjnych w nauce’ (MNiSW, Dobre praktyki w procedurach recenzyjnych w nauce, Warszawa 2011).

Papers submitted to the Editorial System are primarily screened by editors with respect to scope, formal issues and used template. Texts with obvious errors (formatting other than requested, missing references, evidently low scientific quality) will be rejected at this stage or will be sent for the adjustments.

Once verified each article is checked by the anti-plagiarism system Cross Check powered by iThenticate®. After the positive response, the article is moved into: Initially verified manuscripts. When the similarity level is too high, the article will be rejected. There is no strict rule (i.e., percentage of the similarity), and it is always subject to the Editor’s decision.
Initially verified manuscripts are then sent to at least four independent referees outside the author’s institution and at least two of them outside of Poland, who:

have no conflict of interests with the author,
are not in professional relationships with the author,
are competent in a given discipline and have at least a doctorate degree and respective
scientific achievements,
have a good reputation as reviewers.


The review form is available online at the Journal’s Editorial System and contains the following sections:

1. Article number and title in the Editorial System

2. The statement of the Reviewer (to choose the right options):

I declare that I have not guessed the identity of the Author. I declare that I have guessed the identity of the Author, but there is no conflict of interest

3. Detailed evaluation of the manuscript against other researches published to this point:

Do you think that the paper title corresponds with its contents?
Yes No
Do you think that the abstract expresses the paper contents well?
Yes No
Are the results or methods presented in the paper novel?
Yes No
Do the author(s) state clearly what they have achieved?
Yes No
Do you find the terminology employed proper?
Yes No
Do you find the bibliography representative and up-to-date?
Yes No
Do you find all necessary illustrations and tables?
Yes No
Do you think that the paper will be of interest to the journal readers?
Yes No

4. Reviewer conclusion

Accept without changes
Accept after changes suggested by reviewer.
Rate manuscript once again after major changes and another review
Reject


5. Information for Editors (not visible for authors).

6. Information for Authors


Reviewing is carried out in the double blind process (authors and reviewers do not know each other’s names).

The appointed reviewers obtain summary of the text and it is his/her decision upon accepting/rejecting the paper for review within a given time period 21 days.

The reviewers are obliged to keep opinions about the paper confidential and to not use knowledge about it before publication.

The reviewers send their review to the Archives of Foundry Engineering by Editorial System. The review is archived in the system.

Editors do not accept reviews, which do not conform to merit and formal rules of scientific reviewing like short positive or negative remarks not supported by a close scrutiny or definitely critical reviews with positive final conclusion. The reviewer’s remarks are sent to the author. He/she has to consider all remarks and revise the text accordingly.

The author of the text has the right to comment on the conclusions in case he/she does not agree with them. He/she can request the article withdrawal at any step of the article processing.

The Editor-in-Chief (supported by members of the Editorial Board) decides on publication based on remarks and conclusions presented by the reviewers, author’s comments and the final version of the manuscript.

The final Editor’s decision can be as follows:
Accept without changes
Reject


The rules for acceptance or rejection of the paper and the review form are available on the Web page of the AFE publisher.

Once a year Editorial Office publishes present list of cooperating reviewers.
Reviewing is free of charge.
All articles, including those rejected and withdrawn, are archived in the Editorial System.

Reviewers

List of Reviewers 2022

Shailee Acharya - S. V. I. T Vasad, India
Vivek Ayar - Birla Vishvakarma Mahavidyalaya Vallabh Vidyanagar, India
Mohammad Azadi - Semnan University, Iran
Azwinur Azwinur - Politeknik Negeri Lhokseumawe, Indonesia
Czesław Baron - Silesian University of Technology, Gliwice, Poland
Dariusz Bartocha - Silesian University of Technology, Gliwice, Poland
Iwona Bednarczyk - Silesian University of Technology, Gliwice, Poland
Artur Bobrowski - AGH University of Science and Technology, Kraków
Poland Łukasz Bohdal - Koszalin University of Technology, Koszalin Poland
Danka Bolibruchova - University of Zilina, Slovak Republic
Joanna Borowiecka-Jamrozek- The Kielce University of Technology, Poland
Debashish Bose - Metso Outotec India Private Limited, Vadodara, India
Andriy Burbelko - AGH University of Science and Technology, Kraków
Poland Ganesh Chate - KLS Gogte Institute of Technology, India
Murat Çolak - Bayburt University, Turkey
Adam Cwudziński - Politechnika Częstochowska, Częstochowa, Poland
Derya Dispinar- Istanbul Technical University, Turkey
Rafał Dojka - ODLEWNIA RAFAMET Sp. z o. o., Kuźnia Raciborska, Poland
Anna Dolata - Silesian University of Technology, Gliwice, Poland
Tomasz Dyl - Gdynia Maritime University, Gdynia, Poland
Maciej Dyzia - Silesian University of Technology, Gliwice, Poland
Eray Erzi - Istanbul University, Turkey
Flora Faleschini - University of Padova, Italy
Imre Felde - Obuda University, Hungary
Róbert Findorák - Technical University of Košice, Slovak Republic
Aldona Garbacz-Klempka - AGH University of Science and Technology, Kraków, Poland
Katarzyna Gawdzińska - Maritime University of Szczecin, Poland
Marek Góral - Rzeszow University of Technology, Poland
Barbara Grzegorczyk - Silesian University of Technology, Gliwice, Poland
Grzegorz Gumienny - Technical University of Lodz, Poland
Ozen Gursoy - University of Padova, Italy
Gábor Gyarmati - University of Miskolc, Hungary
Jakub Hajkowski - Poznan University of Technology, Poland
Marek Hawryluk - Wroclaw University of Science and Technology, Poland
Aleš Herman - Czech Technical University in Prague, Czech Republic
Mariusz Holtzer - AGH University of Science and Technology, Kraków, Poland
Małgorzata Hosadyna-Kondracka - Łukasiewicz Research Network - Krakow Institute of Technology, Poland
Dario Iljkić - University of Rijeka, Croatia
Magdalena Jabłońska - Silesian University of Technology, Gliwice, Poland
Nalepa Jakub - Silesian University of Technology, Gliwice, Poland
Jarosław Jakubski - AGH University of Science and Technology, Kraków, Poland
Aneta Jakubus - Akademia im. Jakuba z Paradyża w Gorzowie Wielkopolskim, Poland
Łukasz Jamrozowicz - AGH University of Science and Technology, Kraków, Poland
Krzysztof Janerka - Silesian University of Technology, Gliwice, Poland
Karolina Kaczmarska - AGH University of Science and Technology, Kraków, Poland
Jadwiga Kamińska - Łukasiewicz Research Network – Krakow Institute of Technology, Poland
Justyna Kasinska - Kielce University Technology, Poland
Magdalena Kawalec - AGH University of Science and Technology, Kraków, Poland
Gholamreza Khalaj - Islamic Azad University, Saveh Branch, Iran
Angelika Kmita - AGH University of Science and Technology, Kraków, Poland
Marcin Kondracki - Silesian University of Technology, Gliwice Poland
Vitaliy Korendiy - Lviv Polytechnic National University, Lviv, Ukraine
Aleksandra Kozłowska - Silesian University of Technology, Gliwice, Poland
Ivana Kroupová - VSB - Technical University of Ostrava, Czech Republic
Malgorzata Lagiewka - Politechnika Czestochowska, Częstochowa, Poland
Janusz Lelito - AGH University of Science and Technology, Kraków, Poland
Jingkun Li - University of Science and Technology Beijing, China
Petr Lichy - Technical University Ostrava, Czech Republic
Y.C. Lin - Central South University, China
Mariusz Łucarz - AGH University of Science and Technology, Kraków, Poland
Ewa Majchrzak - Silesian University of Technology, Gliwice, Poland
Barnali Maji - NIT-Durgapur: National Institute of Technology, Durgapur, India
Pawel Malinowski - AGH University of Science and Technology, Kraków, Poland
Marek Matejka - University of Zilina, Slovak Republic
Bohdan Mochnacki - Technical University of Occupational Safety Management, Katowice, Poland
Grzegorz Moskal - Silesian University of Technology, Poland
Kostiantyn Mykhalenkov - National Academy of Science of Ukraine, Ukraine
Dawid Myszka - Silesian University of Technology, Gliwice, Poland
Maciej Nadolski - Czestochowa University of Technology, Poland
Krzysztof Naplocha - Wrocław University of Science and Technology, Poland
Daniel Nowak - Wrocław University of Science and Technology, Poland
Tomáš Obzina - VSB - Technical University of Ostrava, Czech Republic
Peiman Omranian Mohammadi - Shahid Bahonar University of Kerman, Iran
Zenon Opiekun - Politechnika Rzeszowska, Rzeszów, Poland
Onur Özbek - Duzce University, Turkey
Richard Pastirčák - University of Žilina, Slovak Republic
Miroslawa Pawlyta - Silesian University of Technology, Gliwice, Poland
Jacek Pezda - ATH Bielsko-Biała, Poland
Bogdan Piekarski - Zachodniopomorski Uniwersytet Technologiczny, Szczecin, Poland
Jacek Pieprzyca - Silesian University of Technology, Gliwice, Poland
Bogusław Pisarek - Politechnika Łódzka, Poland
Marcela Pokusová - Slovak Technical University in Bratislava, Slovak Republic
Hartmut Polzin - TU Bergakademie Freiberg, Germany
Cezary Rapiejko - Lodz University of Technology, Poland
Arron Rimmer - ADI Treatments, Doranda Way, West Bromwich, West Midlands, United Kingdom
Jaromír Roučka - Brno University of Technology, Czech Republic
Charnnarong Saikaew - Khon Kaen University Thailand Amit Sata - MEFGI, Faculty of Engineering, India
Mariola Saternus - Silesian University of Technology, Gliwice, Poland
Vasudev Shinde - DKTE' s Textile and Engineering India Robert Sika - Politechnika Poznańska, Poznań, Poland
Bozo Smoljan - University North Croatia, Croatia
Leszek Sowa - Politechnika Częstochowska, Częstochowa, Poland
Sławomir Spadło - Kielce University of Technology, Poland
Mateusz Stachowicz - Wroclaw University of Technology, Poland
Marcin Stawarz - Silesian University of Technology, Gliwice, Poland
Grzegorz Stradomski - Czestochowa University of Technology, Poland
Roland Suba - Schaeffler Skalica, spol. s r.o., Slovak Republic
Maciej Sułowski - AGH University of Science and Technology, Kraków, Poland
Jan Szajnar - Silesian University of Technology, Gliwice, Poland
Michal Szucki - TU Bergakademie Freiberg, Germany
Tomasz Szymczak - Lodz University of Technology, Poland
Damian Słota - Silesian University of Technology, Gliwice, Poland
Grzegorz Tęcza - AGH University of Science and Technology, Kraków, Poland
Marek Tkocz - Silesian University of Technology, Gliwice, Poland
Andrzej Trytek - Rzeszow University of Technology, Poland
Mirosław Tupaj - Rzeszow University of Technology, Poland
Robert B Tuttle - Western Michigan University United States Seyed Ebrahim Vahdat - Ayatollah Amoli Branch, Islamic Azad University, Amol, Iran
Iveta Vaskova - Technical University of Kosice, Slovak Republic
Dorota Wilk-Kołodziejczyk - AGH University of Science and Technology, Kraków, Poland
Ryszard Władysiak - Lodz University of Technology, Poland
Çağlar Yüksel - Atatürk University, Turkey
Renata Zapała - AGH University of Science and Technology, Kraków, Poland
Jerzy Zych - AGH University of Science and Technology, Kraków, Poland
Andrzej Zyska - Czestochowa University of Technology, Poland



List of Reviewers 2021

Czesław Baron - Silesian University of Technology, Gliwice, Poland
Imam Basori - State University of Jakarta, Indonesia
Leszek Blacha - Silesian University of Technology, Gliwice
Poland Artur Bobrowski - AGH University of Science and Technology, Kraków, Poland
Danka Bolibruchova - University of Zilina, Slovak Republic
Pedro Brito - Pontifical Catholic University of Minas Gerais, Brazil
Marek Bruna - University of Zilina, Slovak Republic
Marcin Brzeziński - AGH University of Science and Technology, Kraków, Poland
Andriy Burbelko - AGH University of Science and Technology, Kraków, Poland
Alexandros Charitos - TU Bergakademie Freiberg, Germany
Ganesh Chate - KLS Gogte Institute of Technology, India
L.Q. Chen - Northeastern University, China
Zhipei Chen - University of Technology, Netherlands
Józef Dańko - AGH University of Science and Technology, Kraków, Poland
Brij Dhindaw - Indian Institute of Technology Bhubaneswar, India
Derya Dispinar - Istanbul Technical University, Turkey
Rafał Dojka - ODLEWNIA RAFAMET Sp. z o. o., Kuźnia Raciborska, Poland
Anna Dolata - Silesian University of Technology, Gliwice, Poland
Agnieszka Dulska - Silesian University of Technology, Gliwice, Poland
Maciej Dyzia - Silesian University of Technology, Poland
Eray Erzi - Istanbul University, Turkey
Przemysław Fima - Institute of Metallurgy and Materials Science PAN, Kraków, Poland
Aldona Garbacz-Klempka - AGH University of Science and Technology, Kraków, Poland
Dipak Ghosh - Forace Polymers P Ltd., India
Beata Grabowska - AGH University of Science and Technology, Kraków, Poland
Adam Grajcar - Silesian University of Technology, Gliwice, Poland
Grzegorz Gumienny - Technical University of Lodz, Poland
Gábor Gyarmati - Foundry Institute, University of Miskolc, Hungary
Krzysztof Herbuś - Silesian University of Technology, Gliwice, Poland
Aleš Herman - Czech Technical University in Prague, Czech Republic
Mariusz Holtzer - AGH University of Science and Technology, Kraków, Poland
Małgorzata Hosadyna-Kondracka - Łukasiewicz Research Network - Krakow Institute of Technology, Kraków, Poland
Jarosław Jakubski - AGH University of Science and Technology, Kraków, Poland
Krzysztof Janerka - Silesian University of Technology, Gliwice, Poland
Robert Jasionowski - Maritime University of Szczecin, Poland
Agata Jażdżewska - Gdansk University of Technology, Poland
Jan Jezierski - Silesian University of Technology, Gliwice, Poland
Karolina Kaczmarska - AGH University of Science and Technology, Kraków, Poland
Jadwiga Kamińska - Centre of Casting Technology, Łukasiewicz Research Network – Krakow Institute of Technology, Poland
Adrian Kampa - Silesian University of Technology, Gliwice, Poland
Wojciech Kapturkiewicz- AGH University of Science and Technology, Kraków, Poland
Tatiana Karkoszka - Silesian University of Technology, Gliwice, Poland
Gholamreza Khalaj - Islamic Azad University, Saveh Branch, Iran
Himanshu Khandelwal - National Institute of Foundry & Forging Technology, Hatia, Ranchi, India
Angelika Kmita - AGH University of Science and Technology, Kraków, Poland
Grzegorz Kokot - Silesian University of Technology, Gliwice, Poland
Ladislav Kolařík - CTU in Prague, Czech Republic
Marcin Kondracki - Silesian University of Technology, Gliwice, Poland
Dariusz Kopyciński - AGH University of Science and Technology, Kraków, Poland
Janusz Kozana - AGH University of Science and Technology, Kraków, Poland
Tomasz Kozieł - AGH University of Science and Technology, Kraków, Poland
Aleksandra Kozłowska - Silesian University of Technology, Gliwice Poland
Halina Krawiec - AGH University of Science and Technology, Kraków, Poland
Ivana Kroupová - VSB - Technical University of Ostrava, Czech Republic
Wacław Kuś - Silesian University of Technology, Gliwice, Poland
Jacques Lacaze - University of Toulouse, France
Avinash Lakshmikanthan - Nitte Meenakshi Institute of Technology, India
Jaime Lazaro-Nebreda - Brunel Centre for Advanced Solidification Technology, Brunel University London, United Kingdom
Janusz Lelito - AGH University of Science and Technology, Kraków, Poland
Tomasz Lipiński - University of Warmia and Mazury in Olsztyn, Poland
Mariusz Łucarz - AGH University of Science and Technology, Kraków, Poland
Maria Maj - AGH University of Science and Technology, Kraków, Poland
Jerzy Mendakiewicz - Silesian University of Technology, Gliwice, Poland
Hanna Myalska-Głowacka - Silesian University of Technology, Gliwice, Poland
Kostiantyn Mykhalenkov - Physics-Technological Institute of Metals and Alloys, National Academy of Science of Ukraine, Ukraine
Dawid Myszka - Politechnika Warszawska, Warszawa, Poland
Maciej Nadolski - Czestochowa University of Technology, Poland
Daniel Nowak - Wrocław University of Science and Technology, Poland
Mitsuhiro Okayasu - Okayama University, Japan
Agung Pambudi - Sebelas Maret University in Indonesia, Indonesia
Richard Pastirčák - University of Žilina, Slovak Republic
Bogdan Piekarski - Zachodniopomorski Uniwersytet Technologiczny, Szczecin, Poland
Bogusław Pisarek - Politechnika Łódzka, Poland
Seyda Polat - Kocaeli University, Turkey
Hartmut Polzin - TU Bergakademie Freiberg, Germany
Alena Pribulova - Technical University of Košice, Slovak Republic
Cezary Rapiejko - Lodz University of Technology, Poland
Arron Rimmer - ADI Treatments, Doranda Way, West Bromwich West Midlands, United Kingdom
Iulian Riposan - Politehnica University of Bucharest, Romania
Ferdynand Romankiewicz - Uniwersytet Zielonogórski, Zielona Góra, Poland
Mario Rosso - Politecnico di Torino, Italy
Jaromír Roučka - Brno University of Technology, Czech Republic
Charnnarong Saikaew - Khon Kaen University, Thailand
Mariola Saternus - Silesian University of Technology, Gliwice, Poland
Karthik Shankar - Amrita Vishwa Vidyapeetham , Amritapuri, India
Vasudev Shinde - Shivaji University, Kolhapur, Rajwada, Ichalkaranji, India
Robert Sika - Politechnika Poznańska, Poznań, Poland
Jerzy Sobczak - AGH University of Science and Technology, Kraków, Poland
Sebastian Sobula - AGH University of Science and Technology, Kraków, Poland
Marek Soiński - Akademia im. Jakuba z Paradyża w Gorzowie Wielkopolskim, Poland
Mateusz Stachowicz - Wroclaw University of Technology, Poland
Marcin Stawarz - Silesian University of Technology, Gliwice, Poland
Andrzej Studnicki - Silesian University of Technology, Gliwice, Poland
Mayur Sutaria - Charotar University of Science and Technology, CHARUSAT, Gujarat, India
Maciej Sułowski - AGH University of Science and Technology, Kraków, Poland
Sutiyoko Sutiyoko - Manufacturing Polytechnic of Ceper, Klaten, Indonesia
Tomasz Szymczak - Lodz University of Technology, Poland
Marek Tkocz - Silesian University of Technology, Gliwice, Poland
Andrzej Trytek - Rzeszow University of Technology, Poland
Jacek Trzaska - Silesian University of Technology, Gliwice, Poland
Robert B Tuttle - Western Michigan University, United States
Muhammet Uludag - Selcuk University, Turkey
Seyed Ebrahim Vahdat - Ayatollah Amoli Branch, Islamic Azad University, Amol, Iran
Tomasz Wrobel - Silesian University of Technology, Gliwice, Poland
Ryszard Władysiak - Lodz University of Technology, Poland
Antonin Zadera - Brno University of Technology, Czech Republic
Renata Zapała - AGH University of Science and Technology, Kraków, Poland
Bo Zhang - Hunan University of Technology, China
Xiang Zhang - Wuhan University of Science and Technology, China
Eugeniusz Ziółkowski - AGH University of Science and Technology, Kraków, Poland
Sylwia Żymankowska-Kumon - AGH University of Science and Technology, Kraków, Poland
Andrzej Zyska - Czestochowa University of Technology, Poland



List of Reviewers 2020

Shailee Acharya - S. V. I. T Vasad, India
Mohammad Azadi - Semnan University, Iran
Rafał Babilas - Silesian University of Technology, Gliwice, Poland
Czesław Baron - Silesian University of Technology, Gliwice, Poland
Dariusz Bartocha - Silesian University of Technology, Gliwice, Poland
Emin Bayraktar - Supmeca/LISMMA-Paris, France
Jaroslav Beňo - VSB-Technical University of Ostrava, Czech Republic
Artur Bobrowski - AGH University of Science and Technology, Kraków, Poland
Grzegorz Boczkal - AGH University of Science and Technology, Kraków, Poland
Wojciech Borek - Silesian University of Technology, Gliwice, Poland
Pedro Brito - Pontifical Catholic University of Minas Gerais, Brazil
Marek Bruna - University of Žilina, Slovak Republic
John Campbell - University of Birmingham, United Kingdom
Ganesh Chate - Gogte Institute of Technology, India
L.Q. Chen - Northeastern University, China
Mirosław Cholewa - Silesian University of Technology, Gliwice, Poland
Khanh Dang - Hanoi University of Science and Technology, Viet Nam
Vladislav Deev - Wuhan Textile University, China
Brij Dhindaw - Indian Institute of Technology Bhubaneswar, India
Derya Dispinar - Istanbul Technical University, Turkey
Malwina Dojka - Silesian University of Technology, Gliwice, Poland
Rafał Dojka - ODLEWNIA RAFAMET Sp. z o. o., Kuźnia Raciborska, Poland
Anna Dolata - Silesian University of Technology, Gliwice, Poland
Agnieszka Dulska - Silesian University of Technology, Gliwice, Poland
Tomasz Dyl - Gdynia Maritime University, Poland
Maciej Dyzia - Silesian University of Technology, Gliwice, Poland
Eray Erzi - Istanbul University, Turkey
Katarzyna Gawdzińska - Maritime University of Szczecin, Poland
Sergii Gerasin - Pryazovskyi State Technical University, Ukraine
Dipak Ghosh - Forace Polymers Ltd, India
Marcin Górny - AGH University of Science and Technology, Kraków, Poland
Marcin Gołąbczak - Lodz University of Technology, Poland
Beata Grabowska - AGH University of Science and Technology, Kraków, Poland
Adam Grajcar - Silesian University of Technology, Gliwice, Poland
Grzegorz Gumienny - Technical University of Lodz, Poland
Libor Hlavac - VSB Ostrava, Czech Republic
Mariusz Holtzer - AGH University of Science and Technology, Kraków, Poland
Philippe Jacquet - ECAM, Lyon, France
Jarosław Jakubski - AGH University of Science and Technology, Kraków, Poland
Damian Janicki - Silesian University of Technology, Gliwice, Poland
Witold Janik - Silesian University of Technology, Gliwice, Poland
Robert Jasionowski - Maritime University of Szczecin, Poland
Jan Jezierski - Silesian University of Technology, Gliwice, Poland
Jadwiga Kamińska - Łukasiewicz Research Network – Krakow Institute of Technology, Poland
Justyna Kasinska - Kielce University Technology, Poland
Magdalena Kawalec - Akademia Górniczo-Hutnicza, Kraków, Poland
Angelika Kmita - AGH University of Science and Technology, Kraków, Poland
Ladislav Kolařík -Institute of Engineering Technology CTU in Prague, Czech Republic
Marcin Kondracki - Silesian University of Technology, Gliwice, Poland
Sergey Konovalov - Samara National Research University, Russia
Aleksandra Kozłowska - Silesian University of Technology, Gliwice, Poland
Janusz Krawczyk - AGH University of Science and Technology, Kraków, Poland
Halina Krawiec - AGH University of Science and Technology, Kraków, Poland
Ivana Kroupová - VSB - Technical University of Ostrava, Czech Republic
Agnieszka Kupiec-Sobczak - Cracow University of Technology, Poland
Tomasz Lipiński - University of Warmia and Mazury in Olsztyn, Poland
Aleksander Lisiecki - Silesian University of Technology, Gliwice, Poland
Krzysztof Lukaszkowicz - Silesian University of Technology, Gliwice, Poland
Mariusz Łucarz - AGH University of Science and Technology, Kraków, Poland
Katarzyna Major-Gabryś - AGH University of Science and Technology, Kraków, Poland
Pavlo Maruschak - Ternopil Ivan Pului National Technical University, Ukraine
Sanjay Mohan - Shri Mata Vaishno Devi University, India
Marek Mróz - Politechnika Rzeszowska, Rzeszów, Poland
Sebastian Mróz - Czestochowa University of Technology, Poland
Kostiantyn Mykhalenkov - National Academy of Science of Ukraine, Ukraine
Dawid Myszka - Politechnika Warszawska, Warszawa, Poland
Maciej Nadolski - Czestochowa University of Technology, Częstochowa, Poland
Konstantin Nikitin - Samara State Technical University, Russia
Daniel Pakuła - Silesian University of Technology, Gliwice, Poland


This page uses 'cookies'. Learn more