@article{Stawarz_M._SiMo_2017,
 author={Stawarz, M.},
 howpublished={online},
 year={2017},
 abstract={<p>
 The article presents crystallization process of silicon molybdenum 
 ductile cast iron (SiMo). The alloy with 5% silicon content and with
 </p>
 <p>
 variable amounts of Mo in a range of 0-1% was chosen for the research. 
 The carbon content in the analysed alloys did not exceed 3,1%.
 </p>
 <p>
 The studies of crystallization process were based on thermal &#8211; 
 derivative analysis (TDA). Chemical composition of all examined samples
 </p>
 <p>
 was analysed with the use of LECO spectrometer. Additionally, the carbon 
 and the sulphur content was determined basing on carbon and
 </p>
 <p>
 sulphur LECO analyser. For metallographic examination, the scanning 
 electron microscopy (SEM) with EDS analyser was used. Disclosed
 </p>
 <p>
 phases have been also tested with the use of X-ray diffraction. The 
 results allowed the description of crystallization processes of silicon
 </p>
 <p>
 molybdenum ductile cast iron using thermal &#8211; derivative analysis (TDA). 
 Conducted studies did not allow for the clear identification of all
 </p>
 <p>
 complex phases containing molybdenum, occurring at the grain boundaries. 
 Therefore, the further stages of the research could include the
 </p>
 <p>
 use of a transmission electron microscope to specify the description of 
 complex compounds present in the alloy. 
 </p>},
 title={SiMo Ductile Iron Crystallization Process},
 type={Artykuły / Articles},
 volume={vol. 17},
 number={No 1},
 journal={Archives of Foundry Engineering},
 publisher={The Katowice Branch of the Polish Academy of Sciences},
 doi={10.1515/afe-2017-0027},
 keywords={Crystallization process, Silicon cast iron, SiMo, TDA},
}