TY - JOUR N2 - Investigations were carried out to ensure the granulated blast furnace (GBF) slag as an alternative mould material in foundry industry by assessing the cast products structure property correlations. Sodium silicate-CO2 process was adopted for preparing the moulds. Three types of moulds were made with slag, silica sand individually and combination of these two with 10% sodium silicate and 20 seconds CO2 gassing time. A356 alloy castings were performed on these newly developed slag moulds. The cast products were investigated for its metallography and mechanical properties. Results reveal that cast products with good surface finish and without any defects were produced. Faster heat transfers in slag moulds enabled the cast products with fine and refined grain structured; and also, lower Secondary Dendrite Arm Spacing (SDAS) values were observed than sand mould. Slag mould casting shows improved mechanical properties like hardness, compression, tensile and impact strength compared to sand mould castings. Two types of tensile fracture modes, namely cleavage pattern with flat surfaces representing Al−Si eutectic zone and the areas of broken Fe-rich intermetallic compounds which appear as flower-like morphology was observed in sand mould castings. In contrast, GBF slag mould castings exhibit majority in dimple fracture morphology with traces of cleavage fracture. Charpy impact fractured surfaces of sand mould castings shows both transgranular and intergranular fracture modes. Only intergranular fracture mode was noticed in both GBF slag and mixed mould castings. L1 - http://journals.pan.pl/Content/101990/PDF/afe-2017-0033.pdf L2 - http://journals.pan.pl/Content/101990 PY - 2017 IS - No 1 DO - 10.1515/afe-2017-0033 KW - mechanical properties KW - Silica sand KW - GBF slag KW - CO2 process KW - A 356 alloy castings KW - SEM-EDX A1 - Jinugu, B.R. A1 - Inampudi, N.M. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol. 17 DA - 2017 T1 - Microstructure, SDAS and Mechanical Properties of A356 alloy Castings Made in Sand and Granulated Blast Furnace Slag Moulds UR - http://journals.pan.pl/dlibra/publication/edition/101990 T2 - Archives of Foundry Engineering ER -