TY - JOUR N2 - The subject of this paper was to compare the influence of selected coatings on bending strength of moulds and cores manufactured in a furan technology. In a range of study, there were used three kinds of coatings - water based coating and two kind of alcohol based coating manufactured by FOSECO. Coating were applicated by brush, overpouring/flow and spraying. For each application method, there were realized different kind of drying- at ambient temperature, in a furnace and by burning. Physicochemical properties of coatings were such selected to accommodate them to the application method and type of coating. Based on the conducted studies it was observed that for water based coating application method doesn’t have an important influence on bending strength and it is necessary to optimize the time and temperature of drying to achieve better results of bending strength. For alcohol based coatings, drying by burning causes significant deterioration of bending strength of the mould and core and drying process at ambient allows to obtain high bending strength of mould/cores in regard to time of drying. L1 - http://journals.pan.pl/Content/106799/PDF/AFE%202_2018_30.pdf L2 - http://journals.pan.pl/Content/106799 PY - 2018 IS - No 2 DO - 10.24425/122522 KW - water based coating KW - alcohol based coating KW - bending strength KW - moulding sand KW - furan resin A1 - Dorula, J. A1 - Romelczyk, R. A1 - Przyszlak, N. A1 - Siodmok, B. A1 - Studnicki, A. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol.18 DA - 2018 T1 - The Influence of Selected Water and Alcohol Based Coatings on Bending Strength of Foundry Moulds and Cores Manufactured in Furan Technology UR - http://journals.pan.pl/dlibra/publication/edition/106799 T2 - Archives of Foundry Engineering ER -