TY - JOUR N2 - It was found that the addition of carbon fibers (CFs) does not affect the crosslinking process in the microwave radiation (800 W, 2.45 GHz) of the BioCo2 binder, which is a water solution of poly(acrylic acid) and dextrin (PAA/D). It has influence on BioCo2 thermal properties. The CFs addition improves the thermostability of a binder and leads to the reduction of gas products quantity generated in the temperature range of 300-1100°C (TG-DTG, Py-GC/MS). Moreover, it causes the emission of harmful decomposition products such as benzene, toluene, xylene and styrene to be registered in a higher temperatures (above 700°C). BioCo2 binder without CFs addition is characterized by the emission of these substances in the lower temperature range. This indicates the positive effect of carbon fibers presence on the amount of released harmful products. The selected technological tests (permeability, friability, bending strength, tensile strength) have shown that the moulding sand with the 0.3 parts by weight carbon fibers addition displays the worst properties. The addition of 0.1 parts by weight of CFs is sufficient to obtain a beneficial effect on the analyzed moulding sands properties. The reduction of harmful substances at the higher temperatures can also be observed. L1 - http://journals.pan.pl/Content/107831/PDF/AFE%203_2018_26.pdf L2 - http://journals.pan.pl/Content/107831 PY - 2018 IS - No 3 EP - 160 KW - carbon fiber KW - polymer binder KW - thermostability KW - moulding sand A1 - Żymankowska-Kumon, S. A1 - Grabowska, B. A1 - Bobrowski, A. A1 - Drożyński, D. A1 - Kaczmarska, K. A1 - Cukrowicz, S. A1 - Gawluk, B. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol.18 DA - 2018.09.21 T1 - Influence of Carbon Fibers Addition on Selected Properties of Microwave-Cured Moulding Sand Bonded with BioCo2 Binder SP - 152 UR - http://journals.pan.pl/dlibra/publication/edition/107831 T2 - Archives of Foundry Engineering ER -