N2 - The primary microstructure of new Co-based superalloy of Co-20Ni-7Al-7W (at.%) type was showed in this article. The alloy was manufactured by induction melting in vacuum furnaces. This alloy is a part of new group of high-temperature materials based on Co solid solution and strengthened by coherent L12 phase similar to Ni-based superalloys with γʹ phase. The final form of Coss/L12 microstructure is obtained after fully heat treatment included homogenization, solutionizing and aging processes. But first step of heat treatment thermal parameters determination is characterization of primary microstructure of alloys after casting process with special attentions on segregations of alloying elements in solid solution and presences of structural elements such as eutectic areas, and other phases precipitations. In analysed case the relatively high homogeneity of chemical composition was expected especially in the case of W distribution, what was confirmed be SEM/EDS analysis in dendritic and interdendritic areas. L1 - http://journals.pan.pl/Content/110942/PDF/AFE%203_2019_13.pdf L2 - http://journals.pan.pl/Content/110942 PY - 2019 IS - No 3 DO - 10.24425/afe.2019.127143 KW - New Co-based superalloys KW - Co-20Ni-7Al-7W alloy KW - Primary microstructure A1 - Tomaszewska, A. A1 - Moskal, G. A1 - Mikuszewski, T. A1 - Junak, G. A1 - Płachta, A. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol. 19 DA - 2019.08.19 T1 - Primary Microstructure Characterization of As-Casted Co-20Ni-7Al-7W Superalloy UR - http://journals.pan.pl/dlibra/publication/edition/110942 T2 - Archives of Foundry Engineering