TY - JOUR N2 - The article focuses on the analysis of the effect of Zr on the properties of the aluminium alloy AlSi9Cu1Mg. The effect of Zr was evaluated depending on the change in mechanical properties and heat resistance during a gradual addition of Zr with an increase of 0.05 wt. % Zr. Half of the cast experimental samples from each variant were heat treated by precipitation hardening T6 (hereinafter HT). The measured values in both states indicate an improvement of the mechanical properties, especially in the experimental variants with a content of Zr ≥ 0.20 wt. %. In the evaluation of Rm, the most significant improvement occurred in the experimental variant with an addition of Zr 0.25 wt. % after HT and E in the experimental variant with addition of Zr 0.20 wt. % after HT. Thus, a difference was found from the results of the authors defining the positive effect of Zr, in particular at 0.15 wt. %. When evaluating the microstructure of the AlSi9Cu1Mg alloy after Zr alloying, Zr phases are already eliminated with the addition of Zr 0.10 wt. %. Especially at higher levels of Zr ≥ 0.20 wt. %, long needle phases with slightly cleaved morphology are visible in the metal matrix. It can be stated that a negative manifestation of Zr alloying is expressed by an increase in gassing of experimental alloys, especially in variants with a content of Zr ≥ 0.15 wt. %. Experimental samples were cast into ceramic moulds. The development of an experimental alloy AlSi9Cu1Mg alloyed with Zr would allow the production of a more sophisticated material applicable to thin-walled Al castings capable of operating at higher temperature loads. L1 - http://journals.pan.pl/Content/114690/PDF/AFE%202_2020_02.pdf L2 - http://journals.pan.pl/Content/114690 PY - 2020 IS - No 2 EP - 18 DO - 10.24425/afe.2020.131295 KW - Solidification process KW - Heat treatment KW - AlSi9Cu1Mg KW - AlZr15 KW - Ceramic moulds A1 - Matejka, M. A1 - Kuriš, M. A1 - Bolibruchova, D. A1 - Pastirčák, R. PB - The Katowice Branch of the Polish Academy of Sciences VL - vol. 20 DA - 2020.02.18 T1 - Influence of Zr on AlSi9Cu1Mg Alloy Cast in Ceramic SP - 13 UR - http://journals.pan.pl/dlibra/publication/edition/114690 T2 - Archives of Foundry Engineering ER -