Archives of Foundry Engineering | 2012 | No 2 |

Abstract

The paper presents the results of studies to determine the effect of complex surface and bulk modification and double filtration during mould pouring on the stereological parameters of macrostructure and mechanical properties of castings made from the post-production waste IN-713C and the MAR-247 nickel alloys. The evaluation covered the number of grains per 1mm2 of the sample surface area, the average area of grains and the shape index, hardness HB, tensile strength and resistance to high temperature creep. The results indicate the possibility of controlling the stereological parameters of macrostructure through application of several variants of the modification, controlling in this way also different low- and high-temperature properties. The positive effect of double filtration of the alloy during mould pouring on the metallurgical quality and mechanical properties of castings has also been emphasized.

Go to article

Abstract

The goal of this contribution is summary of physical – chemistry properties of usually used foundry silica and no – silica sands in Czech foundries. With the help of dilatometry analysis theoretical assumptions of influence of grain shape and size on dilatation value of sands were confirmed. Determined was the possibility of dilatometry analysis employment for preparing special (hybrid) sands with lower and/or more linear character of dilatation.

Go to article

Abstract

Ductile iron was quenched using two-variant isothermal transformation. The first treatment variant consisted of one-phase austenitization at a temperature tγ = 830, 860 or 900°C, cooling down to an isothermal transformation temperature of 300 or 400°C and holding from 8 to 64 minutes. The second treatment variant consisted of two-phase austenitization. Cast iron was austenitizied at a temperature tγ = 950°C and cooled down to a supercritical temperature tγ’ = 900, 860 or 830°C. Isothermal transformation was conducted under the same conditions as those applied to the first variant. Ferrite cast iron was quenched isothermally. Basic strength (Rp0.2, Rm) and plastic (A5) properties as well as matrix microstructure and hardness were examined. As a result of heat treatment, the following ADI grades were obtained: EN-GJS-800-8, EN-GJS-1200-2 and EN-GJS-1400-1 in accordance with PN–EN 1564:2000 having plasticity of 1.5÷4 times more than minimum requirements specified in the standard.

Go to article

Abstract

The results of studies on the use of modern two cored wires injection method for production of nodular graphite cast iron with use of unique implementation of drum ladle as a treatment/ transport and casting ladle instead vertical treatment ladle was described. The injection of length of Ø 9mm wires, cored: in FeSi + Mg nodulariser mixture and inoculant master alloy is a treatment method which can be used to produce iron melted in coreless induction furnace. This paper describes the results of using this method for possibility production of ductile iron under specific industrial conditions. In this case was taken ductile iron with material designation: EN-GJS-450- 10 Grade according PN-EN 1563:2000. Microstructure of 28 trials was controlled on internally used sample which has been correlated with standard sample before. The paper presents typical metallic matrix and graphite characteristic. Additionally, mechanical properties were checked in one experiment. Because of further possibility treatment temperature reduction only the rough magnesium recovery and cost of this new method are given.

Go to article

Abstract

The paper deals with problem of optimal used automatic workplace for HPDC technology - mainly from aspects of operations sequence, efficiency of work cycle and planning of using and servicing of HPDC casting machine. Presented are possible ways to analyse automatic units for HPDC. The experimental part was focused on the rationalization of the current work cycle time for die casting of aluminium alloy. The working place was described in detail in the project. The measurements were carried out in detail with the help of charts and graphs mapped cycle of casting workplace. Other parameters and settings have been identified. The proposals for improvements were made after the first measurements and these improvements were subsequently verified. The main actions were mainly software modifications of casting center. It is for the reason that today's sophisticated workplaces have the option of a relatively wide range of modifications without any physical harm to machines themselves. It is possible to change settings or unlock some unsatisfactory parameters.

Go to article

Abstract

One of the purposes of the application of chemically modified inorganic binders is to improve knocking out properties and the related reclamability with previously used in foundry inorganic binder (water glass), which allowing the use of ecological binders for casting nonferrous metals. Good knocking out properties of the sands is directly related to the waste sands reclamability, which is a necessary condition of effective waste management. Reclamation of moulding and core sands is a fundamental and effective way to manage waste on site at the foundry, in accordance with the Environmental Guidelines. Therefore, studies of reclamation of waste moulding and core sands with new types of inorganic binders (developed within the framework of the project) were carried out. These studies allowed to determine the degree of recovery of useful, material, what the reclaimed sand is, and the degree of its use in the production process. The article presents these results of investigation. They are a part of broader research programme executed under the project POIG.01.01.02-00- 015/09 "Advanced materials and technologies".

Go to article

Abstract

The results of studies on the use of magnesium alloy in modern Tundish for production of vermicular graphite cast irons were described. This paper describes the results of using a low-magnesium ferrosilicon alloy for the production of vermicular graphite cast irons. The paper presents a vermicular (and nodular) graphite in different walled castings. The results of trials have shown that the magnesium Tundish process can produce high quality vermicular graphite irons under the specific industrial conditions of Foundries - Odlewnie Polskie S.A. in Starachowice. In this work describes too preliminary studies on the oxygen state in cast iron and their effect on graphite crystallization.

Go to article

Abstract

The article presents the issues of costs analysis of iron casts manufacturing using automated foundry lines. Particular attention was paid to departmental costs, conversion costs and costs of in-plant transport. After the Pareto analysis had been carried out, it was possible to set the model area of the process and focus on improving activities related to finishing of a chosen group of casts. In order to eliminate losses, the activities realised in this domain were divided into activities with added value, activities with partially added value and activities without added value. To streamline the production flow, it was proposed to change the location of workstations related to grinding, control and machining of casts. Within the process of constant improvement of manufacturing processes, the aspect of work ergonomics at a workstation was taken into account. As a result of the undertaken actions, some activities without added value were eliminated, efficiency was increased and prime costs of manufacturing casts with regard to finishing treatment were lowered.

Go to article

Abstract

Magnesium alloys thanks to their high specific strength have an extensive potential of the use in a number of industrial applications. The most important of them is the automobile industry in particular. Here it is possible to use this group of materials for great numbers of parts from elements in the car interior (steering wheels, seats, etc.), through exterior parts (wheels particularly of sporting models), up to driving (engine blocks) and gearbox mechanisms themselves. But the use of these alloys in the engine structure has its limitations as these parts are highly thermally stressed. But the commonly used magnesium alloys show rather fast decrease of strength properties with growing temperature of stressing them. This work is aimed at studying this properties both of alloys commonly used (of the Mg-Al-Zn, Mn type), and of that ones used in industrial manufacture in a limited extent (Mg-Al-Sr). These thermomechanical properties are further on complemented with the microstructure analysis with the aim of checking the metallurgical interventions (an effect of inoculation). From the studied materials the test castings were made from which the test bars for the tensile test were subsequently prepared. This test took place within the temperature range of 20°C – 300°C. Achieved results are summarized in the concluding part of the contribution.

Go to article

Abstract

The experimental material consisted of semi-finished products of high-grade, medium-carbon constructional steel with: manganese, chromium, nickel, molybdenum and boron. The experimental material consisted of steel products obtained in three metallurgical processes: electric and desulfurized (E), electric and desulfurized with argon-refined (EA) and oxygen converter with vacuum degassed of steel (KP). The production process involved two melting technologies: in a 140-ton basic arc furnace with desulphurisation and argon refining variants, and in a 100-ton oxygen converter. Billet samples were collected to analyze: relative volume of impurities, microstructure and fatigue tests. The samples were quenched and austenitized at a temperature of 880o C for 30 minutes. They were then cooled in water and tempered by holding the sections at a temperature of 200, 300, 400, 500 and 600o C for 120 minutes and air-cooled. Fatigue tests were performed with the use of a rotary bending machine at a frequency of 6000 cpm. The results were statistical processed and presented in graphic form. This paper discusses the results of microstructural analyses, the distribution of the relative volume of impurities in different size ranges, the fatigue strength characteristics of different production processes, the average number of sampledamaging cycles and the average values of the fatigue strength coefficient for various heat processing options.

Go to article

Abstract

Homogeneity of die castings is influenced by wide range of technological parameters as piston velocity in filling chamber of die casting machine, filling time of mould cavity, temperature of cast alloy, temperature of the mould, temperature of filling chamber, surface pressure on alloy during mould filling, final pressure and others. Based on stated parameters it is clear, that main parameters of die casting are filling time of die mould cavity and velocity of the melt in the ingates. Filling time must ensure the complete filling of the mould cavity before solidification process can negatively influence it. Among technological parameters also belong the returning material, which ratio in charge must be constrained according to requirement on final homogeneity of die castings. With the ratio of returning material influenced are the mechanical properties of castings, inner homogeneity and chemical composition.

Go to article

Abstract

In contrast to casting to conventional non-reusable “sand” moulds, for which calculating technique for an optimum design of the gating system is comparatively well-developed, a trial-and-error method is applied mostly for casting to ceramic shell moulds made by the investment casting technology. A technologist selects from gating systems of several types (that are standardized by the foundry mostly) on the basis of experience. However, this approach is not sustainable with ever growing demands on quality of castings and also the economy of their fabrication as well as with new types of complex sizeable castings introduced to the production gradually (by new customers from the aircraft industry above all) any more. The simulation software may be used as a possible tool for making the process of optimising gating systems more effective.

Go to article

Abstract

Mathematical programming, constraint programming and computational intelligence techniques, presented in the literature in the field of operations research and production management, are generally inadequate for planning real-life production process. These methods are in fact dedicated to solving the standard problems such as shop floor scheduling or lot-sizing, or their simple combinations such as scheduling with batching. Whereas many real-world production planning problems require the simultaneous solution of several problems (in addition to task scheduling and lot-sizing, the problems such as cutting, workforce scheduling, packing and transport issues), including the problems that are difficult to structure. The article presents examples and classification of production planning and scheduling systems in the foundry industry described in the literature, and also outlines the possible development directions of models and algorithms used in such systems.

Go to article

Abstract

The paper presents the results of examination concerning optimization of the σ phase precipitates with respect to the functional properties of ferritic-austenitic cast steel. The examined material comprised two grades of corrosion-resistant cast steel, namely GX2CrNiMoN25-6-3 and GX2CrNiMoCuN25-6-3-3, used for example in elements of systems of wet flue gas desulphurisation in power industry. The operating conditions in media heated up to 70°C and containing Cl- and SO4 ions and solid particles produce high erosive and corrosive wear. The work proposes an application of the σ phase as a component of precipitation strengthening mechanism in order to increase the functional properties of the material. Morphology and quantities of σ phase precipitates were determined, as well as its influence on the erosion and corrosion wear resistance. It was shown that annealing at 800°C or 900°C significantly improves tribological properties as compared with the supersaturated state, and the best erosion and corrosion wear resistance achieved due to the ferrite decomposition δ → γ’ + σ was exhibited in the case of annealing at the temperature of 800°C for 3 hours.

Go to article

Abstract

Results of investigations of wear resistant of two species of cast steel were introduced in the article (low-alloyed and chromium cast steel) on the background of the standard material which was low alloy wear resistant steel about the trade name CREUSABRO ®8000. The investigations were executed with two methods: abrasive wears in the stream of loose particles (the stream of quartz sand) and abrasive wears particles fixed (abrasive paper with the silicon carbide). Comparing the results of investigations in the experiments was based about the counted wear index which characterizes the wears of the studied material in the relation to the standard material.

Go to article

Abstract

The paper presents adaptation problem of lamellar/rod growth of eutectic. The transformation of eutectic microstructure was investigated systematically. A interpretation of the eutectic growth with theory minimum entropy production was presented.

Go to article

Abstract

Production of spheroidal graphite cast iron is today quite mastered technology. There are many methods achieving the nodular graphite morphology. Each of these methods have specific characteristics and requirements to technical support, properties and the type of applied modifier. Selection of the spheroidization method is dependent on foundry disposition, production character, economic balance, quality requirements, etc. In case of centrifugally casting the core, which fills body and neck of the roll, is created by ductile iron. Considering the sophisticated production of centrifugally cast rolls for hot rolling mills it is necessary to ensure a high reproducibility and reliability of ductile cast iron production quality in the bulk range of 9-18 t per tapping. These conditions are in the Roll Foundry in Vítkovicke Slevarny, spol. s r.o. provided and verified mastered overpour method and the newly injection of cored wire in the melt.

Go to article

Abstract

Particles of the Fe-Al type (less than 50 µm in diameter) were sprayed onto the 045 steel substrate by means of the detonation method. The TEM, SAED and EDX analyses revealed that the Fe-Al particles have been partially melted in the experiment of coating formation. Particle undergone melting even within about 80% of its volume. Therefore, solidification of the melted part of particles was expected. Solidification differed significantly due to a large range of chemical composition of applied particles (from 15 at.% Al up to 63 at.% Al). A single particle containing 63 at.% Al was subjected to the detailed analysis, only. The TEM / SAED techniques revealed in the solidified part of particle three sub-layers: an amorphous phase, A ε , periodically situated FeAl + Fe2Al5 phases, and a non-equilibrium phase, Nε . A hypothesis dealing with the inter-metallic phases formation in such a single particle of the nominal composition 0 N = 0.63 is presented. At first, the solid / liquid system is treated as an interconnection: substrate liquid nonmelted particle part / / . Therefore, it is suggested that the solidification occurs simultaneously in two directions: towards a substrate and towards a non-melted part of particle. The solidification mechanism is referred to the Fe-Al meta-stable phase diagram. It is shown that the melted part of particle solidifies rapidly according to the phase diagram of meta-stable equilibrium and at a significant deviation from the thermodynamic equilibrium.

Go to article

Abstract

Shot blasting machines are widely used for automated surface treatment and finishing of castings. In shot blasting processes the stream of shots is generated and shaped by blasting turbines, making up a kinetic and dynamic system comprising a separating rotor, an adapting sleeve and a propelling rotor provided with blades. The shot blasting performance- i.e. the quality of shot treated surfaces depends on the actual design and operational parameters of the unit whilst the values of relevant parameters are associated with the geometry of turbine components and the level of its integration with the separator system. The circulation of the blasting medium becomes the integrating factor of the process line, starting from the hopper, through the propeller turbine, casting treatment, separation of contaminated abrasive mixture, to its recycling and reuse. Inferior quality of the abrasive agent (shot) and insufficient purity of the abrasive mixture are responsible for low effectiveness of shot blasting. However, most practitioners fail to fully recognize the importance of proper diagnostics of the shot blasting process in industrial conditions. The wearing of major machine components and of the blasting agent and quality of shot treated surfaces are often misinterpreted, hence the need to take into account all factors involved in the process within the frame of a comprehensive methodology. This paper is an attempt to formulate and apply the available testing methods to the engineering practice in industrial conditions.

Go to article

Abstract

In paper is presented technology of bimetallic layered castings based on founding method of layer coating directly in cast process so-called method of mould cavity preparation. Prepared castings consist two fundamental parts i.e. bearing part and working part (layer). The bearing part of bimetallic layered casting is typical foundry material i.e. unalloyed cast steel, whereas working part is plate of austenitic alloy steel sort X2CrNi 18-9. The ratio of thickness between bearing and working part is 8:1. The aim of paper was assessed the quality of the joint between bearing and working part in dependence of pouring temperature and carbon concentration in cast steel. The quality of the joint in bimetallic layered castings was evaluated on the basis of ultrasonic non-destructive testing, structure and microhardness researches.

Go to article

Abstract

The influence of aluminium (added in quantity from about 0.6% to about 2.8%) on both the alloy matrix and the shape of graphite precipitates in cast iron treated with a fixed amounts of cerium mischmetal (0.11%) and ferrosilicon (1.29%) is discussed in the paper. The metallographic examinations were carried out for specimens cut out of the separately cast rods of 20 mm diameter. It was found that the addition of aluminium in the amounts from about 0.6% to about 1.1% to the cast iron containing about 3% of carbon, about 3.7% of silicon (after graphitizing modification), and 0.1% of manganese leads to the occurrence of the ferrite-pearlite matrix containing cementite precipitates in the case of the treatment of the alloy with cerium mischmetal . The increase in the quantity of aluminium up to about 1.9% or up to about 2.8% results either in purely ferrite matrix in this first case or in ferrite matrix containing small amounts of pearlite in the latter one. Nodular graphite precipitates occurred only in cast iron containing 1.9% or 2.8% of aluminium, and the greater aluminium content resulted in the higher degree of graphite spheroidization. The noticeable amount of vermicular graphite precipitates accompanied the nodular graphite.

Go to article

Abstract

The paper addresses the macro- and microsegregation of alloying elements in the new-developed Mn-Al TRIP steels, which belong to the third generation of advanced high-strength steels (AHSS) used in the automotive industry. The segregation behaviour both in the as-cast state and after hot forging was assessed in the macro scale by OES and by EDS measurements in different structural constituents. The structural investigations were carried out using light and scanning electron microscopy. A special attention was paid to the effect of Nb microaddition on the structure and the segregation of alloying elements. The tendency of Mn and Al to macrosegregation was found. It is difficult to remove in Nb-free steels. Microsegregation of Mn and Al between austenite and ferritic structural constituents can be removed.

Go to article

Abstract

The modification of the chemical composition of non-metallic inclusions by rare-earth elements in the new-developed microalloyed steels was discussed in the paper. The investigated steels are assigned to production of forged elements by thermomechanical treatment. The steels were melted in a vaccum induction furnace and modification of non-metallic inclusions was carried out by the michmetal in the amount of 2.0 g per 1 kg of steel. It was found that using material charge of high purity and a realization of metallurgical process in vacuous conditions result in a low concentration of sulfur (0.004%), phosphorus (from 0.006 to 0.008%) and oxygen (6 ppm). The high metallurgical purity is confirmed by a small fraction of non-metallic inclusions averaging 0.075%. A large majority of non-metallic inclusions are fine, globular oxide-sulfide or sulfide particles with a mean size 17 µm2 . The chemical composition and morphology of non-metallic inclusions was modified by Ce, La and Nd, what results a small deformability of nonmetallic inclusions during hot-working.

Go to article

Abstract

The most important parameters which predetermine mechanical properties of a material in aspects of suitability for castings to machinery components are: tensile strength (Rm), elongation (A5, hardness (HB) and impact strength (KCV). Heat treatment of aluminum alloys is performed to increase mechanical properties of the alloys mainly. The paper comprises a testing work concerning effect of heat treatment process consisting of solution heat treatment and natural ageing on mechanical properties and structure of AlZn10Si7MgCu alloy moulded in metal moulds. Investigated alloy was melted in an electric resistance furnace. Run of crystallization was presented with use of thermal-derivative method (ATD). This method was also implemented to determination of heat treatment temperature ranges of the alloy. Performed investigations have enabled determination of heat treatment parameters’ range, which conditions suitable mechanical properties of the investigated alloy. Further investigations will be connected with determination of optimal parameters of T6 heat treatment of the investigated alloy and their effect on change of structure and mechanical/technological properties of the investigated alloy.

Go to article

Abstract

The work presents the results of the research and tests of the surface machining of the S355NL and X5CrNi18-10 steels with the concentraded stream of heat with the usage of the GTAW method. The surface layers of the tested steels were remelted with the electric arc using the current of the electric arc 50, 100, 150 and 200A.The machining was done in the atmosphere of argon with the constant speed of the welding head. A microscope examination was performed of the obtained structure and measurements of depth, width and hardness of the received surface layer were performed. Moreover the relation between the current of the electric arc and geometry of the remelted layers with their microhardness was examined.

Go to article

Abstract

To the main advantages of magnesium alloys belongs their low density, and just because of such property the alloys are used in aviation and rocket structures, and in all other applications, where mass of products have significant importance for conditions of their operation. To additional advantages of the magnesium alloys belongs good corrosion resistance, par with or even surpassing aluminum alloys. Magnesium is the lightest of all the engineering metals, having a density of 1.74 g/cm3 . It is 35% lighter than aluminum (2.7 g/cm3 ) and over four times lighter than steel (7.86 g/cm3 ). The Mg-Li alloys belong to a light-weight metallic structural materials having mass density of 1.35-1.65 g/cm3 , what means they are two times lighter than aluminum alloys. Such value of mass density means that density of these alloys is comparable with density of plastics used as structural materials, and therefore Mg–Li alloys belong to the lightest of all metal alloys. In the present paper are discussed melting and crystallization processes of ultra-light weight MgLi12,5 alloys recorded with use of ATND methods. Investigated magnesium alloy was produced in Krakow Foundry Research Institute on experimental stand to melting and casting of ultra-light weight alloys. Obtained test results in form of recorded curves from ATND methods have enabled determination of characteristic temperatures of phase transitions of the investigated alloy.

Go to article

Abstract

Skeleton castings macrostructure can be shaped in many ways, by choosing an appropriate material of cores and manufacturing technologies. Important factor, which puts foundry techniques over the other technologies of periodic cellular materials, is ability to adjust mechanical properties by changing the microstructure of an alloy from which the casting is made. The influence on the microstructure of the skeleton casting can be implemented by choosing the thermal properties, mainly thermal conductivity factor, of mould and core materials. Macro- and microstructure of skeleton castings with octahedron elementary cells was presented in this paper. The analysis concerns the differences in morphology of eutectic silicone depending on the location of measurements cross sections areas. The use of thermo-insulating material with appropriate properties assures correct fill of mould cavity and homogeneous microstructure on whole volume of skeleton casting. The selection of technological parameters of the casting process if very important as well.

Go to article

Abstract

The paper presents the possibility of the usage of the concfocal microscope for define the type of tribological wear present during the technical dry friction on the testing machine of the pin-on-disc T-01M. The pin was a remelted high-speed steel and the disc was made from sintered carbides. The surface layer of the high-speed steel was remelted with the electric arc with different parameters. The intensity of the electric arc current was changed, the scanning speed and the single, overlapping remeltings were used. On the basis of the 3D, 2D view of the surface friction of the pin (made from the remelted high-speed steel), disc (made from the sintered carbides) and the surface roughness profile run along the marked line, the presence of the abrasive wear can be defined with the description of the elementary wear processes due to the abrasive and/or adhesive wear.

Go to article

Abstract

The aim of that work was the evaluation of the quality of welded connections elements (welds) from the 30HGS steel and titanium alloy Ti6Al4V. The metallographic, factographic tests were used, and measurements of microhardness with the Vickers method. In the head weld of the 30HGS steel there were non-metallic partial division and bubbles observed. The average microhardness in the head connection was 320 HV0.1. There was no significant increase/decrease observed of microhardness in the head influence zone of the weld. There was a good condition of head connections observed, in accordance with the standard EN12517 and EN25817. In the head weld of Ti6Al4V titanium alloy there were single, occasional non-metallic interjections and bubbles observed. There were no cracks both on the weld, and on the border of the heat influence zone. The value of microhardness in head connection was in the range 300÷445 HV0.1. Reveal a very good condition of the head connections in accordance with the standard EN12517 and EN25817. The factographic tests prove the correctness of welded connections done and then heat treatment in case of steel and titanium alloy.

Go to article

Abstract

The study presented here is related with one of the components of a hybrid decision support system called CAPCAST (Computer Aided Process - CAST), developed under a research project at the Faculty of Metals Engineering and Industrial Computer Science, AGH University of Science and Technology. This is a module for rule generation to serve the knowledge base operating in an expert system. The scope of the system operation involves the selection of technological parameters for the manufacture of machine parts from ductile iron. However, it can be extended to include other materials and technologies.

Go to article

Abstract

The article presents analysis of the influence of ingate size on the Lost Foam casting process. In particular, analysis of simulation tests has been carried out to determine the ingate size influence on the rate of filling of the mould cavity, pressure in the gas gap and size of the gas gap. A specially prepared mathematical model of the process and an original calculation algorithm were used in simulation tests of full-mould casting. The tests have indicated that the increase of the ingate size results in the increase of filling rate and increase of pressure of gases in the gas gap. However, significant influence on mould cavity filling occurs only when the ingate size is less than ~1 cm2.

.

Go to article

Abstract

The article presents the results of the research on the influence of the shape of reaction chamber on spheroidisation of cast iron produced with use of the inmold method. The amounts of nodular graphite precipitates in castings produced with the use of different reaction chambers have been compared.

Go to article

Abstract

The paper presents results of studies on the effect of the nodular cast iron metal matrix composition on the abrasive and adhesive wear resistance. Nodular cast iron with different metal matrix obtained in the rough state and ADI were tested. To research of abrasive and adhesive wear the pearlitic and bainitic cast iron with carbides and without this component were chosen. The influence of the carbides amount for cast iron wear resistance was examined. It was found, that the highest abrasive and adhesive wear resistance under conditions of dry friction has a nodular cast iron with carbides with upper and lower bainite. Carbides in bainitic and pearlitic cast iron significantly increase the wear resistance in these conditions. In terms of fluid friction the largest wear resistance had cast iron group with the highest hardness.

Go to article

Abstract

This paper presents the influence of annealing time 30, 60 and 120 min at 1000°C for quenching CuAl7Fe5Ni5W2Si2 bronze in 10% water solution of NaCl, on the microstructure and mechanical properties. The presented results concern the species newly developed aluminum-iron-nickel bronze, with additions W and Si. In order to determine changes in the microstructure of the hardened bronze metallographic studies were performed on cylindrical samples of diameter 10 mm, on the metallographic microscope with digital image analysis, X-ray phase analysis, EDX point with the digital recording on the computer. Specified percentage of the microstructure of martensite and bainite, participation of proeutectoid α phase in the microstructure, grain size of former β phase, the amount of dissolved κ phase. It was found that in the microstructure of bronze in the cast state, there are a number of intermetallic phases of κ type. At interphase boundaries of primary intermetallic faceted precipitates, especially rich in tungsten (IM_W), nucleate and grow dendritic primary intermetallic κI phases, with chemical composition similar to the type of Fe3Si iron silicide. Dissolved, during the heating, in the β phase are all the intermediate phase included in the microstructure, with the exception of primary intermetallic phases of tungsten and κI. Prolongation of the isothermal annealing causes coagulation and coalescence of primary phases. In microstructure of the bronze after quenching obtained the α phase precipitation on the grain boundary of secondary β phase, coarse bainite and martensite, for all annealing times. With the change of annealing time are changed the relative proportions of individual phases or their systems, in the microstructure. In the microstructure of bronze, hold at temperature of 1000°C for 60 min, after quenching martensitic microstructure was obtained with the primary phases, and the least amount of bainite

Go to article

Abstract

Until now, the mould sand in general use in the foundry industry are based on bentonite, which resulted from the fact that a good recognition properties and phenomena associated with this material. Come to know and normalized content of montmorillonite and carbonates and their important role in the construction of bentonite, and mass properties of the participation of compressive strength or scatter. Halloysite is widely used in industry and beyond them. However, little is known about its use in the foundry in Poland and abroad. This article presents preliminary research conducted at the Foundry Department of Silesian University of Technology on this material. Will raise the question of the representation of this two materials, which contains information connected with history and formation of materials, their structure and chemical composition. In the research, the results of compressive strength tests in wet masses of quartz matrix, where as a binder is used halloysite and bentonite in different proportions.

Go to article

Abstract

Structure, and thus the mechanical properties of steel are primarily a function of chemical composition and the solidification process which can be influenced by the application of the inoculation treatment. This effect depends on the modifier used. The article presents the results of studies designed to assess the effects of structural low alloy steel inoculation by selected modifying additives. The study was performed on nine casts modeled with different inoculants, assessment of the procedure impact was based on the macrostructure of made castings. The ratio of surface area equivalent to the axial zone of the crystals and columnar crystals zone was adopted as a measure of the inoculation effect.

Go to article

Abstract

The work presents the analysis results of the structure of the coat obtained by dipping in silumin AlSi5 of two grades of alloy cast steel: GX6CrNiTi18-10 (LH18N9T) and GX39Cr13 (LH14). The temperature of the silumin bath was 750±5°C, and the hold-up time of the cast steel element τ = 180 s. The absolute thickness of the coat obtained in the given conditions was g = 104 μm on cast steel GX6CrNiTi18-10 and g = 132 μm on GX39Cr13. The obtained coat consisted of three layers of different phase structure. The first layer from the base “g1`” was constructed of the phase AlFe including Si and alloy additives of the tested cast steel grades: Cr and Ni (GX6CrNiTi18-10) and Cr (GX39Cr13). The second layer “g1``” of intermetallic phases AlFe which also contains Si and Cr crystallizes on it. The last, external layer “g2” of the coat consists of the silumin containing the intermetallic phases AlFeSi which additionally can contain alloy additives of the cast steel. It was shown that there were no carbides on the coat of the tested cast steels which are the component of their microstructure, as it took place in the case of the coat on the high speed steels.

Go to article

Abstract

The paper presents the results of abrasive wear resistance tests carried out on high-vanadium cast iron with spheroidal VC carbides. The cast iron of eutectic composition was subjected to spheroidising treatment using magnesium master alloy. The tribological properties were examined for the base cast iron (W), for the cast iron subjected to spheroidising treatment (S) and for the abrasion-resistant steel (SH). Studies have shown that high-vanadium cast iron with both eutectic carbides and spheroidal carbides has the abrasion resistance twice as high as the abrasion-resistant cast steel. The spheroidisation of VC carbides did not change the abrasion resistance compared to the base high-vanadium grade.

Go to article

Abstract

This work presents the technology of making foam plastics patterns used in casting as well as the final shaping stand. The analysis of the sintering process was carried out aiming at determining the influence of the pressure and the time of sintering on the flexural strength properties. The analysis of the research results confirmed that when the sintering pressure grows to the value of Pa =1,7 bar the flexural strength also increases, when the pressure value is higher than that, the degradation of the material takes place and the strength properties decrease.

Go to article

Abstract

The current work presents the research results of abrasion wear and adhesive wear at rubbing and liquid friction of new austenitic, austenitic-ferritic (“duplex”) cast steel and gray cast iron EN-GJL-250, spheroidal graphite iron EN-GJS-600-3, pearlitic with ledeburitic carbides and spheroidal graphite iron with ledeburitic carbides with a microstructure of the metal matrix: pearlitic, upper bainite, mixture of upper and lower bainite, martensitic with austenite, pearlitic-martensitic-bainitic-ausferritic obtained in the raw state. The wearing quality test was carried out on a specially designed and made bench. Resistance to abrasion wear was tested using sand paper P40. Resistance to adhesive wear was tested in interaction with steel C55 normalized, hardened and sulfonitrided. The liquid friction was obtained using CASTROL oil. It was stated that austenitic cast steel and “duplex” are characterized by a similar value of abrasion wear and adhesive wear at rubbing friction. The smallest decrease in mass was shown by the cast steel in interaction with the sulfonitrided steel C55. Austenitic cast steel and “duplex” in different combinations of friction pairs have a higher wear quality than gray cast iron EN-GJL250 and spheroidal graphite iron EN-GJS-600-3. Austenitic cast steel and “duplex” are characterized by a lower wearing quality than the spheroidal graphite iron with bainitic-martensitic microstructure. In the adhesive wear test using CASTROL oil the tested cast steels and cast irons showed a small mass decrease within the range of 1÷2 mg.

Go to article

Abstract

Article present various forms of transfer of information available on the Internet. An attempt was made to show the possibility of such a selection of the knowledge sources that, taking into account user preferences, would arouse his interest, showing in parallel the intended substantive content. This commitment is shown in the context of the current assumptions of building a platform dedicated to support the needs of production processes in foundry and metallurgy.

Go to article

Abstract

The work is a continuation of research on the use water mist cooling in order to increase efficiency of die-casting aluminum alloys. The paper presents results of research and analysis process, spraying water and generated a stream of water mist, the effect of the type of nozzle, the nozzle size and shape of the emitting of the water mist on the wall surface of casting die on the microstructure and geometry of water mist stream and cooling efficiency. Tests were used to perform high-speed camera to record video in the visible and infrared camera. Results were used to develop a computerized image analysis and statistical analysis. The study showed that there are statistical relationships between water and air flow and geometry of the nozzle and nozzle emitting a stream of microstructure parameters of water mist and heat the incoming stream. These relationships are described mathematical models that allow you to control the generating of adequate stream of water mist and a further consequence, the cooling efficiency of casting die.

Go to article

Abstract

In this work, the change of the structure and microhardness of Ti6Al4V titanium alloy after remelting and remelting with SiC alloing by electric arc welding (GTAW method) was studied. The current intensity equal 100 A and fixed scan speed rate equal 0,2 m/min has been used to remelting surface of the alloy. Change of structure were investigated by optical and scanning electron microscopy. Microhardness test showed, that the remelting of the surface does not change the hardness of the alloy. Treated by GTAW SiC alloying leads to the formation of hard (570 HV0, 1) surface layer with a thickness of 2 mm. The resulting surface layer is characterized by diverse morphology alloyed zone. The fracture of alloy after conventional heat treatment, similarly to fracture after remelting with GTAW is characterized by extremely fine dimples of plastic deformation. In the alloyed specimens the intergranular and crystalline fracture was identified.

Go to article

Abstract

Vacuum conditions in foundry installations are generated using electric-driven vacuum pumps. The purpose of the experiment is to evaluate the performance of a vacuum-assisted system for compaction of moulding sand basing on registered plots of selected electric power parameters of the power-supplying system of the pumps. Model testing done on an experimental vacuum system installation, power-supplied from a system incorporating the recorders of instantaneous current and voltage values. Following the numerical procedure, the experimental data are analysed to yield mathematical relationships between the variations of the generated vacuum pressure levels and variations of selected electric power parameters. Registered and computed values of selected parameters: instantaneous and RMS voltage and current values, active, reactive and apparent power levels and power coefficient allow for diagnosing the adequacy and reliability of the system operation. According to the authors, the applied monitoring of the power parameters of a vacuum-assisted installation may become an effective and easy practical method of evaluating the performance of such installations, used also in foundry plants.

Go to article

Abstract

This article contains information concerning of the analysis the possibility of defining refinery qualities of the slag based thermophysical and thermodynamical data. The paper presents a model of slag refining processes and a method of determining the reduction capability of slag solutions. Slag was analysed with the use of the DTA methods for the brass melting conductions. The study of computer program including the satisfactory number of data there are used in to the design a modern device rotating head used for gas-slag refining. It was achieved that the refining gas and fluxes were distributed ever by the rotating head. High effectiveness of the gas-slag refining processes was proved for the brass.

Go to article

Editorial office

CHIEF EDITORS
Editor
J. Szajnar
Deputy Editor
J. Jezierski

SUBJECT EDITORS
Theoretical Aspects of Casting Processes
K. Eigenfeld – Freiberg, Germany
E. Guzik – Kraków, Poland
T. G. Mathia - Lyon, France
W. Wołczyński – Kraków, Poland
Innovative Foundry Technologies and Materials
T. Elbel – Ostrava, Czech Republic
Z. Ignaszak – Poznań, Poland
O. P. Pandey – Punjab, India
A. Pereira - Vigo, Spain
Foundry Processes Computer Aiding
B. Mochnacki – Częstochowa, Poland
J. Roučka – Brno, Czech Republic
J.S. Suchy – Kraków, Poland
Mechanization, Automation and Robotics in Foundry
J. Bast – Freiberg, Germany
R. Wrona – Kraków, Poland
Transport Systems in Foundry
J. Dańko – Kraków, Poland
Z. Li – Shijiazhuang, China
Castings Quality Management
D. Bolibruchova– Żilina, Slovak Republic
J. D. B. de Mello - Santa Monica, Brazil
M. Perzyk – Warszawa, Poland
Environment Protection
M. Holtzer – Kraków, Poland
H. Polzin – Freiberg, Germany
J. Sobczak – Kraków, Poland
I. Volchok – Zaporizhzhya, Ukraine

EDITORIAL ADVISORY BOARD
J. Braszczyński – Częstochowa, Poland
B. K. Dhindaw – Rupnagar, India
L. A. Dobrzański – Gliwice, Poland
W. A. Hufenbach – Dresden, Germany
P. Jelínek – Ostrava, Czech Republic
L. Jeziorski – Częstochowa, Poland
J. Lacaze – Toulouse, France
V. L. Naydek – Kiev, Ukraine
A. Passerone – Genova, Italy
I. Riposan – Bucharest, Romania
F. Romankiewicz – Zielona Góra, Poland
A. Sládek – Żilina, Slovak Republic

INTERNATIONAL SCIENTIFIC REVIEW COMMITTEE
S. A. Argyropoulos – Toronto, Canada
M. Azadi – Tehran, Iran
Y. Babaskin – Kiev, Ukraine
K. Bako – Miskolc, Hungary
E. Bayraktar – Paris, France
L. Bechný – Zilina, Slovak Republic
V. Bednarova - Ostrava, Czech Republic
F. Bińczyk – Katowice, Poland
A. Bokota – Częstochowa, Poland
G.P. Borisov – Kiev, Ukraine
A. Bydałek – Kraków, Poland
C. H. Cáceres – Brisbane, Australia
J. Čech – Brno, Czech Republic
L. Q. Chen – Shenyang, China
A. Chojecki – Kraków, Poland
M. Cholewa – Gliwice, Poland
I. A. Dibrov – Moscow, Russia
D. Dispinar – Istanbul, Turkey
S. M. Dobosz – Kraków, Poland
V. I. Dubodelov – Kiev, Ukraine
A. Fedoryszyn – Krakow, Poland
J. Głownia – Kraków, Poland
K. Granat – Wrocław, Poland
J. Hampl – Ostrava, Czech Republic
J. Helber – Düsseldorf, Germany
M. Hetmańczyk – Katowice, Poland
M. Horáček – Brno, Czech Republic
M. Kaczorowski – Warszawa, Poland
W. Kapturkiewicz – Kraków, Poland
R. Kawalla – Freiberg, Germany
Z. Konopka – Czestochowa, Poland
D. Kopyciński – Kraków, Poland
W. K. Krajewski – Kraków, Poland
Z. Libo – Beijing, China
P. Lichy – Ostrava, Czech Republic
Y. P. Lim – Setapak, Malaysia
T. Lipiński – Olsztyn, Poland
E. Majchrzak – Gliwice, Poland
A. Mityayev - Zaporizhzhya, Ukraine
M. Murgaš – Trnava, Slovak Republic
I. Nová – Liberec, Czech Republic
W. Orłowicz – Rzeszów, Poland
T. Pacyniak – Łódź, Poland
B. Piekarski – Szczecin, Poland
A. Rimmer – West Bromwich, United Kingdom
S. Samavedam – Hyderabad, India
P. Schumacher – Leoben, Austria
N. Sczygiol – Częstochowa, Poland
P. Skočovský – Żilina, Slovak Republic
M.S. Soiński – Częstochowa, Poland
J. Sokolowski – Ottawa, Kanada
K. V. Sudhakar – Butte, USA
B. G. Thomas - Champaign, USA
M. Trbižan – Ljubljana, Slovenia
J. Vuorinen – Tampere, Finland
E. Ziółkowski – Kraków, Poland
J. Zych – Kraków, Poland

ASSOCIATE EDITORS
D. Bartocha – Gliwice, Poland, - editorial secretary
J. Suchoń – Gliwice, Poland - editorial secretary
J. Szymszal – Katowice, Poland, Statistic Editor
A. Dulska – Gliwice, Poland
M. Kondracki – Gliwice, Poland
C. Borek –Chicago, USA, Language Editor

 

Contact

ul. Towarowa 7,
44-100 Gliwice, Poland
e-mail: kikm@polsl.pl

This page uses 'cookies'. Learn more