TitleThe Structure of the Silumin Coat on Alloy Cast Steels
Journal titleArchives of Foundry Engineering
KeywordsInnovative Casting Technologies ; Dip Coating ; Alloy Cast Steel ; Silumin
Divisions of PASNauki Techniczne
Archives of Foundry Engineering continues the publishing activity started by Foundry Commission of the Polish Academy of Sciences (PAN) in Katowice in 1978. The initiator of it was the first Chairman Professor Dr Eng. Wacław Sakwa – Corresponding Member of PAN, Honorary Doctor of Czestochowa University of Technology and Silesian University of Technology. This periodical first name was „Solidification of Metals and Alloys” , and made possible to publish the results of works achieved in the field of the Basic Problems Research Cooperation. The subject of publications was related to the title of the periodical and concerned widely understand problems of metals and alloys crystallization in a casting mold. In 1978-2000 the 44 issues have been published. Since 2001 the Foundry Commission has had patronage of the annually published “Archives of Foundry” and since 2007 quarterly published “Archives of Foundry Engineering”. Thematic scope includes scientific issues of foundry industry:
- Theoretical Aspects of Casting Processes,
- Innovative Foundry Technologies and Materials,
- Foundry Processes Computer Aiding,
- Mechanization, Automation and Robotics in Foundry,
- Transport Systems in Foundry,
- Castings Quality Management,
- Environmental Protection.
The work presents the analysis results of the structure of the coat obtained by dipping in silumin AlSi5 of two grades of alloy cast steel: GX6CrNiTi18-10 (LH18N9T) and GX39Cr13 (LH14). The temperature of the silumin bath was 750±5°C, and the hold-up time of the cast steel element τ = 180 s. The absolute thickness of the coat obtained in the given conditions was g = 104 μm on cast steel GX6CrNiTi18-10 and g = 132 μm on GX39Cr13. The obtained coat consisted of three layers of different phase structure. The first layer from the base “g1`” was constructed of the phase AlFe including Si and alloy additives of the tested cast steel grades: Cr and Ni (GX6CrNiTi18-10) and Cr (GX39Cr13). The second layer “g1``” of intermetallic phases AlFe which also contains Si and Cr crystallizes on it. The last, external layer “g2” of the coat consists of the silumin containing the intermetallic phases AlFeSi which additionally can contain alloy additives of the cast steel. It was shown that there were no carbides on the coat of the tested cast steels which are the component of their microstructure, as it took place in the case of the coat on the high speed steels.
PublisherThe Katowice Branch of the Polish Academy of Sciences
TypeArtykuły / Articles
ReferencesPietrowski S. (2008), The structure of the alphinizing coat on alloy steels, Archives of Foundry Engineering, 8, 4, 229. ; Pietrowski S. (2010), Alfinated coating structure on HS6-5-2 (SW7M) high speed steel, Archives of Foundry Engineering, 10, 4, 191. ; Malkiewicz T. (1976), Metal science of iron-base alloy. ; Dobrzański L. (2006), Engineering materials and material planning. ; Colombier L. (1964), Steels resistant to corrosion and heat-resistant steel.