Preliminary Research on Granulation Process of Dust Waste from Reclamation Process of Moulding Sands with Furan Resin

Journal title

Archives of Foundry Engineering

Yearbook

2012

Numer

No 3

Publication authors

Keywords

Moulding sands ; After reclamation dust ; Granulation ; Environment protection

Divisions of PAS

Nauki Techniczne

Description

Archives of Foundry Engineering continues the publishing activity started by Foundry Commission of the Polish Academy of Sciences (PAN) in Katowice in 1978. The initiator of it was the first Chairman Professor Dr Eng. Wacław Sakwa – Corresponding Member of PAN, Honorary Doctor of Czestochowa University of Technology and Silesian University of Technology. This periodical first name was „Solidification of Metals and Alloys” , and made possible to publish the results of works achieved in the field of the Basic Problems Research Cooperation. The subject of publications was related to the title of the periodical and concerned widely understand problems of metals and alloys crystallization in a casting mold. In 1978-2000 the 44 issues have been published. Since 2001 the Foundry Commission has had patronage of the annually published “Archives of Foundry” and since 2007 quarterly published “Archives of Foundry Engineering”. Thematic scope includes scientific issues of foundry industry:

  • Theoretical Aspects of Casting Processes,
  • Innovative Foundry Technologies and Materials,
  • Foundry Processes Computer Aiding,
  • Mechanization, Automation and Robotics in Foundry,
  • Transport Systems in Foundry,
  • Castings Quality Management,
  • Environmental Protection.

Abstract

The results of investigations of the granulation process of foundry dusts generated in the dry mechanical reclamation process of used sands, where furan resins were binders are presented in the paper. Investigations concerned producing of granules of the determined dimensions and strength parameters. Granules were formed from the dusts mixture consisting in 50 mass% of dusts obtained after the reclamation of the furane sands and in 50 mass % of dusts from sands with bentonite. Dusts from the bentonite sands with water were used as a binder allowing the granulation of after reclamation dusts from the furane sands. The following parameters of the ready final product were determined: moisture content (W), shatter test of granules (Wz) performed directly after the granulation process and after 1, 3, 5, 10 days and nights of seasoning, water-resistance of granules after 24 hours of being immersed in water, surface porosity ep and volumetric porosity ev. In addition the shatter test and water-resistance of granulate dried at a temperature of 105oC were determined. Investigations were performed at the bowl angle of inclination 45o, for three rotational speeds of the bowl being: 10, 15, 20 rpm. For the speed of 10 rpm the granulation tests of dusts mixture after the preliminary mixing in the roller mixer and with the addition of water-glass in the amount of 2% in relation to the amount of dust were carried out. The obtained results indicate that the granulator allows to obtain granules from dusts originated from the reclamations of moulding sands with the furane resin with an addition of dusts from the bentonite sands processing plants.