TitleAnalysis of Solidification Parameters and Macrostructure of IN-713C Castings after Complex Modification
Journal titleArchives of Foundry Engineering
KeywordsNickel alloys ; Superalloys ; modification ; Inoculation ; Solidification ; Thermal analysis ; Macrostructure
Divisions of PASNauki Techniczne
Archives of Foundry Engineering continues the publishing activity started by Foundry Commission of the Polish Academy of Sciences (PAN) in Katowice in 1978. The initiator of it was the first Chairman Professor Dr Eng. Wacław Sakwa – Corresponding Member of PAN, Honorary Doctor of Czestochowa University of Technology and Silesian University of Technology. This periodical first name was „Solidification of Metals and Alloys” , and made possible to publish the results of works achieved in the field of the Basic Problems Research Cooperation. The subject of publications was related to the title of the periodical and concerned widely understand problems of metals and alloys crystallization in a casting mold. In 1978-2000 the 44 issues have been published. Since 2001 the Foundry Commission has had patronage of the annually published “Archives of Foundry” and since 2007 quarterly published “Archives of Foundry Engineering”. Thematic scope includes scientific issues of foundry industry:
- Theoretical Aspects of Casting Processes,
- Innovative Foundry Technologies and Materials,
- Foundry Processes Computer Aiding,
- Mechanization, Automation and Robotics in Foundry,
- Transport Systems in Foundry,
- Castings Quality Management,
- Environmental Protection.
AbstractThe paper presents a research results concerning impact of volume modification (ceramic filter containning cobalt aluminate and hafniumpowder) and simultaneous surface and volume modification on solidification and stereological parameters of macrostructure of castingsmade from post-production scrap of nickel superalloy IN-713C. Research included investigation of the influence of chemical compositionon the temperature Tliq i Tsol and evaluation of following macrostructure parameters: the number of grains per mm2, average grain area andshape coefficient. Results indicate high influence of carbon content on Tliq. Macrostructure of sample castings indicate positive effect of surface and volume modification, however impact of surface modification is more pronounced.