TitleInfluence of Chemical Composition on Porosity in Aluminium Alloys
Journal titleArchives of Foundry Engineering
KeywordsAluminium ; Porosity ; chemical composition
Divisions of PASNauki Techniczne
Archives of Foundry Engineering continues the publishing activity started by Foundry Commission of the Polish Academy of Sciences (PAN) in Katowice in 1978. The initiator of it was the first Chairman Professor Dr Eng. Wacław Sakwa – Corresponding Member of PAN, Honorary Doctor of Czestochowa University of Technology and Silesian University of Technology. This periodical first name was „Solidification of Metals and Alloys” , and made possible to publish the results of works achieved in the field of the Basic Problems Research Cooperation. The subject of publications was related to the title of the periodical and concerned widely understand problems of metals and alloys crystallization in a casting mold. In 1978-2000 the 44 issues have been published. Since 2001 the Foundry Commission has had patronage of the annually published “Archives of Foundry” and since 2007 quarterly published “Archives of Foundry Engineering”. Thematic scope includes scientific issues of foundry industry:
- Theoretical Aspects of Casting Processes,
- Innovative Foundry Technologies and Materials,
- Foundry Processes Computer Aiding,
- Mechanization, Automation and Robotics in Foundry,
- Transport Systems in Foundry,
- Castings Quality Management,
- Environmental Protection.
Porosity is one of the major defects in aluminum castings, which results is a decrease of a mechanical properties. Porosity in aluminum alloys is caused by solidification shrinkage and gas segregation. The final amount of porosity in aluminium castings is mostly influenced by several factors, as amount of hydrogen in molten aluminium alloy, cooling rate, melt temperature, mold material, or solidification interval. This article deals with effect of chemical composition on porosity in Al-Si aluminum alloys. For experiment was used Pure aluminum and four alloys: AlSi6Cu4, AlSi7Mg0, 3, AlSi9Cu1, AlSi10MgCu1.
PublisherThe Katowice Branch of the Polish Academy of Sciences
TypeArtykuły / Articles