The Precipitation Processes and Mechanical Properties of Aged Inconel 718 Alloy After Annealing

Journal title

Archives of Metallurgy and Materials

Yearbook

2017

Numer

No 3

Publication authors

Keywords

Metals and Alloys

Divisions of PAS

Nauki Techniczne

Abstract

<jats:title>Abstract</jats:title><jats:p>Inconel 718 is a precipitation hardenable nickel-iron based superalloy. It has exceptionally high strength and ductility compared to other metallic materials. This is due to intense precipitation of the γ’ and γ” strengthening phases in the temperature range 650-850°C. The main purpose of the authors was to analyze the aging process in Inconel 718 obtained in accordance with AMS 5596, and its effect on the mechanical properties. Tensile and hardness tests were used to evaluate the mechanical properties, in the initial aging process and after reheating, as a function of temperature and time respectively in the ranges 650°-900°C and 5-480 min. In addition, to link the mechanical properties with the microstructure transmission microscopy observations were carried out in selected specimens. As a result, factors influencing the microstructure changes at various stages of strengthening were observed. The authors found that the γ’’ phase nucleates mostly homogenously in the temperature range 650-750°C, causing the greatest increase in strength. On the other hand, the γ’ and δ phases are formed heterogeneously at 850°C or after longer annealing in 800°C, which may weaken the material.</jats:p>

Publisher

Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Commitee on Metallurgy of Polish Academy of Sciences

Date

2017

Identifier

ISSN 1733-3490

DOI

10.1515/amm-2017-0259

×