First part of the article describes how we can by change of gating system achieve better homogeneity of product made by investment casting. Turbine engine flap was made by investment casting technology – lost wax casting. The casting process was realised in vacuum. The initial conditions (with critical occurrence of porosity) was simulated in ProCAST software. Numerical simulation can clarify during analysis of melt turbulent flow in gate system responsible for creation of entrained oxide films. After initial results and conclusions, the new gating system was created with subsequent turbulence analysis. The new design of gating system support direct flow of metal and a decrease of porosity values in observed areas was achieved. Samples taken from a casting produced with use of newly designed gating system was processed and prepared for metallography. The second part of article deals with identification of structural components in used alloy - Inconel 718. The Ni – base superalloys, which are combined unique physical and mechanical properties, are used in aircraft industry for production of aero engine most stressed parts, as are turbine blades.
Porosity is one of the major defects in aluminum castings and results in a decrease of the mechanical properties of Al-Si alloys. It is induced by two mechanisms: solidification shrinkage and gas segregation. One of the methods for complex evaluation of macro and micro porosity in Al-Si alloys is using the Tatur test technique. This article deals with the evaluation of porosity with the help of Tatur tests for selected Al-Si alloys. These results will be compared with results obtained from the ProCAST simulation software.
Porosity is one of the major defects in aluminum castings, which results is a decrease of a mechanical properties. Porosity in aluminum alloys is caused by solidification shrinkage and gas segregation. The final amount of porosity in aluminium castings is mostly influenced by several factors, as amount of hydrogen in molten aluminium alloy, cooling rate, melt temperature, mold material, or solidification interval. This article deals with effect of chemical composition on porosity in Al-Si aluminum alloys. For experiment was used Pure aluminum and four alloys: AlSi6Cu4, AlSi7Mg0, 3, AlSi9Cu1, AlSi10MgCu1.
The work deals with technology Patternless process that combines 3 manufacturing process mold by using rapid prototyping technology, conventional sand formation and 3D milling. It's unconventional technology that has been developed to produce large-sized and heavyduty castings weighing up to several tons. It is used mainly in prototype and small batch production, because eliminating production of models. The work deals with the production of blocks for making molds of gypsum and gypsum drying process technology Thermomold. Into blocks, where were made cavities by milling were casted test castings from AlSi10MgMn alloy by gravity casting. At machining of the mold cavity was varied feed rate of tool of cemented carbide. Evaluated was the surface roughness of test castings, that was to 5 micrometers with feed from 900 to 1300 mm/min. The dimensional accuracy of castings was high at feed rate of 1000 and 1500 mm/min did not exceed 0.025 mm.
This paper considers the assessment of attenuation in aluminium alloys castings and in cast iron prepared by gravity casting method and by casting under pressure. The issue of ultrasound attenuation is important in setting the conditions of non-destructive (NDT) testing, especially in casted materials. The characteristics of the ultrasonic technique and ultrasonic attenuation and the calculation of the attenuation and the velocity of ultrasound are presented in the theoretical part of this paper. For experimental measurements, cylindrical castings from AlSi alloy (a hypoeutectic alloy with a silicon content of about 7% - AlSi7 and a eutectic alloy with a silicon content of about 12% - AlSi12) and from grey and ductile cast iron were made. The ultrasonic records of the casting control, the calculation of ultrasound attenuation for individual samples are listed and described in the experimental part. The evaluation of measurements and comparison of calculated ultrasound attenuation is at the end of this article.