Abstract

In this study T6 heat treated 6063 aluminum alloys were used as substrate material. In order to form a bond between the substrate and the main coating, all samples were coated with Ni-Cr-Al powders. 8 wt% Yttria Stabilized Zirconia powders (YSZ) were coated with plasma spray technique. Thickness of YSZ was 150 m and bond coating was 36 m. XRD and SEM-EDS analyses were performed to characterize the coating layers. These YSZ coated and uncoated samples were subjected to wear testing under different spindle speed, loading and working distance. Wear test results were compared with the kinetic friction coefficients and weight loss values. Wear marks on YSZ coated and uncoated samples were investigated by SEM analysis. By coating with plasma spray technique, the wear resistance of Al alloys was increased without changing the friction coefficient. It was found that spindle speed had significant effect over the wear properties than the load applied. By YSZ coating, wear properties were increased 10 times.
Go to article

Abstract

AISI 52100 bearing steels are commonly used in applications requiring high hardness and abrasion resistance. The bearing steels are working under dynamic loads in service conditions and their toughness properties become important. In order to provide the desired mechanical properties, various heat treatments (austenizing, quenching and tempering) are usually applied. In this study, AISI 52100 bearing steel samples were austenized at 900°C for ½ h and water quenched to room temperature. Then tempering was carried out at 795°C, 400°C and 200°C for ½ h. In order to investigate the effect of heat treatment conditions on wear behavior, dry friction tests were performed according to ASTM G99-05 Standard with a ‘ball-on-disk’ type tribometer. The samples were tested against steel and ceramic counterparts using the parameters of 100 m distance and 30 N load and 0.063 m/s rotational speed. After wear test, the surface characterization was carried out using microscopy. Wear loss values were calculated using a novel optical method on both flat and counterpart specimens.
Go to article

This page uses 'cookies'. Learn more