Abstrakt

The paper presents results of measuring heat diffusivity and thermal conductivity coefficients of used green foundry sand in temperature range ambient – 600 o C. During the experiments a technical purity Cu plate was cast into the green-sand moulds. Basing on measurements of the mould temperature field during the solidification of the casting, the temperature relationships of the measured properties were evaluated. It was confirmed that the obtained relationships are complex and that water vaporization strongly influences thermal conductivity of the moulding sand in the first period of the mould heating by the poured and solidified casting
Przejdź do artykułu

Abstrakt

The paper is devoted to grain-refinement of the medium-aluminium zinc based alloys (MAl-Zn). The system examined was sand cast Zn10 wt. %. Al binary alloy (Zn-10Al) doped with commercial Al-3 wt. % Ti – 0.15 wt. % C grain refiner (Al-3Ti-0.15C GR). Basing on the measured attenuation coefficient of ultrasonic wave it was stated that together with significantly increased structure fineness damping decreases only by about 10 – 20%. The following examinations should establish the influence of the mentioned grain-refinement on strength and ductility of MAl-Zn cast alloys.
Przejdź do artykułu

Abstrakt

The paper presents results of measuring attenuation coefficient of the Al-20 wt.% Zn alloy (AlZn20) inoculated with different grain refiners. During experiments the melted alloys were doped with Al-Ti3-C0.15 refining master alloy. Basing on measurements performed by Krautkramer USLT2000 device with 1MHz ultrasound wave frequency it was stated that grain refinement reduces the attenuation coefficient by about 20-25%. However, the examined alloys can be still classified as the high-damping ones of attenuation greater than 150 dB/m.
Przejdź do artykułu

Abstrakt

The paper presents results of measuring thermal conductivity and heat capacity of bentonite foundry sand in temperature range ambient – 900 OC. During the experiments a technical purity Cu plate was cast into the green-sand moulds. Basing on measurements of the mould temperature field during the solidification of the casting, the temperature relationships of the measured properties were evaluated. It was confirmed that water vaporization strongly influences thermal conductivity of the moulding sand in the first period of the mould heating by the poured casting.
Przejdź do artykułu