This article contains information concerning of the analysis the possibility of defining refinery qualities of the slag based thermophysical and thermodynamical data. The paper presents a model of slag refining processes and a method of determining the reduction capability of slag solutions. Slag was analysed with the use of the DTA methods for the brass melting conductions. The study of computer program including the satisfactory number of data there are used in to the design a modern device rotating head used for gas-slag refining. It was achieved that the refining gas and fluxes were distributed ever by the rotating head. High effectiveness of the gas-slag refining processes was proved for the brass.
The article describes the optimization of the melting brass. Brasses, as one of the most popular alloys of copper, deserve special attention in the context of the processes of melting, which in turn would provide not only products of better quality, but also reduce the cost of their production or refining. For this purpose, several studies carried out deriatographic (DTA) and thermogravimetric (TG) using derivatograph. The results were confronted with the program SLAG - PROP used to evaluate the physicochemical properties of the coatings extraction. Based on the survey and analysis of the program can identify the most favorable physico - chemical properties, which should be carried out treatments. This allows for slag mixtures referred configurations oxide matrix containing specific stimulators of the reaction. Conducted empirical studies indicate a convergence of the areas proposed by the application. It should also be noted that the program also indicates additional areas in which to carry out these processes would get even better, to optimize the melting process, the results.
The article presents an integrated analytical and measurement system for evaluation of the properties of cast metals and alloys. The presented platform is an extension of the SLAG - PROP application with new modules, which allow to use information on metallurgical processes in an even more effective way, as well as to evaluate the finished product. In addition, the construction of a measuring station for the analysis of thermal processes taking place in a metal bath allows for precise observation of phenomena together with their appropriate interpretation. The article presents not only the cooling curves of certain copper alloys. The analysis also covered mechanical properties related to hardness, finished products depending on the mold in which the products were cast. In the literature one can find information about the mechanical properties of products in the improved state, usually after plastic or thermal treatment, omitting their properties obtained as a result of a naturally made casting. The article also presents the method of placing information in the database using a convenient graphical tool.
Slag refining slag with west materials was analysed used the DTA methods. In the paper a method of determining the reduction capability, with the Carbo-N-Ox method, of slag solutions was used. Some relations between the stimulators in the environment - slag - metal system allow to initiate mass exchange reactions in the process of slag refining.The presented in work course of behaviour permits on choice of basic composition of slaglite, the of necessary components stimulating quantities, as well as on accomplishment of opinion of ability refinement. The worked out programme Slag-Prop, after introduction of data with experiment, it allows on next corrections in composition of proposed mixtures also, should be put on properly elaborated factors of multistage reaction with essential usage of suitable stimulators.
A special Slag-Prop Cu database has been developed to archive data from laboratory and industrial tests related to post-reduction slags. In order to enrich the data areas, it was decided to design a system for measuring the temperature of the liquid slag and its viscosity. Objectives of research work are to gather information on the properties of post-slags such as the temperature of liquid slag and its viscosity. The discussed issues are especially important in the foundry practice. Designed research stand and using of database applications can greatly facilitate the work of metallurgists, foundrymen, technologists and scientists. The viscosity measurement was developed and presented earlier. The author's analytical methodology was supplemented by a thyristor measuring system (described in the article). The system temperature measurement can be performed simultaneously in 3 ways to reduce the measurement error. Measurement of the voltage mV - using the Seebeck effect can be measured throughout the entire range of thermocouple resistance, up to 1300 °C. Direct temperature measurement ⁰C - measurement only below 1000 ⁰C. Additional measurement - the measurement can also be read from the pyrometer set above the bath. The temperature and the reading frequency depend on the device itself. The principle of measurement is that in a molten metal / slag crucible, we put a N-type thermocouple. The thermocouples are hung by means of a tripod above the crucible and placed in a crucible. The thermocouple is connected to a compensating line dedicated to this type of thermocouple. The cable is in turn connected to a special multimeter that has the ability to connect to a computer and upload results. Temperature measurement can be performed simultaneously in 3 ways to reduce the measurement error. The Sn-Pb alloy has been subjected to testing for proper operation of the device. In this foot should be observed the supercooling of the liquid, which initiates the crystallization process and in which latent heat begins to exude raising the temperature until the coagulation temperature is reached.
Discusses an attempt to optimize the operation of an electric furnace slag to be decopperisation suspension of the internal recycling process for the production of copper. The paper presents a new method to recover copper from metallurgical slags in arc-resistance electric furnace. It involves the use of alternating current for a first period reduction, constant or pulsed DC in the final stage of processing. Even distribution of the electric field density in the final phase of melting caused to achieve an extremely low content of metallic copper in the slag phase. They achieved by including the economic effects by reducing the time reduction.
Trial series of cast alloy MO59 obtained from qualified scrap was investigated. SEM and TEM of resulting precipitates were conducted. The SEM analysis demonstrated the dependence of silicon, phosphorus, iron, chromium and nickel in the composition of the so-called hard precipitates. TEM analysis showed the formation of phase AlFeSi and AlCr. Made studies have shown the important role of the composition of the batch melts brass CuZn39Pb2 type. The analysis of SEM and TEM resulting precipitates pointed to the formation of various forms of divisions, only one of which was described in the literature character of the so-called hard inclusions. The SEM studies demonstrated the dependence of the occurrence of inclusions rich in silicon, phosphorus, iron, chromium and nickel. In contrast, additional TEM analysis indicated the formation of AlFeSi phase type and AlCr. The results of the analyses referred to the structure of the batch. Due to the difficulty of obtaining recycled materials that do not contain these elements necessary to carry out further analyzes in the direction of defining the role of phosphorus in the formation of the so-called hard inclusions.
The scope of work included the launch of the process of refining slag suspension in a gas oven using a variety of technological additives. After the refining process (in the context of copper recovery), an assessment of the effect of selected reagents at the level of the slag refining suspension (in terms of copper recovery). Method sieve separated from the slag waste fraction of metallic, iron - silicate and powdery waste. Comparison of these photographs macroscopic allowed us to evaluate the most advantageous method of separating metallic fraction from the slag. After applying the sample A (with KF2 + NaCl) we note that in some parts of the slag are still large amounts of metallic fraction. The fraction of slag in a large majority of the elements has the same size of 1 mm, and a larger portion of the slag, the size of which is from 2 to 6 mm. Definitely the best way is to remove the copper by means of the component B (with NaCl ) and D (with KF2 ). However, as a result of removing the copper by means of component C (with CaO) were also obtained a relatively large number of tiny droplets of copper, which was problematic during segregation. In both cases we were able to separate the two fractions in a fast and simple manner.