Abstract

The paper presents the optimization of master alloy amount for the high nodular graphite yield (80-90%) in cast iron obtain in lost foam process. The influence of the gating system configuration and the shape of the reaction chamber, the degree of spheroidisation cast iron was examined. Research has shown that the, optimal of master alloy amount of 1.5% by mass on casting iron. The degree of spheroidisation is also influenced by the gating system configuration. The best spheroidisation effect was obtained for liquid cast iron was fed into the reaction chamber from the bottom and discharged from the top.
Go to article

Abstract

The work presents the analysis results of the structure of the coat obtained by dipping in silumin AlSi5 of two grades of alloy cast steel: GX6CrNiTi18-10 (LH18N9T) and GX39Cr13 (LH14). The temperature of the silumin bath was 750±5°C, and the hold-up time of the cast steel element τ = 180 s. The absolute thickness of the coat obtained in the given conditions was g = 104 μm on cast steel GX6CrNiTi18-10 and g = 132 μm on GX39Cr13. The obtained coat consisted of three layers of different phase structure. The first layer from the base “g1`” was constructed of the phase AlFe including Si and alloy additives of the tested cast steel grades: Cr and Ni (GX6CrNiTi18-10) and Cr (GX39Cr13). The second layer “g1``” of intermetallic phases AlFe which also contains Si and Cr crystallizes on it. The last, external layer “g2” of the coat consists of the silumin containing the intermetallic phases AlFeSi which additionally can contain alloy additives of the cast steel. It was shown that there were no carbides on the coat of the tested cast steels which are the component of their microstructure, as it took place in the case of the coat on the high speed steels.
Go to article

Abstract

The work presents the research results of the silumin coat structure applied on the carbidic alloy ductile iron with the metal matrix: pearlitic, bainitic and martensitic. The coats were made in the AlSi5 silumin bath at the temperature tk = 750±5°C. The holding time of cast iron element in the bath was τ = 180s. Irrespective of the kind of tested ductile iron the obtained coat consisted of three layers with a different phase composition. The first layer from the cast iron ground “g1`” is built from Fe4CSi carbide which contains selected alloy additives of the cast iron. On it the second layer “g1``” crystallizes. It consists of the AlFeSi inter-metallic phase which can appear in its pure form or contain a small quantity of the alloy additives of the cast iron. The last external part of the layer “g2” mainly consists of the hypo-eutectic phases of silumin. The AlFeSi inter-metallic phases in the form of free precipitations with a lamellar or faceted morphology can also appear there. These phases also can contain a small quantity of the alloy additives of the cast iron. More than that, in all the layers of the coat there are graphite precipitations. The phenomenon of graphite movement to the coat is caused by intensive dissolving of the cast iron element surface by the aluminum of the silumin bath.
Go to article

Abstract

In the paper presented are results of a research on influence of electrical and physico-chemical properties of materials being parts of multicomponent and multimaterial systems used in foundry practice on efficiency and effectiveness of microwave heating. Effectiveness of the process was evaluated on the grounds of analysis of interaction between selected parameters of permittivity and loss factor, as well as collective index of energy absorbed, reflected and transmitted by these materials. In the examinations used was a stand of waveguide resonance cavity for determining electrical properties and a stand of microwave slot line for determining balance of microwave power emitted into selected materials. The examinations have brought closer the possibility of forecasting the behaviour of multimaterial systems like e.g. model, moulding sand or moulding box in microwave field on the grounds of various electrical and physico-chemical properties. On the grounds of analysis of the results, possible was selecting a group of materials designed for building foundry instrumentation to be effectively used in electromagnetic field.
Go to article

Abstract

The article presents the results of the research on the influence of the shape of reaction chamber on spheroidisation of cast iron produced with use of the inmold method. The amounts of nodular graphite precipitates in castings produced with the use of different reaction chambers have been compared.
Go to article

Abstract

The study discusses the issues connected with the production of thin-walled ceramic slurry in the replicast cs technology. In the ceramic mould production process, a special role is played by the liquid ceramic slurry used to produce the first layer of the mould. The study examines selected technological properties of liquid ceramic slurries used to produce moulds in the replicas cs technology. The ceramic slurries for the tests were prepared based on the binders Ludox Px30 and Sizol 030, enriched with Refracourse flour. The wettability of the pattern's surface by the liquid ceramic slurry and the dependence of the apparent viscosity on the ceramic flour content in the mixture were determined. The wettability of the pattern surface by the liquid ceramic slurry was determined based on the measurement of the wetting angle. The angle was determined by means of an analysis of the computer image obtained with the use of a CDC camera.
Go to article

Abstract

The study presents the results of the investigations of the effect of Cu, Ni, Cr, V, Mo and W alloy additions on the microstructure and mechanical properties of the AlSi7Mg0.3 alloy. The examinations were performed within a project the aim of which is to elaborate an experimental and industrial technology of producing elements of machines and devices complex in their construction, made of aluminium alloys by the method of precision investment casting. It was demonstrated that a proper combination of alloy additions causes the crystallization of complex intermetallic phases in the silumin, shortens the SDAS and improves the strength properties: Rm, Rp0.2,HB hardness. Elevating these properties reduces At, which, in consequence, lowers the quality index Q of the alloy of the obtained casts. Experimental casts were made in ceramic moulds preliminarily heated to 160 °C, into which the AlSi7Mg0.3 alloy with the additions was cast, followed by its cooling at ambient temperature. With the purpose of increasing the value of the quality index Q, it is recommended that the process of alloy cooling in the ceramic mould be intensified and/or a thermal treatment of the casts be performed (ageing)(T6).
Go to article

Abstract

The paper presents the use of rapid prototyping technology of three dimensional printing (3DP) to make a prototype shell casting mold. In the first step, for identification purposes, a mold was prepared to enable different alloys to be cast. All molds being cast were designed in a universal CAD environment and printed with the zp151 composite material (Calcium sulfate hemihydrate) with a zb63 binder (2- pyrrolidone). It is designated to be used to prepare colourful models presenting prototypes or casting models and molds. The usefulness of 3DP technology for use with copper alloys, aluminum and zinc was analyzed. The strength of the mold during casting was assumed as a characteristic comparative feature in the material resistance to high temperature, the quality of the resulting casting and its surface roughness. Casting tests were carried out in vacuum – pressure casting. The casting programs applied, significantly increased the quality of castings and enabled precise mold submergence. Significant improvement was noted in the quality compared to the same castings obtained by gravity casting.
Go to article

Abstract

The work presents the test result of the influence of cooling rate on the microstructure of AZ91 alloy, Vickers micro-hardness and Brinell hardness. Studies cooling and crystallization of AZ91 alloy was cast into the ceramic shells pre-heated to 180 ° C and then air-cooled at ambient temperature or intensively super cooled in the liquid coolant. The TDA method was applied to record and characterize the thermal effect resulting from the phase transformations occurring during the crystallization of AZ91 alloy. The kinetics and dynamics of the thermal processes of crystallization of AZ91 alloy in the ceramic shells were determined. Metallographic tests were performed with the use of an optical microscope. A comparison of these test results with the thermal effect recorded by way of the TDA method was made. Influence of cooling rate of AZ91 on HV0, 01 micro-hardness and Brinell hardness alloy was examined.
Go to article

Abstract

The performed examinations concerning the process of filling the plaster ceramic moulds with aluminium alloys allowed to assess the influence of various methods of introducing the metal into the mould cavity on the macro- and microstructure of the obtained experimental castings. The comparison was performed for castings with graded wall thickness made either of EN AC-44000 alloy or of EN AC-46000 alloy, produced either by gravity casting, or by gravity casting with negative pressure generated around the mould (according to the Vacumetal technology), or by counter-gravity casting. It was found that the silicon crystals grow in size with an increase in wall thickness due to the slower cooling and solidification of castings.
Go to article

Abstract

The work deals with the influence of change in the filling conditions of the ceramic moulds with plaster binder on the presence of gaseous porosity and the microstructure of the achieved test castings with graded wall thickness. Castings made of EN AC-44000 alloy, produced either by gravity casting, or by gravity casting with negative pressure generated around the mould (according to the Vacumetal technology), or by counter-gravity casting were compared. The results of examinations concerning the density of the produced castings indicate that no significant change in porosity was found. The increased size of silicon crystals was found for the increased wall thicknesses due to the slower cooling and solidification of castings.
Go to article

Abstract

Homogeneity of die castings is influenced by wide range of technological parameters as piston velocity in filling chamber of die casting machine, filling time of mould cavity, temperature of cast alloy, temperature of the mould, temperature of filling chamber, surface pressure on alloy during mould filling, final pressure and others. Based on stated parameters it is clear, that main parameters of die casting are filling time of die mould cavity and velocity of the melt in the ingates. Filling time must ensure the complete filling of the mould cavity before solidification process can negatively influence it. Among technological parameters also belong the returning material, which ratio in charge must be constrained according to requirement on final homogeneity of die castings. With the ratio of returning material influenced are the mechanical properties of castings, inner homogeneity and chemical composition.
Go to article

Abstract

The essence of ablation casting technology consists in pouring castings in single-use moulds made from the mixture of sand and a watersoluble binder. After pouring the mould with liquid metal, while the casting is still solidifying, the mould destruction (washing out, erosion) takes place using a stream of cooling medium, which in this case is water. This paper focuses on the selection of moulding sands with hydrated sodium silicate for moulds used in the ablation casting. The research is based on the use of Cordis binder produced by the Hüttenes-Albertus Company. It is a new-generation inorganic binder based on hydrated sodium silicate. Its hardening takes place under the effect of high temperature. As part of the research, loose moulding mixtures based on the silica sand with different content of Cordis binder and special Anorgit additive were prepared. The reference material was sand mixture without the additive. The review of literature data and the results of own studies have shown that moulding sand with hydrated sodium silicate hardened by dehydration is characterized by sufficient strength properties to be used in the ablation casting process. Additionally, at the Foundry Research Institute in Krakow, preliminary semi-industrial tests were carried out on the use of Cordis sand technology in the manufacture of moulds for ablation casting. The possibility to use these sand mixtures has been confirmed in terms of both casting surface quality and sand reclamation.
Go to article

Abstract

The paper analyses specific defects of castings produced by semi-solid casting process, especially rheocasting method SEED, which uses mechanical swirling for reaching proper structure in semisolid state with high content of solid fraction. Heat treated alloy AlSi7Mg0.3 was applied for producing an Engine Bracket casting part. For observing structure, metallographic observation by light and SEM microscopy was used. To analyse the process, software ProCAST was used to simulate the movements in shot chamber and filling of the mold.
Go to article

Abstract

The new investigation method of a permeability of ceramic moulds applied in the investment casting technology, is presented in the paper. Some concepts of performing permeability measurements are shown. Investigations in which the influence of the solid phase fraction in the liquid ceramic moulding sand (LCMS) on a permeability of a multi-layer ceramic mould were performed and discussed. The permeability was estimated during two the most important stages of the technological process: in the first – after wax melting and in the second – after mould annealing. Also an influence of the matrix grain sizes (material for sprinkling) on a ceramic mould permeability was estimated.
Go to article

Abstract

The work is a continuation of research concerning the influence of intensive cooling of permanent mold in order to increase the casting efficiency of aluminium alloys using the multipoint water mist cooling system. The paper presents results of investigation of crystallization process and microstructure of multicomponent synthetic hypereutectic alloy AlSi20CuNiCoMg. The study was conducted for unmodified silumin on the research station allowing the cooling of the special permanent sampler using a program of computer control. Furthermore, the study used a thermal imaging camera to analyze the solidification process of multicomponent alloy. The study demonstrated that the use of mold cooled with water mist stream allows in wide range to form the microstructure of hypereutectic multicomponent silumin. It leads to higher homogeneity of microstructure and refinement of crystallizing phases of casting.
Go to article

Abstract

The work is a continuation of research on the use water mist cooling in order to increase efficiency of die-casting aluminum alloys. The paper presents results of research and analysis process, spraying water and generated a stream of water mist, the effect of the type of nozzle, the nozzle size and shape of the emitting of the water mist on the wall surface of casting die on the microstructure and geometry of water mist stream and cooling efficiency. Tests were used to perform high-speed camera to record video in the visible and infrared camera. Results were used to develop a computerized image analysis and statistical analysis. The study showed that there are statistical relationships between water and air flow and geometry of the nozzle and nozzle emitting a stream of microstructure parameters of water mist and heat the incoming stream. These relationships are described mathematical models that allow you to control the generating of adequate stream of water mist and a further consequence, the cooling efficiency of casting die.
Go to article

Abstract

In highly developed countries, a significant progress in the use of alternative and clean energy sources has recently been observed. The European Union has implemented a programme to build wind turbines. It is estimated that in the coming years, thanks to the support in tax and credit, the global energy will develop very intensively. Many components of the wind turbines are castings. The basic material used for these castings is ductile iron, which in this particular case must meet high requirements imposed by the operating conditions of wind turbines. Anticipating an increase in customer demand for this type of castings, Krakodlew SA has decided to modernize its foundry using the ability to obtain external financing. The ductile iron manufacturing technology is now being developed and adapted to the specific conditions of the foundry plant, including the melting process yielding cast material with the required chemical composition, the technology of moulding, and the conditions for possible secondary metallurgy, spheroidizing treatment and graphitizing inoculation. The fulfilment of the imposed conditions for the casting production demands the use of advanced casting technologies introduced to the manufacturing process. The development of technology to launch the production of ductile iron castings for the wind power industry was supported by The National Centre for Research and Development (NCBiR). This article presents part of research on the binding kinetics of furan resin sands and choice of their composition for moulds and cores to make heavy castings used as components of equipment for the wind power industry.
Go to article

Abstract

Paper presents the results of research on modified surface grain refinement method used in investment casting of hollow, thin-walled parts made of nickel based superalloys. In the current technology, the refining inoculant is applied to the surface of the wax pattern and then, it is transferred to the ceramic mould surface during dewaxing. Because of its chemical activity the inoculant may react with the liquid metal which can cause defects on the external surface of the cast part. The method proposed in the paper aims to reduce the risk of external surface defects by applying the grain refiner only to the ceramic core which shapes the internal surface of the hollow casting. In case of thin-walled parts the grain refinement effect is visible throughout the thickness of the walls. The method is meant to be used when internal surface finish is less important, like for example, aircraft engine turbine blades, where the hollowing of the cast is mainly used to lower the weight and aid in cooling during operation.
Go to article

Abstract

A special Slag-Prop Cu database has been developed to archive data from laboratory and industrial tests related to post-reduction slags. In order to enrich the data areas, it was decided to design a system for measuring the temperature of the liquid slag and its viscosity. Objectives of research work are to gather information on the properties of post-slags such as the temperature of liquid slag and its viscosity. The discussed issues are especially important in the foundry practice. Designed research stand and using of database applications can greatly facilitate the work of metallurgists, foundrymen, technologists and scientists. The viscosity measurement was developed and presented earlier. The author's analytical methodology was supplemented by a thyristor measuring system (described in the article). The system temperature measurement can be performed simultaneously in 3 ways to reduce the measurement error. Measurement of the voltage mV - using the Seebeck effect can be measured throughout the entire range of thermocouple resistance, up to 1300 °C. Direct temperature measurement ⁰C - measurement only below 1000 ⁰C. Additional measurement - the measurement can also be read from the pyrometer set above the bath. The temperature and the reading frequency depend on the device itself. The principle of measurement is that in a molten metal / slag crucible, we put a N-type thermocouple. The thermocouples are hung by means of a tripod above the crucible and placed in a crucible. The thermocouple is connected to a compensating line dedicated to this type of thermocouple. The cable is in turn connected to a special multimeter that has the ability to connect to a computer and upload results. Temperature measurement can be performed simultaneously in 3 ways to reduce the measurement error. The Sn-Pb alloy has been subjected to testing for proper operation of the device. In this foot should be observed the supercooling of the liquid, which initiates the crystallization process and in which latent heat begins to exude raising the temperature until the coagulation temperature is reached.
Go to article

Abstract

The work is a continuation of research on the use of water mist cooling in order to increase efficiency of die-casting aluminum alloys using multipoint water mist cooling system. The paper presents results of investigation on crystallization process and microstructure of synthetic hypereutectic AlSi20 alloy. Casts were made in permanent mold cooled a with water mist stream. The study was conducted for unmodified AlSi20 alloy and a modified one with phosphorus, titanium and boron on the research station allowing sequential multipoint cooling using a dedicated program of computer control. The study demonstrated that the use of mold cooled with water mist stream and solution heat treatment allows in wide range for the formation of the microstructure of hypereutectic silumins. It leads to the growth of microstructure refinement and spheroidizing of phases in the casting.
Go to article

Abstract

The aging granulate is to activate the blowing agent during the manufacturing process to granulate models can re-expand and shape the model of well-sintered granules, smooth surface and a suitable mechanical strength. The article presents the results of studies which aim was to determine the optimum time for aging pre-foamed granules for pre-selected raw materials. The testing samples were shaped in an autoclave, with constant parameters sintering time and temperature. Samples were made at 30 minute intervals. Models have been subjected to flexural strength and hardness.
Go to article

Abstract

Paper presents the results of ATD and DSC analysis of two superalloys used in casting of aircraft engine parts. The main aim of the research was to obtain the solidification parameters, especially Tsol and Tliq, knowledge of which is important for proper selection of casting and heat treatment parameters. Assessment of the metallurgical quality (presence of impurities) of the feed ingots is also a very important step in production of castings. It was found that some of the feed ingots delivered by the superalloy producers are contaminated by oxides located in shrinkage defects. The ATD analysis allows for quite precise interpretation of first stages of solidification at which solid phases with low values of latent heat of solidification are formed from the liquid. Using DSC analysis it is possible to measure precisely the heat values accompanying the phase changes during cooling and heating which, with knowledge of phase composition, permits to calculate the enthalpy of formation of specific phases like γ or γ′.
Go to article

Abstract

The work is a continuation of research concerning the influence of intensive cooling of permanent mold in order to increase the casting efficiency of aluminium alloys using the multipoint water mist cooling system. The paper presents results of investigation of crystallization process and microstructure of synthetic hypereutectic alloys: AlSi15 and AlSi19. Casts were made in permanent mold cooled with water mist stream. The study was conducted for unmodified silumins on the research station allowing the cooling of the special permanent probe using a program of computer control. Furthermore the study used a thermal imaging camera to analyze the solidification process of hypereutectic silumins. The study demonstrated that the use of mold cooled with water mist stream allows in wide range the formation of the microstructure of hypereutectic silumins. It leads to higher homogeneity of microstructure and refinement of crystallizing phases and also it increases subsequently the mechanical properties of casting.
Go to article

Abstract

This article presents the results of studies in the hypoeutectic silumin destined for pressure die casting with the simultaneous addition of chromium and tungsten. The study involved the derivative and thermal analysis of the crystallization process, metallographic analysis and mechanical properties testing. Silumin 226 grade was destined for studies. It is a typical silumin to pressure die casting. AlCr15 and AlW8 preliminary alloys were added to silumin. Its quantity allowed to obtain 0.1, 0.2, 0.3 and 0.4% of Cr and W in the tested alloy. Studies of the crystallization process as well as the microstructure of the silumin poured into DTA sampler allowed to state the presence of additional phase containing 0.2% or more Cr and W. It has not occurred in silumin without the addition of above mentioned elements. It is probably the intermetallic phase containing Cr and W. DTA studies have shown this phase crystallizes at a higher temperature range than α (Al) solid solution. In the microstructure of each pressure die casting containing Cr and W the new phases formed. Mechanical properties tests have shown Cr and W additives in silumin in an appropriate amount may increase its tensile strength Rm (about 11%), the yield strength Rp0.2 (about 21%) and to a small extent elongation A.
Go to article