Abstract

Solidification of AlSiFe alloys was studied using a directional solidification facility and the CALPHAD technique was applied to calculate phase diagrams and to predict occurring phases. The specimens solidified by electromagnetic stirring showed segregation across, and the measured chemical compositions were transferred into phase diagrams. The ternary phase diagrams presented different solidification paths caused by segregation in each selected specimen. The property diagrams showed modification in the sequence and precipitation temperature of the phases. It is proposed in the study to use thermodynamic calculations with Thermo-Calc which enables us to visualize the mushy zone in directional solidification. 2D maps based on property diagrams show a mushy zone with a liquid channel in the AlSi7Fe1.0 specimen center, where significant mass fraction (33%) of β-Al5FeSi phases may precipitate before α-Al dendrites form. Otherwise liquid channel occurred almost empty of β in AlSi7Fe0.5 specimen and completely without β in AlSi9Fe0.2. The property diagrams revealed also possible formation of α–Al8Fe2Si phases.
Go to article

Abstract

Iron is the most common and detrimental impurity in casting alloys and has been associated with many defects. The main consequence of the presence or adding of iron to AlSi alloys is the formation Fe-rich intermetallics with especially deleterious β-Al5FeSi. β-Al5FeSi phases are most often called needles on 2D micro sections, whilst platelets in 3D geometry. The x-ray tomography results have demonstrated Ferich phases with shapes different from simple forms such as needles or platelets and presented bent and branched phases. β grown as complicated structure of bent and branched intermetallics can decrease feeding ability, strengthen pores nucleation and eutectic colonies nucleation leading to lower permeability of mushy zone and porosity in the castings.
Go to article

Abstract

This work is dealing with the impact of molybdenum on the structure properties of commercial cast AlSi10Mg(Cu) alloy. The solidification path of AlSi10Mg(Cu) alloy with various content of molybdenum has been investigated using cooling curve techniques. The samples for testing have been poured into permanent steel mold. The content of molybdenum has been varied from 0 to 0.20 wt. %.The desired chemical composition was achieved by adding of master alloy AlMo10 into commercial AlSi10Mg(Cu) alloy. The micro hardness of as cast alloys with different content of molybdenum has been measured. The microstructure and EDX analysis from the casted samples has been carried out. The results show that molybdenum in commercial AlSi10Cu(Mg) alloy precipitate in the interdendritic region isolated in the form of Al(FeMnMoMg)Si rich intermetallic. The increased content of molybdenum increase slightly liquidus temperature, prolonging precipitation of the last eutectic and surprisingly decrease the micro hardness of commercial alloy for approximately 16 %.
Go to article