The results of mechanical reclamation of waste moulding sands with furfuryl resin and activators of new generation are presented. The aim of the research described in this study was to determine what effect the addition of reclaim obtained in the process of dry mechanical reclamation could have on the properties of furan sands. The sand supplied by one of the domestic foundries was after the initial reclamation subjected to a two-step proper reclamation process. The following tests were carried out on the obtained reclaim: pH, S and N content, loss on ignition and comprehensive sieve analysis. The obtained reclaim was next used as a component of moulding sands with furfuryl resin, wherein it formed 50% and 80% of the base moulding material, respectively. The strength properties of the ready sand mixtures (bending strength Rg u and tensile strength Rm u ) were determined after the hardening time of 0.5, 1, 2, 4 and 24 hours.
A technology of sands with water glass hardened by liquid esters is a cheap and ecologic method of producing moulding sands. Due to these advantages, this technology is still very important in several foundry plants for production of heavy iron and steel castings. Reclamation of the mixed moulding and core sands generates significant amounts of dusts, which require further treatments for their reuse. The results of investigations of a pressureless granulation of dusts generated in the dry mechanical reclamation process of the mixture consisting in app. 90 % of moulding sands from the Floster S technology and in 10 % of core sands with phenolic resin resol type, are presented in the hereby paper. Investigations were aimed at obtaining granulates of the determined dimensional and strength parameters. Granules were formed from the mixture of dusts consisting of 75 mass% of dusts after the reclamation of sands mixture and of 25 mass% of dusts from bentonite sands processing plant. Wetted dusts from bentonite sands were used as a binding agent allowing the granulation of after reclamation dusts originated from the mixed sands technology.
The presented in the paper investigations were aimed at the determination of the reclaimed material (obtained in the dry mechanical reclamation process) addition influence on properties of moulding sands with hydrated sodium silicate modified by colloidal suspension of zinc oxide nanoparticles in propanol. Nanoparticles originated from the thermal decomposition of alkaline zinc carbonate, were used. The results of the reclamation of the spent moulding sand with hydrated sodium silicate performed in the AT-2 testing reclaimer are presented in the paper. Both, spent sands from the Floster S technology and from the technology with the modified water-glass were subjected to the reclamation processes. The following determinations of the reclaimed material were performed: pH reaction, acid demand, ignition loss and Na2O content. The obtained reclaim was used as a matrix component of moulding sands with water-glass in the Floster S technology, in which it constituted 60% and 50% of the sand matrix. The strength properties of the prepared moulding sands were determined (bending strength Rg u , tensile strength Rm u ) after samples storing times: 1h, 2h, 4h and 24 hours.