The results of investigations of spent moulding sands taken from the mould in which the metal core cooling system - to increase the cooling rate of the ladle casting - was applied, are presented in the hereby paper. The changes of the spent moulding sand at the casting external side being the result of degradation and destruction processes of organic binder, were analysed in this publication. Since the reclaimed material, obtained as a result of the mechanical reclamation of spent sands of the same type, is used as a grain matrix of the moulding sand, the amount of a binder left from the previous technological cycle is essential for the sound castings production. On the bases of investigations of the thermal analysis, ignition losses, dusts contents and pH values of the samples taken from the spent sand the conditions under which the process of gases displacing in the casting mould was realised as well as factors limiting the efficient mould degassing - were considered in this study. The possible reason of a periodical occurrence of an increased number of casting defects due to changing gas volume emission, being the reason of the realised technological process, was indicated.
The results of investigations of spent moulding sands taken from the mould at various distances from the surface of the produced casting, are presented in the paper. The casting mould was made with an application of the cooling system of the metal core in order to increase the cooling rate of the ladle casting. As temperature measurements in the mould indicated the heat flow from the metal did not create conditions for the complete burning of a moulding sand. The analysis was performed to find out changes of spent moulding sands caused by degradation and destruction processes of organic binders. Conditions occurring in the casting mould were discussed on the bases of testing: ignition losses, dusts contents, pH reactions and the surface morphology of the moulding sand samples. Factors limiting the effective mould degassing were pointed out. Operations, possible for realization, which can limit the reasons of a periodical occurrence of increased amounts of casting defects due to changing gas evolution rates being the result of the technological process, were also indicated.
The results of investigations of thermal reclamation of spent moulding sands originating from an aluminum alloy foundry plant are presented in this paper. Spent sands were crushed by using two methods. Mechanical fragmentation of spent sand chunks was realized in the vibratory reclaimer REGMAS. The crushing process in the mechanical device was performed either with or without additional crushing-grinding elements. The reclaimed material obtained in this way was subjected to thermal reclamations at two different temperatures. It was found that a significant binder gathering on grain surfaces favors its spontaneous burning, even in the case when a temperature lower than required for the efficient thermal reclamation of furan binders is applied in the thermal reclaimer. The burning process, initiated by gas burners in the reclaimer chamber, generates favorable conditions for self-burning (at a determined amount of organic binders on grain surfaces). This process is spontaneously sustained and decreases the demand for gas. However, due to the significant amount of binder, this process is longer than in the case of reclaiming moulding sand prepared with fresh components.
The thermal reclamation process as a utilisation method of spent moulding and core sands is more costly than other reclamation methods, but in the majority of cases it simultaneously provides the best cleaning of mineral matrices from organic binders. Thus, the application of the thermal analysis methods (TG-DSC), by determining the temperature range within which a degradation followed by a destruction of bounded organic binders in moulding sands, can contribute to the optimisation of the thermal reclamation process and to the limiting its realisation costs. The thermal analysis results of furan resin, one of the most often applied binder in foundry practice, are presented in the hereby paper. The influence of the heating rate of the sample - placed in the thermal analyser - on its degradation and destruction process under oxygen-free (argon) and oxygen (air) conditions, were compared. The recorded TG and DSC curves were used for analysing these processes as the temperature as well as the time function. The obtained results were analysed with regard to determining the required temperature of the thermal reclamation of the investigated organic binder. The usefulness of the developed methodology was found out, however under conditions of meeting several essential requirements concerning the repeatability of performed analyses.
Today, about two thirds of iron alloys casting (especially for graphitizing alloys of iron) are produced into green sand systems with usually organically bonded cores. Separation of core sands from the green sand mixture is very difficult, after pouring. The core sand concentration increase due to circulation of green sand mixture in a closed circulation system. Furthermore in some foundries, core sands have been adding to green sand systems as a replacement for new sands. The goal of this contribution is: “How the green sand systems are influenced by core sands?” This effect is considered by determination of selected technological properties and degree of green sand system re-bonding. From the studies, which have been published yet, there is not consistent opinion on influence of core sand dilution on green sand system properties. In order to simulation of the effect of core sands on the technological properties of green sands, there were applied the most common used technologies of cores production, which are based on bonding with phenolic resin. Core sand concentration added to green sand system, was up to 50 %. Influence of core sand dilution on basic properties of green sand systems was determined by evaluation of basic industrial properties: moisture, green compression strength and splitting strength, wet tensile strength, mixture stability against staling and physical-chemistry properties (pH, conductivity, and loss of ignition). Ratio of active bentonite by Methylene blue test was also determined.