Abstract

The aim of this study was to assess sand accumulation in the gastrointestinal tract and fecal sand excretion in Silesian foals using three diagnostic methods and taking into account the sex and age of the animals. Another aim of the study was to compare the three diagnostic methods. The study was carried out on 21 clinically healthy Silesian foals (10 females and 11 males) from 9-28 weeks old grazed on permanent pasture. The sand intake was assessed using a sedimentation test, abdominal ultrasonography and a quantitative evaluation of sand per 100 g of stool. In the sedimentation test, the sand was palpable in the stool of 57.1% of the horses, and clearly visible in 42.9% of the animals. The ultrasound examination revealed the presence of sand in the gastrointestinal tract in 66.7% of the horses. It was limited to a single location in 60% of the horses, while it was present in several regions in 40% of the horses. The mean amount of sand was 0.14 ± 0.33 g per 100 g of stool. It did not exceed 0.1g in 71.4% foals, while it ranged from 0.1-0.5 g in 23.8% foals. In 4.8% of the animals, it amounted to 1.6 g per 100 g of stool. There was no correlation between age and gender and the results. There was a positive correlation between the ultrasound examination and the sedimentation test. Sand may be accumulated in the gastrointestinal tract of foals without any clinical signs. The amount of sand excreted in the stool is not an indicator of the amount of sand accumulated in the gastrointestinal tract. An abdominal ultrasound examination should be combined with a sedimentation test for more specific results.
Go to article

Abstract

The results of testing the strength properties of experimental ceramic materials containing spending moulding sand after initial mechanical reclamation as a material for subsequent layers of the stucco composition were presented. Tests were carried out on spent moulding sands from various foundry technologies, i.e. sand with furfuryl resin and sand with hydrated sodium silicate. The spent, agglomerated moulding sand has undergone a crushing process. Next, the required granular fractions used for individual layers of the stucco material were separated. Ceramic samples, in which the spent moulding sand was a substitute for fresh silica sand in successive layers of the stucco composition, were prepared. As a reference material, identical ceramic samples were used but with all layers made from the fresh silica sand. Samples prepared in this way were used to determine the bending strength of ceramic materials in the temperature range from 20 to 900ºC. The obtained values of the bending strength have demonstrated that spent moulding sand can be used in investment casting with no adverse effect on the strength of ceramic materials.
Go to article

Abstract

The drainage consolidation method has been efficiently used to deal with soft ground improvement. Nowadays, it has been suggested to use a new sand soil which is a composite of sand and recycled glass waste. The permeability performance of glass-sand soil was explored to judge the feasibility of glass-sand soil backfilled in the drainage consolidation of sand-drained ground. For comparison purposes, different mix proportions of recycled glass waste, fineness modulus, and glass particle size were analyzed to certify the impact on the permeability coefficient and the degree of consolidation. The numerical results show that adding a proper amount of recycled glass waste could promote the permeability performance of glass-sand soil, and the glasssand soil drain could be consolidated more quickly than a sand drain. Experiments showed that glass-sand soil with the a 20% mix of recycled glass waste reveals the optimum performance of permeability.
Go to article

Abstract

The aim of the hereby paper is to present the developed model of determining the volume and surface porosity based on the main fraction of polifractional materials, its experimental verification and utilisation for the interpretation of effects accompanying the formation of a moulding sand apparent density, porosity and permeability in the blowing processes of the core and moulds technology.
Go to article

Abstract

Using the available analytical methods, including the determination of chemical composition using wavelength-dispersive X-ray fluorescent spectroscopy technique and phase composition determined using X-ray diffraction, microstructural observations in a highresolution scanning microscope equipped with an X-ray microanalysis system as well as determination of characteristic softening and sintering temperatures using high-temperature microscope, the properties of particular chromite sands were defined. For the study has been typed reference sand with chemical properties, physical and thermal, treated as standard, and the sands of the regeneration process and the grinding process. Using these kinds of sand in foundries resulted in the occurrence of the phenomenon of the molding mass sintering. Impurities were identified and causes of sintering of a moulding sand based on chromite sand were characterized. Next, research methods enabling a quick evaluation of chromite sand suitability for use in the preparation of moulding sands were selected.
Go to article

Abstract

The article presents the directions of foundry waste management, mainly used for spent foundry sands (SFS) and dust after the reclamation of this waste. An important aspect of environmental protection in foundry production is the reduction of the amount of generated waste as a result of SFS regeneration. The advantage is the reuse of waste, which reduces the costs of raw materials purchase and environmental fees for landfilling. Non -recycled spent foundry sands can be used in other industries. SFS is most often used in road and construction industries as well as inert material in closed mines (Smoluchowska and Zgut 2005; Bany-Kowalska 2006). An interesting direction of using SFS is its application in gardening and agriculture. The article presents the advantages and disadvantages of such use. It was found that spent foundry sands can be useful for the production of soil mixtures for many agricultural and horticultural applications. Due to the possibility of environmental pollution with heavy metals and organic compounds, such an application is recommended for the so-called green sands, i.e. SFS with mineral binders. In addition, an innovative solution for the energy use of dusts after spent foundry sands reclamation with organic binders has been discussed and proposed by some researchers. It was shown that dust from reclaimed SFS with organic binders can be used as an alternative fuel and raw material in cement kilns, due to the high percentage of organic substances which determine their calorific value and silica.
Go to article

Abstract

This is a short report about the first Cenozoic shark fossil from Svalbard. The specimen derives from the late Paleocene greenish sandstone of the Grumantbyen Formation, which is exposed in Fossildalen on the western side of Colesbukta on Spitsbergen. The single tooth is assigned to the Paleogene sand tiger shark genus Striatolamia that also is known from other polar regions. The Fossildalen specimen represents the northernmost Paleogene shark record, and is the second reported body fossil of a vertebrate from the Cenozoic of Spitsbergen.
Go to article

Abstract

In this work, the influence of microwave drying parameters such as irradiation time and microwave power level on the properties of synthetic moulding sands is presented. Determination of compressive strength Rc s, shear strength Rt s and permeability Ps of synthetic moulding sands with the addition of two different bentonites, after drying process with variable microwave parameters were made. The research works were carried out using the microwave oven with regulated power range of the electromagnetic field. From the results obtained, the significant influence of both drying time and microwave power level on the selected properties of moulding sands was observed. In comparison to the conventional drying method, microwave drying allows to obtain higher compressive strength of the synthetic moulding sand. The influence of application microwave irradiation on permeability was not observed. Higher strength characteristics and shorter drying time are major advantages of application of the electromagnetic irradiation for drying of the synthetic moulding sand with regard to conventional drying method.
Go to article

Abstract

The paper focuses on investigation of properties of two most widely used self-set sand binder systems APNB and FNB across the Globe, for making molds and cores in foundries to produce castings of different sizes involving wide range of metals and alloys, ferrous and nonferrous. This includes study of compression strength values of samples made out of molding sand at different binder addition level using new, mechanically reclaimed (MR) and thermally reclaimed (TR) sand. Strength values studied include dry strength (at room temperature) at specified intervals simulating different stages of mold handling, namely stripping and pre heating, followed by degraded strength after application of thinner based zircon wash by brush, subsequent lighting of, then checking strength both in warm (degraded strength) & cold (recovered strength) conditions. Throughout the cycle of mold movement from stripping to knock out, strength requirements can be divided into two broad classifications, one from stripping to closing (dry strength) and another from pouring to knock out (hot & retained strength). Although the process for checking of dry strength are well documented, no method using simple equipments for checking hot & retained strength are documented in literature. Attempts have been made in this paper to use some simple methods to standardize process for checking high strength properties using ordinary laboratory equipments. Temperature of 450°C has been chosen by trial & error method to study high temperature properties to get consistent & amplified values. Volume of gases generated for both binders in laboratory at 850°C have also been measured. Nature of gases including harmful BTEX and PAH generated on pyrolysis of FNB and APNB bonded sands are already documented in a publication [1]. This exercise has once again been repeated in same laboratory, AGH University, Poland with latest binder formulations in use in two foundries in India.
Go to article

Abstract

The investigation results of the mechanical reclamation of spent moulding sands from the Cordis technology are presented in the paper. The quality assessment of the obtained reclaim and the influence of the reclaim fraction in a matrix on the core sand strength is given. The reclaim quality assessment was performed on the basis of the determination of losses on ignition, Na2O content on reclaim grains and pH values. The reclaim constituted 100%, 75% and 50% of the core sand matrix, for which the bending strength was determined. The matrix reclamation treatment was performed in the experimental rotor reclaimer RD-6. Spent sands were applied in as-delivered condition and after the heating to a temperature of 140 o C. Shaped samples for strength tests were made by shooting and hardening of sands in the warmbox technology.
Go to article

Abstract

This study summarises the research efforts undertaken in iron foundry plants in which the process are mostly automated and mechanised. The research program was limited in scope, focusing on causes of surface defects in castings products that are attributable to the bentonite-containing sand and the mould system. One of the potential roots of surface defects is heterogeneity of sand grains, containing lumped ball-shaped grains and irregular pellets with a layered-structure. The moisture contents of those lumped grains is different than the moisture level required in the process, besides these grains may contain various elements and metallic compounds which, when cast into moulds, may react with molten metals in an uncontrolled manner. As a result, surface defects are produced, such as surface blowholes, burst penetration, sand holes, slag inclusions, pinhole porosity. This study investigated the efficiency of key sand preparation and moulding machines and installations integrated into the casting process line. The efficiency of machines and installations is defined in terms of quality parameters of sand mix and moulds, which are associated with the emergence of surface defects on castings.
Go to article

Abstract

Until now, the mould sand in general use in the foundry industry are based on bentonite, which resulted from the fact that a good recognition properties and phenomena associated with this material. Come to know and normalized content of montmorillonite and carbonates and their important role in the construction of bentonite, and mass properties of the participation of compressive strength or scatter. Halloysite is widely used in industry and beyond them. However, little is known about its use in the foundry in Poland and abroad. This article presents preliminary research conducted at the Foundry Department of Silesian University of Technology on this material. Will raise the question of the representation of this two materials, which contains information connected with history and formation of materials, their structure and chemical composition. In the research, the results of compressive strength tests in wet masses of quartz matrix, where as a binder is used halloysite and bentonite in different proportions.
Go to article

Abstract

The study evaluated the curing properties of natural silica sand moulded with 1% by weight Furotec 132 resin binder catalysed by Furocure CH Fast acid and Furocure CH Slow acid. Physical properties of this sand included an AFS number of 47.35, 4.40 % clay, 0 % magnetic components, 0.13 % moisture, and 64.5 % of the size distribution spread over three consecutive sieves (150 – 600 μm). The sand was washed repeatedly to remove all the clay and oven dried. 2 kg washed sand samples were mulled with pre-determined weights of either catalyst to give 30 %, 50 % and 70 % by weight of 20 g Furotec 132 resin which was added last. Furotec 132 resin + Furocure CH Slow acid catalyst system gives longer bench lives and strip times but the maximum compressive strength in excess of 5000 N/cm2 is attained after more than 8.5 hours curing time irrespective of the weight % of catalyst added relative to the resin. On that basis, exceeding 30 weight % Furocure CH Slow acid catalyst when sand moulding with Furotec 132 resin has neither technical nor economic justification. In comparison, the Furotec 132 resin + Furocure CH Fast acid catalyst system was only capable of producing mould specimens with maximum compressive strength above 5000 N/cm2 at 30 weight % catalyst addition rate. At 50 and 70 weight % catalyst addition rates, the mulled sand rapidly turned dark green then bluish with a significant spike in temperature to about 40 oC, far exceeding the optimum curing temperature of Furotec 132. This high temperature accelerates the curing rate but with a very low degree of resin curing which explains the low compressive strength. In fact the sand grains fail to bond and have a dry, crumbly texture implying dehydration. Thus, not more than 30 weight % Furocure CH Fast acid catalyst should be used in sand moulding.
Go to article

Abstract

Ablation casting is a technological process in which the increased cooling rate causes microstructure refinement, resulting in improved mechanical properties of the final product. This technology is particularly suitable for the manufacture of castings with intricate shapes and thin walls. Currently, the ablation casting process is not used in the Polish industry. This article presents the results of strength tests carried out on moulding sands based on hydrated sodium silicate hardened in the Floster S technology, intended for ablation casting of the AlSi7Mg (AK7) aluminium alloy. When testing the bending and tensile strengths of sands, parameters such as binder and hardener content were taken into account. The sand mixtures were tested after 24h hardening at room temperature. The next stage of the study describes the course of the ablation casting process, starting with the manufacture of foundry mould from the selected moulding mixture and ending in tests carried out on the ready casting to check the surface quality, structure and mechanical properties. The results were compared with the parallel results obtained on a casting gravity poured into the sand mould and solidifying in a traditional way at ambient temperature.
Go to article

Abstract

The results of investigations of the influence of the matrix grain sizes on properties of cores made by the blowing method are presented in the hereby paper. Five kinds of matrices, differing in grain size compositions, determined by the laser diffraction method in the Analysette 22NanoTec device, were applied in investigations. Individual kinds of matrices were used for making core sands in the Cordis technology. From these sands the shaped elements, for determining the apparent density of compacted sands and their bending strength, were made by the blowing method. The shaped elements (cores) were made at shooting pressures being 3, 4 and 5 atn. The bending strength of samples were determined directly after their preparation and after the storing time of 1 hour.
Go to article

Abstract

The paper presents the idea of the integrated recycling system of used moulding sands with organic resins. A combination of the method of forecasting averaged ignition loss values of moulding sands after casting and defining the range of necessary matrix reclamation treatments in order to obtain its full recycling constitutes the basics of this process. The results of own investigations, allowing to combine ignition loss values of spent moulding sands after casting knocking out with amounts of dusts generated during the mechanical reclamation treatment of such sands, were utilized in the system.
Go to article

Abstract

Core sands for blowing processes, belong to these sands in which small amount of the applied binding material has the ability of covering the sand matrix surface in a way which - at relatively small coating thickness - allows to achieve the high strength. Although the deciding factor constitute, in this aspect, strength properties of a binder, its viscosity and ability to moisten the matrix surface, the essential meaning for the strength properties of the prepared moulding sand and the mould has the packing method of differing in sizes sand grains with the coating of the binding material deposited on their surfaces. The knowledge of the influence of the compaction degree of grains forming the core on the total contact surface area can be the essential information concerning the core strength. Forecasting the strength properties of core sands, at known properties of the applied chemically hardened binder and the quartz matrix, requires certain modifications of the existing theoretical models. They should be made more realistic with regard to assumptions concerning grain sizes composition of quartz sands and the packing structure deciding on the active surface area of the contacts between grains of various sizes and - in consequence - on the final strength of cores.
Go to article

Abstract

The aim of the study was to determine the applicability of a new product added to water glass-containing foundry sands hardened with ethylene glycol diacetate. The new additive designated by the symbol "B" is a composition of aqueous solutions of modified polyalcohols, improving the sand knocking out properties. The scope of studies included testing various mechanical and technological properties of foundry sand mixtures, such as permeability, friability, life cycle of cores and knocking out properties. In the technological studies, two types of water glass with different values of the silica modulus and density, designated as R145 and R150, were used. Moulding sands were prepared with the additive "B". For comparison, reference sands with water glass but without the additive "B" were also made. In Part I of the article, the results of studies of the effect of additive "B" on the properties of foundry sands with water glass hardened by CO2 blowing were discussed.
Go to article

Abstract

In the paper, a research on effects of baking temperature on chromite sand base of moulding sands bonded with sodium silicate is presented. Pure chromite sand and its chromite-based moulding sand prepared with use of sodium silicate were subjected to heating within 100 to 1200 °C. After cooling-down, changes of base grains under thermal action were determined. Chromite moulding sand was prepared with use of 0.5 wt% of domestic made, unmodified sodium silicate (water-glass) grade 145. After baking at elevated temperatures, creation of rough layer was observed on grain surfaces, of both pure chromite sand and that used as base of a moulding sand. Changes of sand grains were evaluated by scanning microscopy and EDS analyses. It was found that changes on grain surfaces are of laminar nature. The observed layer is composed of iron oxide (II) that is one of main structural components of chromite sand. In order to identify changes in internal structure of chromite sand grains, polished sections were prepared of moulding sand hardened with microwaves and baked at elevated temperatures. Microscopic observations revealed changes in grains structure in form of characteristically crystallised acicular particles with limited magnesium content, intersecting at various angles. EDS analysis showed that these particles are composed mostly of chromium oxide (III) and iron oxide (II). The temperature above that the a.m. changes are observed in both chromite-based moulding sand and in pure chromite sand. The observed phenomena were linked with hardness values and mass of this sand.
Go to article

Abstract

Modern investigation methods and equipment for the quality estimation of the moulding sands matrices with organic binders, in their circulation process, are presented in the paper. These methods, utilising the special equipment combined with the authors investigation methods developed in the Faculty of Foundry Engineering, AGH the University of Science and Technology, allow for the better estimation of the matrix quality. Moulding sands systems with organic binders require an in-depth approach to factors deciding on the matrix technological suitability as well as on their environmental impact. Into modern methods allowing for the better assessment of the matrix quality belongs the grain size analysis of the reclaimed material performed by means of the laser diffraction and also the estimation of the moulding sand gas evolution rate and identification of the emitted gases and their BTEX group gases content, since they are specially hazardous from the point of view of the Occupational Safety and Health.
Go to article

Abstract

In the paper, a research on effects of baking temperature on chromite sand base of moulding sands bonded with sodium silicate is presented. Pure chromite sand and its chromite-based moulding sand prepared with use of sodium silicate were subjected to heating within 100 to 1200 °C. After cooling-down, changes of base grains under thermal action were determined. Chromite moulding sand was prepared with use of 0.5 wt% of domestic made, unmodified sodium silicate (water-glass) grade 145. After baking at elevated temperatures, creation of rough layer was observed on grain surfaces, of both pure chromite sand and that used as base of a moulding sand. Changes of sand grains were evaluated by scanning microscopy and EDS analyses. It was found that changes on grain surfaces are of laminar nature. The observed layer is composed of iron oxide (II) that is one of main structural components of chromite sand. In order to identify changes in internal structure of chromite sand grains, polished sections were prepared of moulding sand hardened with microwaves and baked at elevated temperatures. Microscopic observations revealed changes in grains structure in form of characteristically crystallised acicular particles with limited magnesium content, intersecting at various angles. EDS analysis showed that these particles are composed mostly of chromium oxide (III) and iron oxide (II). The temperature above that the a.m. changes are observed in both chromite-based moulding sand and in pure chromite sand. The observed phenomena were linked with hardness values and mass of this sand.
Go to article

Abstract

The cumulative results of investigations of the possibility of using the reclaimed materials after the mechanical, thermal or mechanical-thermal reclamation for making cores by means of the blowing method in the alkaline CO2 technology, are presented in the paper. Three kinds of spent sands: with furfuryl resin, bentonite and alkaline phenolic resin, obtained from the foundry, were subjected to three kinds of reclamation: mechanical, thermal and combined mechanical-thermal, applying for this aim adequate experimental devices. The obtained reclaims were assessed with regard to the degree of the matrix liberation from the determined binding material. Reclaims of moulding sands with binders of the form of resin were assessed with regard to ignition loss values and pH reaction, while reclaims of moulding sands with bentonite with regard to the residual clay content and pH value. In all cases the results of the performed sieve analyses were estimated and the average characteristic diameter dl was determined. The reclaimed matrix was applied as a full substitute of the fresh high-silica sand in typical procedures of preparing core sands used for making shaped samples for bending strength investigations, Rg u .
Go to article

Abstract

Recently, some major changes have occurred in the structure of the European foundry industry, such as a rapid development in the production of castings from compacted graphite iron and light alloys at the expense of limiting the production of steel castings. This created a significant gap in the production of heavy steel castings (exceeding the weight of 30 Mg) for the metallurgical, cement and energy industries. The problem is proper moulding technology for such heavy castings, whose solidification and cooling time may take even several days, exposing the moulding material to a long-term thermal and mechanical load. Owing to their technological properties, sands with organic binders (synthetic resins) are the compositions used most often in industrial practice. Their main advantages include high strength, good collapsibility and knocking out properties, as well as easy mechanical reclamation. The main disadvantage of these sands is their harmful effect on the environment, manifesting itself at various stages of the casting process, especially during mould pouring. This is why new solutions are sought for sands based on organic binders to ensure their high technological properties but at the same time less harmfulness for the environment. This paper discusses the possibility of reducing the harmful effect of sands with furfuryl binders owing to the use of resins with reduced content of free furfuryl alcohol and hardeners with reduced sulphur content. The use of alkyd binder as an alternative to furfuryl binder has also been proposed and possible application of phenol-formaldehyde resins was considered.
Go to article

Abstract

The paper presents the results of laboratory tests into the effects of moisture and the content of two types of bentonite on dielectric properties of moulding sand. The use of electromagnetic waves in foundry industry is becoming more and more popular, which provides to some extent alternatives to conventional drying methods. Experimental studies published so far have shown the validity of using microwaves for drying classic moulding sands with bentonite. However, these studies lack data on the effect of moisture or bentonite content in moulding sand on the real component ε' or imaginary component ε'' of the relative complex electrical permittivity. The presented results may become in the future the basis for the evaluation of the composition of moulding sands, taking into account the phenomena occurring under the influence of electromagnetic field, which directly translates into the quality of the castings made and may constitute an attempt to develop a mathematical model of electric properties of moulding sands.
Go to article

Abstract

It was found that the addition of carbon fibers (CFs) does not affect the crosslinking process in the microwave radiation (800 W, 2.45 GHz) of the BioCo2 binder, which is a water solution of poly(acrylic acid) and dextrin (PAA/D). It has influence on BioCo2 thermal properties. The CFs addition improves the thermostability of a binder and leads to the reduction of gas products quantity generated in the temperature range of 300-1100°C (TG-DTG, Py-GC/MS). Moreover, it causes the emission of harmful decomposition products such as benzene, toluene, xylene and styrene to be registered in a higher temperatures (above 700°C). BioCo2 binder without CFs addition is characterized by the emission of these substances in the lower temperature range. This indicates the positive effect of carbon fibers presence on the amount of released harmful products. The selected technological tests (permeability, friability, bending strength, tensile strength) have shown that the moulding sand with the 0.3 parts by weight carbon fibers addition displays the worst properties. The addition of 0.1 parts by weight of CFs is sufficient to obtain a beneficial effect on the analyzed moulding sands properties. The reduction of harmful substances at the higher temperatures can also be observed.
Go to article