During the machining processes, heat gets generated as a result of plastic deformation of metal and friction along the tool–chip and tool–work piece interface. In materials having high thermal conductivity, like aluminium alloys, large amount of this heat is absorbed by the work piece. This results in the rise in the temperature of the work piece, which may lead to dimensional inaccuracies, surface damage and deformation. So, it is needed to control rise in the temperature of the work piece. This paper focuses on the measurement, analysis and prediction of work piece temperature rise during the dry end milling operation of Al 6063. The control factors used for experimentation were number of flutes, spindle speed, depth of cut and feed rate. The Taguchi method was employed for the planning of experimentation and L18 orthogonal array was selected. The temperature rise of the work piece was measured with the help of K-type thermocouple embedded in the work piece. Signal to noise (S/N) ratio analysis was carried out using the lower-the-better quality characteristics. Depth of cut was identified as the most significant factor affecting the work piece temperature rise, followed by spindle speed. Analysis of variance (ANOVA) was employed to find out the significant parameters affecting the work piece temperature rise. ANOVA results were found to be in line with the S/N ratio analysis. Regression analysis was used for developing empirical equation of temperature rise. The temperature rise of the work piece was calculated using the regression equation and was found to be in good agreement with the measured values. Finally, confirmation tests were carried out to verify the results obtained. From the confirmation test it was found that the Taguchi method is an effective method to determine optimised parameters for minimization of work piece temperature.
In this study, Taguchi method is used to find out the effect of micro alloying elements like vanadium, niobium and titanium on the hardness and tensile strength of the normalized cast steel. Based on this method, plan of experiments were made by using orthogonal arrays to acquire the data on hardness and tensile strength. The signal to noise ratio and analysis of variance (ANOVA) are used to investigate the effect of these micro alloying elements on these two mechanical properties of the micro alloyed normalized cast steel. The results indicated that in the micro alloyed normalized cast steel both these properties increases when compared to non-micro-alloyed normalized cast steel. The effect of niobium addition was found to be significantly higher to obtain higher hardness and tensile strength when compared to other micro alloying elements. The maximum hardness of 200HV and the maximum tensile strength of 780 N/mm2 were obtained in 0.05%Nb addition micro alloyed normalized cast steel. Micro-alloyed with niobium normalized cast steel have the finest and uniform microstructure and fine pearlite colonies distributed uniformly in the ferrite. The optimum condition to obtain higher hardness and tensile strength were determined. The results were verified with experiments.
The dry sliding wear behavior of heat-treated super duplex stainless steel AISI 2507 was examined by taking pin-on-disc type of wear-test rig. Independent parameters, namely applied load, sliding distance, and sliding speed, influence mainly the wear rate of super duplex stainless steel. The said material was heat treated to a temperature of 850°C for 1 hour followed by water quenching. The heat treatment was carried out to precipitate the secondary sigma phase formation. Experiments were conducted to study the influence of independent parameters set at three factor levels using the L27 orthogonal array of the Taguchi experimental design on the wear rate. Statistical significance of both individual and combined factor effects was determined for specific wear rate. Surface plots were drawn to explain the behavior of independent variables on the measured wear rate. Statistically, the models were validated using the analysis of variance test. Multiple non-linear regression equations were derived for wear rate expressed as non-linear functions of independent variables. Further, the prediction accuracy of the developed regression equation was tested with the actual experiments. The independent parameters responsible for the desired minimum wear rate were determined by using the desirability function approach. The worn-out surface characteristics obtained for the minimum wear rate was examined using the scanning electron microscope. The desired smooth surface was obtained for the determined optimal condition by desirability function approach.
Variation in final casting dimensions is a major challenge in the investment casting industry. Additional correction operations such as die tool reworking as well as coining operations affect foundry productivity significantly. In this paper influence of basic parameters such as wax material, mould material, number of ceramic coats and feed location on the dimensional accuracy of stainless-steel casting has been investigated. Two levels of each factor were chosen for experimental study. Taguchi approach has been used to design the experiment and to identify the optimal condition of each parameter for reduced dimensional deviation. Analysis of variance has been carried out to determine the contribution of each process parameter. The result reports that selected parameters have significant effect on the dimensional variability of investment casting. Mould material is the dominant parameter with the largest contribution followed by number of ceramic coats and wax material whereas feed location is having negligible contribution.