The FMEA (Failure Mode and Effects Analysis) method consists in analysis of failure modes and evaluation of their effects based on determination of cause-effect relationships for formation of possible product or process defects. Identified irregularities which occur during the production process of piston castings for internal combustion engines were ordered according to their failure rates, and using Pareto-Lorenz analysis, their per cent and cumulated shares were determined. The assessments of risk of defects occurrence and their causes were carried out in ten-point scale of integers, while taking three following criteria into account: significance of effects of the defect occurrence (LPZ), defect occurrence probability (LPW) and detectability of the defect found (LPO). A product of these quantities constituted the risk score index connected with a failure occurrence (a so-called “priority number,” LPR). Based on the observations of the piston casting process and on the knowledge of production supervisors, a set of corrective actions was developed and the FMEA was carried out again. It was shown that the proposed improvements reduce the risk of occurrence of process failures significantly, translating into a decrease in defects and irregularities during the production of piston castings for internal combustion engines.
The chosen, typical causes of quality defects of cast-iron „alphin” rings embedded in aluminum cast are being presented in this paper. Diffusive joint of those inserts with the pistons casts is being used, due to extreme work conditions of destructive influence of the fuel mix and variable thermo-mechanical loads, which reign in the combustion motor working chamber.
In the dissertation it has been shown, that so called “time-thermal treatment” (TTT) of the alloy in liquid state as overheating the metal with around 250o C above Tliq. and detailing it in temperature for 30 to 40 minutes has the influence on changing the crystallization parameters (Tliq., TEmin. , TEmax., TE(Me), TSol.). It was ascertained, that overheating the AlSi17Cu5Mg alloy substantially above Tliq. results with microcrystalline structure. Evenly distributed in the eutectic warp primeval silicon crystals and supersaturated with alloying additives of base content (Cu, Mg, Fe) of α(Al) solution, ensures not only increase durability in ambient temperature, but also at elevated temperature (250o C), what due to it’s use in car industry is an advantage.
In the dissertation it has been shown, that so called „time-thermal treatment” (TTT) of the alloy in liquid state, as overheating the metal with around 250o C above the Tliq. and detaining it in this temperature for around 30 minutes, improves the mechanical properties (HB, Rm, R0,2). It was ascertained, that overheating the AlSi17Cu5Mg alloy aids the modification, resulting with microcrystalline structure. Uniform arrangement of the Si primeval crystals in the warp, and α(Al) solution type, supersaturated with alloying elements present in the base content (Cu, Mg) assures not only increased durability in the ambient temperature, but also at elevated temperature (250o C), what is an advantage, especially due to the use in car industry.
Conceptions of analogue electronics circuit based on a multiple-input ﬂoating gate ﬁeld-eﬀect transistor MOS (MIFGMOS) have been presented. The simple add and diﬀerential voltage ampliﬁers with one and two MIFGMOS transistors and multiple-input operational ampliﬁers with their application have been proposed. One of them was used for the realisation of a controlled ﬂoating resistor. Results of circuit simulations in SPICE programme using the simple substitute macromodel of MIFGMOS transistor have been shown.