The aim of presented studies was to develop a new geometry of the overflow part of standard ATD–C tester for derivative thermal analysis in a way that it would allow to obtain samples for abrasion and mechanical properties tests in the same mould without the need of cutting them from a block of material. The pattern of new ATD–P tester has parts reflecting implemented samples. Computer simulations regarding initial verification of new tester were performed in NovaFlow software. Chromium cast iron melts were made for testing the sampler in real conditions and TDA analysis for casting material were conducted. The sandmix was prepared on silica sand matrix per the ALPHASET technology. This new solution greatly simplifies the preparations of materials difficult to machine.
Professor Piotr Pierański, an outstanding Polish physicists, excellent researcher and brilliant lecturer, passed away on the 23rd February 2018. The article quotes some recollections of his numerous friends and coworkers wordwide.
The paper presents the results of studies of the effect of chromium concentration on the solidification process, microstructure and selected properties of cast iron with vermicular graphite. The vermicular graphite cast iron was obtained by an Inmold process. Studies covered the cast iron containing chromium in a concentration at which graphite is still able to preserve its vermicular form. The effect of chromium on the temperature of eutectic crystallization and on the temperature of the start and end of austenite transformation was discussed. The conditions under which, at a predetermined chromium concentration, the vermicular graphite cast iron of a pearlitic matrix is obtained were presented, and the limit concentration of chromium was calculated starting from which partial solidification of the cast iron in a metastable system takes place. The effect of chromium on the hardness of cast iron, microhardness of individual phases and surface fraction of carbides was disclosed.
The main purpose of the paper is to present a method which allows taking into account the anisotropic properties of dynamo steel sheets. An additional aim is to briefly present anisotropic properties of these sheets which are caused by occurrences of some textures. In order to take into account textures occurring in dynamo sheets, a certain sheet sample is divided into elementary segments. Two matrix equations, describing changes of the magnetic field, are transformed to one non-linear algebraic equation in which the field strength components are unknown. In this transformation the flux densities assigned to individual elementary segments are replaced by functions of flux densities of easy magnetization axes of all textures occurring in the given dynamo sheet. The procedure presented in the paper allows determining one non-linear matrix equation of the magnetic field distribution; in this equation all textures occurring in a dynamo sheet are included. Information about textures occurring in typical dynamo sheets may be used in various approaches regarding the inclusion of anisotropic properties of these sheets, but above all, the presented method can be helpful in calculations of the magnetic field distribution in anisotropic dynamo sheets.
The paper concerns the processes connected with the formation of chromium white cast iron microstructure. The influence of titanium and strontium on the alloy crystallization has been described using TDA method and EDS analysis. Conducted experiments allowed the determination of the selected additions influence on the microstructure of examined alloys. TDA analysis enabled indication of the characteristic temperatures of thermal effects for samples with strontium and titanium and the comparison of results for the reference sample without additions. The results of TDA test also included the analysis of the temperature first derivative values, which presented interesting differences as well. The scanning microscopy observation clearly indicated the difference between the effect of strontium and titanium on the alloy microstructure. The EDS analysis helped to identify the chemical composition of the evolving phases and confirmed the strontium presence in the eutectic. Experimental results allowed to draw reliable conclusions about the effect of applied additions on the crystallization and microstructure of chromium cast iron.
Mechanical properties of aluminum-silicon alloys are defined by condition of alloying components in the structure, i.e. plastic metallic matrix created from solid solution on the basis of Al, as well as hard and brittle precipitations of silicon. Size and distribution of silicon crystals are the main factors having effect on field of practical applications of such alloys. Registration of crystallization processes of the alloys on stage of their preparation is directly connected with practical implementation of crystallization theory to controlling technological processes, enabling obtainment of suitable structure of the material and determining its usage for specific requirements. An attempt to evaluate correlation between values of characteristic points laying on crystallization curves and recorded with use of developed by the author TVDA method (commonly denominated as ATND method) is presented in the paper together with assessment of hardness of tested alloy. Basing on characteristic points from the TVDA method, hardness of EN AC-AlSi9Mg alloy modified with strontium has been described in the paper in a significant way by the first order polynomial.
The article presents crystallization process of silicon molybdenum ductile cast iron (SiMo). The alloy with 5% silicon content and with variable amounts of Mo in a range of 0-1% was chosen for the research. The carbon content in the analysed alloys did not exceed 3,1%. The studies of crystallization process were based on thermal – derivative analysis (TDA). Chemical composition of all examined samples was analysed with the use of LECO spectrometer. Additionally, the carbon and the sulphur content was determined basing on carbon and sulphur LECO analyser. For metallographic examination, the scanning electron microscopy (SEM) with EDS analyser was used. Disclosed phases have been also tested with the use of X-ray diffraction. The results allowed the description of crystallization processes of silicon molybdenum ductile cast iron using thermal – derivative analysis (TDA). Conducted studies did not allow for the clear identification of all complex phases containing molybdenum, occurring at the grain boundaries. Therefore, the further stages of the research could include the use of a transmission electron microscope to specify the description of complex compounds present in the alloy.
Among the family of stainless steels, cast austenitic stainless steels (CASSs) are preferably used due to their high mechanical properties and corrosion resistance. These steels owe their properties to their microstructural features consisting of an austenitic matrix and skeletal or lathy type δ-ferrite depending on the cooling rate. In this study, the solidification behavior of CASSs (304L and 316L grades) was studied using ThermoCalc software in order to determine the solidification sequence and final microstructure during cooling. Theoretical findings were supported by the microstructural examinations. For the mechanical characterization, not only hardness measurements but also tribological studies were carried out under dry sliding conditions and worn surfaces were examined by microscopy and 3D profilometric analysis. Results were discussed according to the type and amount of microstructural features.
To the main advantages of magnesium alloys belongs their low density, and just because of such property the alloys are used in aviation and rocket structures, and in all other applications, where mass of products have significant importance for conditions of their operation. To additional advantages of the magnesium alloys belongs good corrosion resistance, par with or even surpassing aluminum alloys. Magnesium is the lightest of all the engineering metals, having a density of 1.74 g/cm3 . It is 35% lighter than aluminum (2.7 g/cm3 ) and over four times lighter than steel (7.86 g/cm3 ). The Mg-Li alloys belong to a light-weight metallic structural materials having mass density of 1.35-1.65 g/cm3 , what means they are two times lighter than aluminum alloys. Such value of mass density means that density of these alloys is comparable with density of plastics used as structural materials, and therefore Mg–Li alloys belong to the lightest of all metal alloys. In the present paper are discussed melting and crystallization processes of ultra-light weight MgLi12,5 alloys recorded with use of ATND methods. Investigated magnesium alloy was produced in Krakow Foundry Research Institute on experimental stand to melting and casting of ultra-light weight alloys. Obtained test results in form of recorded curves from ATND methods have enabled determination of characteristic temperatures of phase transitions of the investigated alloy.
In the dissertation it has been shown, that so called “time-thermal treatment” (TTT) of the alloy in liquid state as overheating the metal with around 250o C above Tliq. and detailing it in temperature for 30 to 40 minutes has the influence on changing the crystallization parameters (Tliq., TEmin. , TEmax., TE(Me), TSol.). It was ascertained, that overheating the AlSi17Cu5Mg alloy substantially above Tliq. results with microcrystalline structure. Evenly distributed in the eutectic warp primeval silicon crystals and supersaturated with alloying additives of base content (Cu, Mg, Fe) of α(Al) solution, ensures not only increase durability in ambient temperature, but also at elevated temperature (250o C), what due to it’s use in car industry is an advantage.
Today’s industry aims at such situation, where number of defective products, so called defects shall approach to zero. Therefore, one introduces a various changes in technology of production, introduces improvements which would help in accomplishment of this objective. Another important factor is introduction of different type of testing, which shall help in assessment which factor has significant effect on quantity of rejects, and which one could be neglected. Existence of casting rejects is unavoidable; therefore a new ideas, technologies and innovations are necessary in the entire widely understood foundry branch, in order to minimize such adverse effect. Performance of tests aimed at unequivocal determination of an effect of vibrations during crystallization on mechanical properties and porosity of the EN ACAlSi17 alloy was the objective of the present work. To do this, there were produced 36 castings from EN AC-AlSi17 alloy. All the castings underwent machining operations. Half of the casting was destined to strength tests, the other half served to determination of an effect of vibrations on porosity of the alloy. The specimens were divided into 12 groups, depending on amplitude of vibrations and tilt angle of metal mould during pouring operation.
A numerical model of binary alloy crystallization, based on the cellular automaton technique, is presented. The model allows to follow the crystallization front movement and to generate the images of evolution of the dendritic structures during the solidification of a binary alloy. The mathematic description of the model takes into account the proceeding thermal, diffusive, and surface phenomena. There are presented the results of numerical simulations concerning the multi-dendritic growth of solid phase along with the accompanying changes in the alloying element concentration field during the solidification of Al + 5% wt. Mg alloy. The model structure of the solidified casting was achieved and compared with the actual structure of a die casting. The dendrite interaction was studied with respect to its influence on the generation and growth of the primary and secondary dendrite arms and on the evolution of solute segregation both in the liquid and in the solid state during the crystallization of the examined alloy. The morphology of a single, free-growing dendritic crystal was also modelled. The performed investigations and analyses allowed to state e.g. that the developed numerical model correctly describes the actual evolution of the dendritic structure under the non-equilibrium conditions and provides for obtaining the qualitatively correct results of simulation of the crystallization process.
In this paper crystallization studies of low-alloyed construction cast steel were presented for different additions of chromium, nickel and molybdenum modified with vanadium and titanium. Studies were conducted using developed TDA stand, which additionally enabled evaluation of cooling rate influence on crystallization process of investigated alloys.
Paper presents the results of studies on primary crystallization and wear resistance of high chromium cast iron inoculated with ferrotitanium intended for work in abrasive conditions. Primary crystallization was examined with use of TDA method, wear tests of the samples were conducted using the modified pin-on-disk method.
The article shows results of studies of primary crystallization and wear resistance of Cr-Ni-Mo cast steel intended for work in corrosive and abrasive conditions. The studies of primary crystallization were conducted with use of TDA method and modified tester allowing measurement casting cooling time influence on the cooling and crystallization curves of studied alloys. After heat treatment of examined cast steel wear tests of the samples were conducted on pin-on-disc type device.
The article is a case study of the steel milling ring casting of about 6 tonnes net weight. The casting has been cast in the steel foundry the authors have been cooperating with. The aim was to analyse the influence of the shape of the chills and the material which was used to make them on the casting crystallization process. To optimally design the chills the set of the computer simulation has been carried out with 3 chills’ shape versions and 3 material’s versions and the results have been compared with the technology being in use (no chills). The proposed chills were of different thermal conductivity from low to high. Their shapes were obviously dependant on the adjacent casting surface geometry but were the result of the attempt to optimise their effect with the minimum weight, too. The chills working efficiency was analysed jointly with the previously designed top feeders system. The following parameters have been chosen to compare their effectiveness and the crystallization process: time to complete solidification and so-called fed volume describing the casting feeding efficiency. The computer simulations have been carried out with use of MagmaSoft v. 5.2 software. Finally, the optimisation has led to 15% better steel yield thanks to 60% top feeders weight reduction and 40% shorter solidification time. The steel ring cast with use of such technology fulfil all quality criteria.
Paper describes the results of Fe80Si11B9 amorphous ribbon investigation after pulsed laser interference heating and conventional annealing. As a result of interference heating periodically placed laser heated microareas were obtained. Structure characterisation by scanning and transmission electron microscopy showed in case of laser heated samples presence of crystalline nanostructure in amorphous matrix. Microscopy observations showed significant difference in material structure after laser heating – nanograin structure, and material after annealing – dendritic structure. Magnetic force microscopy investigation showed expanded magnetic structure in laser heated microareas, while amorphous matrix did not give magnetic signal. Change of magnetic properties was examined by magnetic hysteresis loop measurement, which showed that the laser heating did not have a significant influence on soft magnetic properties.
This paper presents the effect of the temperature and hold time in the holding furnace of 226 silumin on the characteristic quantities of TDA curves. The temperature of phase transformations and the cooling rate were tested.It has been shown that increasing both the hold time and the temperature in the holdingfurnace cause the decreasethe end ofα+Al9Fe3Si2+β and α+Al2Cu+βternary eutectics crystallizationtemperature in the tested silumin. This is due to the fact an increase in amounts of impurities as a result of reacting theliquid alloy with the gases contained in the air.It has been shown, however, that examined technological factors ofthe metal preparation do not cause systematic changes in the cooling rate.
This paper shows how it is possible to obtain an ausferrite in compacted graphite iron (CGI) without heat treatment of castings. Vermicular graphite in cast iron was obtained using Inmold technology. Molybdenum was used as alloying additive at a concentration from 1.6 to 1.7% and copper at a concentration from 1 to 3%. It was shown that ausferrite could be obtained in CGI through the addition of molybdenum and copper in castings with a wall thickness of 3, 6, 12 and 24 mm. Thereby the expensive heat treatment of castings was eliminated. The investigation focuses on the influence of copper on the crystallization temperature of the graphite eutectic mixture in cast iron with the compacted graphite. It has been shown that copper increases the eutectic crystallization temperature in CGI. It presents how this element influences ausferrite microhardness as well as the hardness of the tested iron alloy. It has been shown that above-mentioned properties increases with increasing the copper concentration.
The paper presents the results of the research on the effect of copper on the crystallization process, microstructure and selected properties of the compacted graphite iron. Compacted graphite in cast iron was obtained using Inmold process. The study involved the cast iron containing copper at a concentration up to approximately 4%. The effect of copper on the temperature of the eutectic crystallization as well as the temperature of start and finish of the austenite transformation was given. It has been shown that copper increases the maximum temperature of the eutectic transformation approximately by 5C per 1% Cu, and the temperature of the this transformation finish approximately by 8C per 1% Cu. This element decreases the temperature of the austenite transformation start approximately by 5C per 1% Cu, and the finish of this transformation approximately by 6C per 1% Cu. It was found that in the microstructure of the compacted graphite iron containing about 3.8% Cu, there are still ferrite precipitations near the compacted graphite. The effect of copper on the hardness of cast iron and the pearlite microhardness was given. This stems from the high propensity to direct ferritization of this type of cast iron. It has been shown copper increases the hardness of compacted graphite iron both due to its pearlite forming action as well as because of the increase in the pearlite microhardness (up to approx. 3% Cu). The conducted studies have shown copper increases the hardness of the compacted graphite iron approximately by 35 HB per 1% Cu.
The article is focused on thermomechanical and plastic properties of two high-manganese TRIPLEX type steels with an internal marking 1043 and 1045. Tensile tests at ambient temperature and at a temperature interval 600°C to 1100°C were performed for these heats with a different chemical composition. After the samples having been ruptured, ductility was observed which was expressed by reduction of material after the tensile test. Then the stacking fault energy was calculated and dilatation of both high-manganese steels was measured. At ambient temperature (20°C), 1043 heat featured higher tensile strength by 66MPa than 1045 heat. Microhardness was higher by 8HV0,2 for 1045 steel than for 1043 steel (203HV0,2). At 20°C, ductility only differed by 3% for the both heats. Decrease of tensile properties occurred at higher temperatures of 600 up to 1100°C. This tensile properties decrease at high temperatures is evident for most of metals. The strength level difference of the both heats in the temperature range 20°C up to 1100°C corresponded to 83 MPa, while between 600°C and 1100°C the difference was only 18 MPa. In the temperature range 600°C to 800°C, a decrease in ductility values down to 14 % (1045 heat), or 22 % (1043 heat), was noticed. This decrease was accompanied with occurrence of complex Aluminium oxides in a superposition with detected AlN particles. Further ductility decrease was only noted for 1043 heat where higher occurrence of shrinkag porosity was observed which might have contributed to a slight decrease in reduction of area values in the temperature range 900°C to 1100°C, in contrast to 1045 heat matrix.
This paper describes the possibility of using very short periods of solution annealing in the heat treatment of unmodified hypoeutectic silumin alloy AlSi7Mg0,3 casted by method of casting with crystallization under pressure with forced convection (direct squeeze casting process). Castings prepared at different casting parameters were subjected to special heat treatment called SST (Silicon Spheroidization Treatment), which were originally used only for the modified silumin alloys to spheroidization of eutectic silicon. Temperature holding time in solution annealing of T6 heat treatment is limited in the SST process to only a few minutes. It was studied the effect of casting parameters and periods of solution annealing on ultimate strength, yield strength, and especially ductility that in the unmodified silumin alloy castings is relatively low.
The article presents results of studies of silicon – molybdenum cast iron (4.42% Si, 2.59% Mo and 2.48% C wt.-%) crystallization process. Metallographic analysis was carried out using SEM-scanning electron microscopy with the EDS system. In order to determine the phase composition, X-ray diffraction studies were performed. Thermo-Calc, a computer simulation program, was used to simulate the crystallization process. . The obtained data allowed to describe the effect of some elements on the crystallization process. The silicon phase of MnSi could not be identified during metallographic studies. Also, computer simulation of the crystallization process did not answer the question at which point the silicon phase of MnSi crystallizes in the tested alloy. Therefore, not all results obtained were linked to the registered crystallization process (TDA process). The EDS analysis revealed an unusual distribution of molybdenum in the microstructure of the sample, where it is clearly visible that the area enriched with this element is also the separation of spheroidal graphite. The possibility of occurrence of Mo-rich micro-areas found in graphite is considered. The case is debatable and difficult to resolve at this stage. Perhaps, at such a high concentration of molybdenum (2.59% Mo) in the alloy, conditions are created for simultaneously crystallization of graphite and molybdenum phases.
Particles of the Fe-Al type (less than 50 µm in diameter) were sprayed onto the 045 steel substrate by means of the detonation method. The TEM, SAED and EDX analyses revealed that the Fe-Al particles have been partially melted in the experiment of coating formation. Particle undergone melting even within about 80% of its volume. Therefore, solidification of the melted part of particles was expected. Solidification differed significantly due to a large range of chemical composition of applied particles (from 15 at.% Al up to 63 at.% Al). A single particle containing 63 at.% Al was subjected to the detailed analysis, only. The TEM / SAED techniques revealed in the solidified part of particle three sub-layers: an amorphous phase, A ε , periodically situated FeAl + Fe2Al5 phases, and a non-equilibrium phase, Nε . A hypothesis dealing with the inter-metallic phases formation in such a single particle of the nominal composition 0 N = 0.63 is presented. At first, the solid / liquid system is treated as an interconnection: substrate liquid nonmelted particle part / / . Therefore, it is suggested that the solidification occurs simultaneously in two directions: towards a substrate and towards a non-melted part of particle. The solidification mechanism is referred to the Fe-Al meta-stable phase diagram. It is shown that the melted part of particle solidifies rapidly according to the phase diagram of meta-stable equilibrium and at a significant deviation from the thermodynamic equilibrium.