Mechanical reclamation process of spent moulding sands generate large amounts dusts containing mainly rubbed spent binding agents and quartz dust. The amounts of post-reclamation dusts, depending of the reclamation system efficiency and reclaim dedusting system, can reach 5 -10% in relation to the total reclaimed moulding sand. This dust due to the high content of the organic substances is a threat to the environment and therefore requires the storage on landfills specially adapted for this type of waste. On the other hand, the presence of organic substances causes that these dusts have relatively high energy values that could be used. However, at present there is no coherent, environmentally friendly concept for the management of this type of dust. The paper presents the results of tests of thermal utilization the dusts (as a source of energy) were carried out at AGH University of Science and Technology. Thermal utilization of dusts was carried out in the co-burning with carbon carriers process or in individual burning (Patent PL 227878 B1 and patent application PL - 411 902).
The work presents the results of examinations concerning the influence of various amounts of home scrap additions on the porosity of castings made of MgAl9Zn1 alloy. The fraction of home scrap in the metal charge ranged from 0 to 100%. Castings were pressure cast by means of the hot-chamber pressure die casting machine under the industrial conditions in one of the domestic foundries. Additionally, for the purpose of comparison, the porosity of specimens cut out directly of the MgAl9Zn1 ingot alloy was also determined. The examinations consisted in the qualitative assessment of porosity by means of the optical microscopy and its quantitative determination by the method of weighting specimens in air and in water. It was found during the examination that the porosity of castings decreases with an increase in the home scrap fraction in the metal charge. The qualitative examinations confirmed the beneficial influence of the increased home scrap fraction on the porosity of castings. It was concluded that the reusing of home scrap in a foundry can be a good way of reduction of costs related to the production of pressure castings.
The work presents the results of examinations concerning the influence of various amounts of home scrap additions on the properties of castings made of MgAl9Zn1 alloy. The fraction of home scrap in the metal charge ranged from 0 to 100%. Castings were pressure cast by means of the hot-chamber pressure die casting machine under the industrial conditions in one of the domestic foundries. The examinations consisted in the determination of the following properties: tensile strength Rm, yield strength Rp0.2, and the unit elongation A5, all being measured during the static tensile test. Also, the hardness measurements were taken by the Brinell method. It was found that the mechanical properties (mainly the strength properties) are being improved up to the home scrap fraction of 50%. Their values were increased by about 30% over this range. Further rise in the home scrap content, however, brought a definite decrease in these properties. The unit elongation A5 exhibited continual decrease with an increase in the home scrap fraction in the metal charge. A large growth of hardness was noticed for the home scrap fraction increasing up to the value of 50%. Further increasing the home scrap percentage, however, did not result in a significant rise of the hardness value any more.