Casting covers major area of production all over the world. Resin bonded casting is widely used in today’s manufacturing industries. Furan No bake casting is most widely accepted in indian foundries due to its excellent surface finish and dimensional stability. It is a self-setting binder and it has a lower work and strip times. Though the casting process is also known as process of uncertainty, in the present study, an attempt has been made to investigate the effect of Grain Fineness Number, Loss of Ignition, Potential of Hydrogen, % of Resin with respect to sand, Sand Temperature and Compressive strength of the mould on Sand Inclusion defect – one of the most dominating defect in the Krislur Castomech Pvt. Ltd. Industry situated at Bhavnagar, Gujarat, India. The experiments were conducted based on response surface methodology (RSM) and sequential approach using face centered central composite design. The results show that quadratic model with removal of some insignificant term is comparatively best fits for Sand Inclusion Defect.
The results of investigations of spent moulding sands taken from the mould in which the metal core cooling system - to increase the cooling rate of the ladle casting - was applied, are presented in the hereby paper. The changes of the spent moulding sand at the casting external side being the result of degradation and destruction processes of organic binder, were analysed in this publication. Since the reclaimed material, obtained as a result of the mechanical reclamation of spent sands of the same type, is used as a grain matrix of the moulding sand, the amount of a binder left from the previous technological cycle is essential for the sound castings production. On the bases of investigations of the thermal analysis, ignition losses, dusts contents and pH values of the samples taken from the spent sand the conditions under which the process of gases displacing in the casting mould was realised as well as factors limiting the efficient mould degassing - were considered in this study. The possible reason of a periodical occurrence of an increased number of casting defects due to changing gas volume emission, being the reason of the realised technological process, was indicated.
In this article, there were presented results of research on influence of reclamation process on the ecological quality of reclaim sand with furan resin used in nonferrous foundry. The quality of reclaimed sand is mainly define by two group of chemical substances from elution of reclaimed sand: Dissolves Organic Carbon (DOC) and Total Dissolves Solids (TDS). Reclaimed sand used in test was prepared in experimental thermal reclaimer and mechanical vibration reclaimer REGMAS installed in Faculty of Foundry Engineering at University of Science and Technology in Krakow. The reference point is molding sand shaking out and crumble in jaw crusher. Test of elution was made in acreditation laboratory in Center For Research and Environmental Control in Katowice up to the standard with Dissolves Organic Carbon (DOC) - PN-EN 1484:1999; Total Dissolves Solids (TDS) - PN-EN 15216:2010. The standard for elution test is PN-EN 12457- 4:2006. Except that we were made loss of ignition test, to check how many resin was rest on sand grains.