The work presents the investigation results concerning the structure of composite pressure die castings with AlSi11 alloy matrix reinforced with SiC particles. Examination has been held for composites containing 10 and 20 volume percent of SiC particles. The arrangement of the reinforcing particles within the matrix has been qualitatively assessed in specimens cut out of the castings. The index of distribution was determined on the basis of particle count in elementary measuring fields. The tensile strength, the yield point and elongation of the obtained composite were measured. Composite castings were produced at various values of the piston velocity in the second stage of injection, diverse intensification pressure values, and various injection gate width values. The regression equation describing the change of the considered arrangement particles index and mechanical properties were found as a function of the pressure die casting parameters. The infuence of particle arrangement in composite matrix on mechanical properties these material was examined and the functions of correlations between values were obtained. The conclusion gives the analysis and the interpretation of the obtained results.
Wear resistance of TiC-cast steel metal matrix composite has been investigated. Composites were obtained with SHSB method known as SHS synthesis during casting. It has been shown the differences in wear between composite and base cast steel. The Miller slurry machine test were used to determine wear loss of the specimens. The slurry was composed of SiC and water. The worn surface of specimens after test, were studied by SEM. Experimental observation has shown that surface of composite zone is not homogenous and consist the matrix lakes. Microscopic observations revealed the long grooves with SiC particles indented in the base alloy area, and spalling pits in the composite area. Due to the presence of TiC carbides on composite layer, specimens with TiC reinforced cast steel exhibited higher abrasion resistance. The wear of TiC reinforced cast steel mechanism was initially by wearing of soft matrix and in second stage by polishing and spalling of TiC. Summary weight loss after 16hr test was 0,14÷0,23 g for composite specimens and 0,90 g for base steel