Abstract

The work determined the influence of aluminium in the amount from about 1% to about 7% on the graphite precipitates in cast iron with relatively high silicon content (3.4% to 3.90%) and low manganese content (about 0.1%). The cast iron was spheroidized with cerium mixture and graphitized with ferrosilicon. The performed treatment resulted in occurring of compact graphite precipitates, mainly nodular and vermicular, of various size. The following parameters were determined: the area percentage occupied by graphite, perimeters of graphite precipitates per unit area, and the number of graphite precipitates per unit area. The examinations were performed by means of computer image analyser, taking into account four classes of shape factor. It was found that as the aluminium content in cast iron increases from about 1.1% to about 3.4%, the number of graphite precipitates rises from about 700 to about 1000 per square mm. For higher Al content (4.2% to 6.8%) this number falls within the range of 1300 – 1500 precipitates/mm2 . The degree of cast iron spheroidization increases with an increase in aluminium content within the examined range, though when Al content exceeds about 2.8%, the area occupied by graphite decreases. The average size of graphite precipitates is equal to 11-15 μm in cast iron containing aluminium in the quantity from about 1.1% to about 3.4%, and for higher Al content it decreases to about 6 μm.
Go to article

Abstract

The paper presents an analysis of factors affecting the wear of cylinder liners. The effect of the graphite precipitation morphology on the cylinder liner wear mechanism is presented. Materials used to cast cylinder liners mounted in a number of engines have been examined for their conformity with requirements set out in applicable Polish industrial standard. A casting for a prototype cylinder liner has been made with a microstructure guaranteeing good service properties of the part.
Go to article

Abstract

In modern times, there are increasing requirements for products quality in every part of manufacturing industry and in foundry industry it is not different. That is why a lot of foundries are researching, how to effectively produce castings with high quality. This article is dealing with search of the influence of using different types of risers or chills on shrinkage cavity production in ductile iron castings. Differently shaped risers were designed using the Wlodawer´s modulus method and test castings were poured with and without combination of chills. Efficiency of used risers and chills was established by the area of created shrinkage cavity using the ultrasound nondestructive method. There are introduced the production process of test castings and results of ultrasound nondestructive reflective method. The object of this work is to determine an optimal type of riser or chill for given test casting in order to not use overrated risers and thus increase the cost effectiveness of the ductile iron castings production.
Go to article

Abstract

The paper proposes a methodology useful in verification of results of dilatometric tests aimed at determination of temperatures defining the start and the end of eutectoid transformation in the course of ductile cast iron cooling, based on quenching techniques and metallographic examination. For an industrial melt of ductile cast iron, the effect of the rate of cooling after austenitization at temperature 900°C carried out for 30 minutes on temperatures TAr1 start and TAr1 end was determined. The heating rates applied in the study were the same as the cooling rates and equaled 30, 60, 90, 150, and 300°C/h. It has been found that with increasing cooling rate, values of temperatures TAr1 start and TAr1 end decrease by several dozen degrees.
Go to article

Abstract

The paper presents the results of investigations of the growth of protective coating on the surface of ductile iron casting during the hot-dip galvanizing treatment. Ductile iron of the EN-GJS-600-3 grade was melted and two moulds made by different technologies were poured to obtain castings with different surface roughness parameters. After the determination of surface roughness, the hot-dip galvanizing treatment was carried out. Based on the results of investigations, the effect of casting surface roughness on the kinetics of the zinc coating growth was evaluated. It was found that surface roughness exerts an important effect on the thickness of produced zinc coating
Go to article

Abstract

The paper presents a solidification sequence of graphite eutectic cells of A and D types, as well as globular and cementite eutectics. The morphology of eutectic cells in cast iron, the equations for their growth and the distances between the graphite precipitations in A and D eutectic types were analyzed. It is observed a critical eutectic growth rate at which one type of eutectic transformed into another. A mathematical formula was derived that combined the maximum degree of undercooling, the cooling rate of cast iron, eutectic cell count and the eutectic growth rate. One type of eutectic structure turned smoothly into the other at a particular transition rate, transformation temperature and transformational eutectic cell count. Inoculation of cast iron increased the number of eutectic cells with flake graphite and the graphite nodule count in ductile iron, while reducing the undercooling. An increase in intensity of inoculation caused a smooth transition from a cementite eutectic structure to a mixture of cementite and D type eutectic structure, then to a mixture of D and A types of eutectics up to the presence of only the A type of eutectic structure. Moreover, the mechanism of inoculation of cast iron was studied.
Go to article

Abstract

The paper discusses the reasons for the current trend of substituting ductile iron castings by aluminum alloys castings. However, it has been shown that ductile iron is superior to aluminum alloys in many applications. In particular it has been demonstrated that is possible to produce thin wall wheel rim made of ductile iron without the development of chills, cold laps or misruns. In addition it has been shown that thin wall wheel rim made of ductile iron can have the same weight, and better mechanical properties, than their substitutes made of aluminum alloys.
Go to article

Abstract

The paper presents results of examination of material parameters of cast iron with structure obtained under rapid resolidification conditions carried out by means of the nanoindentation method.
Go to article

Abstract

Steel and cast-iron products, due to their low price and beneficial properties, are the most widely used among metals; their consumption has become an indicator of the economic development of countries. The characteristics of iron raw materials, in relation to current metallurgical requirements, are presented in the present this article. The globalization of the trade and development of steelmaking technologies have caused significant changes in the quality of raw materials in the last half-century forcing improvements in processing technologies. In many countries, standard concentrates (at least 60% Fe) are almost twice as rich as those processed in the mid-20th century. Methods of quality assessment have been improved and quality standards tightened. The quality requirements for the most important raw materials ‒ iron ores and concentrates, steel scrap, major alloy metals, coking coal, and coke, as well as gas and other energy media ‒ are reviewed in the present paper. Particular attention is paid to the quality testing methodology. The quality of many raw materials is evaluated multi-parametrically: both chemical and physical characteristics are important. Lower-quality parameters in raw materials equate to significantly lower prices obtained by suppliers in the market. The markets for these raw materials are diversified and governed by separate sets of newly introduced rules. Price benchmarks (e.g. for standard Australian metallurgical coal) or indices (for iron concentrates) apply. Some raw materials are quoted within the framework of the commodity market system (certain alloying components and steel scrap). The abandonment of the long-established system of multi-annual contracts has led to wide fluctuations in prices, which have reached a scale similar to that of other metals.
Go to article

Abstract

An attempt to summarize the primary iron raw materials and steel market’s hundred years history as well as influence of economic indicators on the iron ore deposit qualification for extraction has been undertaken in the paper. Steel products are crucial to the world economy, and their production has a major impact on the environment. The main factor is the huge scale of the production and growth rate, unprecedented among minerals. Iron ore and concentrates production has increased more than thirty times over the past century, and the geological resource base at the current level of consumption has provided almost 250 years of sufficiency. There have been tremendous changes in the world geography of the ore and steel industry. The iron ore mining industry is the driver of other economic activities (land transport, freight, metallurgy) and involves huge capital and human resources. The consumption of iron raw materials is also considered as an important indicator of the countries development and current or even future economic situation. Population growth remains one of the key stimulating factors. The prices of ore and iron concentrates depend on the quality of the raw material, delivery conditions, market balance and the weight of the ordered cargo. They are usually the subject of negotiations. In the past, they were long-term contracts, while short-term (yearly, quarterly) and current spot transactions are now significant. The prices of ores and concentrates in relation to steel prices are showing a strong correlation. The average iron content of the reserves has been reduced in the largest producers in the 21st century, however it does not translate into the quality of mining output. Exploitation of the richer parts of the mineral deposit is usually carried out. The high content of iron in the output is a response to the technological requirements of the metallurgy where the blast furnace charge should contain at least 56% Fe and 5–8% FeO. The current surplus of geological-mining supply (large resource base) justifies that a mineral deposit choice, destined for excavation, is economic profit maximization as well as social and environmental considerations.
Go to article

Abstract

The purpose of this paper is to focus on the loss separation of non-grain-oriented electrical steels used for speed-variable rotating electrical machines. The impact of laser-cutting, used in prototype manufacturing and of flux density harmonics, occurring locally in the lamination, on the loss distribution is studied in detail. Iron losses occurring under operation can physically be separated in different loss components. In this paper, a frequency-based loss model with parameters identified for single-sheet tester specimens, cut in strips of different widths, is therefore used. Moreover, a time-domain approach considers loss distributions occurring from higher harmonics. Hysteresis losses having high sensitivity to cut edge effects are calculated by the well-known Jiles-Atherton model adapting the frequency-based loss parameters. The model is validated by free-curve measurements at a single-sheet tester. It has been shown that the studied elliptical hysteresis model becomes inaccurate particularly for specimens with small strip widths with similar dimensions as teeth of electrical machine laminations. The incorrect mapping of losses occurring from minor hysteresis loops due to higher harmonics is concluded. The results showconsequently that both, the impact of a cut edge effect and local distributions of flux density harmonics need to be considered in terms of accurate iron loss prediction of electrical machine design.
Go to article

Abstract

In the research, relationships between matrix structure and hardness of high-quality Ni-Mn-Cu cast iron containing nodular graphite and nickel equivalent value were determined. Nickel equivalent values were dependent on chemical composition and differences between them resulted mostly from nickel concentration in individual alloys. Chemical compositions of the alloys were selected to obtain, in raw condition, austenitic and austenitic-martensitic cast iron. Next, stability of matrix of raw castings was determined by dilatometric tests. The results made it possible to determine influence of nickel equivalent on martensite transformation start and finish temperatures.
Go to article

Abstract

This paper deals with influence on segregation of iron based phases on the secondary alloy AlSi7Mg0.3 microstructure by chrome. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich phases. It is impossible to remove iron from melt by standard operations, but it is possible to eliminate its negative influence by addition some other elements that affect the segregation of intermetallics in less harmful type. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of chrome as iron corrector of iron based phases. By experimental work were used three different amounts of AlCr20 master alloy a three different temperature of chill mold. Our experimental work confirmed that chrome can be used as an iron corrector in Al-Si alloy, due to the change of intermetallic phases and shortening their length.
Go to article

Abstract

The excellent property combination of thin wall ductile iron castings (TWDI), including thin wall alloyed cast iron (e.g. austenitic TWDI) has opened new horizons for cast iron to replace steel castings and forgings in many engineering applications with considerable cost benefits. TWDI is considered as a potential material for the preparation of light castings with good mechanical and utility properties, the cost of which is relatively low. In this study, unalloyed and high Ni-alloyed (25% Ni) spheroidal graphite cast iron, with an austenitic metallic matrix were investigated. The research was conducted for thin-walled iron castings with 2, 3 and 5mm wall thickness, using different mould temperature (20°C, and 160°C) to achieve various cooling rates. The metallographic examinations i.e. characteristic of graphite nodules, metallic matrix, and primary grains of austenite dendrites (in high-nickel NTWDI) and mechanical properties were investigated. The study shows that homogeneity of the casting structure of thin-walled castings varies when changing the wall thickness and mould temperature. Finally, mechanical properties of thin-walled ductile iron castings with ferritic-pearlitic and austenitic metallic matrix have been shown.
Go to article

Abstract

Presence of iron in Al-Si cast alloys is common problem mainly in secondary (recycled) aluminium alloys. Better understanding of iron influence in this kind of alloys can lead to reduction of final castings cost. Presented article deals with examination of detrimental iron effect in AlSi10MgMn cast alloy. Microstructural analysis and ultimate tensile strength testing were used to consider influence of iron to microstructure and mechanical properties of selected alloy
Go to article

Abstract

This study presents an analysis of aluminium cast iron structure (as-cast condition) which are used in high temperatures. While producing casts of aluminium iron, the major influence has been to preserve the structure of the technological process parameters. The addition of V, Ti, Cr to an Fe-C-Al alloy leads to the improvement of functional and mechanical cast qualities. In this study, a method was investigated to eliminate the presence of undesirable Al4C3 phases in an aluminium cast iron structure and thereby improve the production process. V and Ti additions to aluminium cast iron allow the development of FeAl - VC or TiC alloys. In particular, V or Ti contents above 5 wt.% were found to totally eliminate the presence of Al4C3. In addition, preliminary work indicates that the alloy with the FeAl - VC or TiC structure reveals high oxidation resistance. The introduction of 5 wt.% chromium to aluminium cast iron strengthened the Al4C3 precipitate. Thus, the resultant alloy can be considered an intermetallic FeAl matrix strengthened by VC and TiC or modified Al4C3 reinforcements.
Go to article

Abstract

In the paper, a relationship between chemical composition of Ni-Mn-Cu cast iron and its structure, hardness and corrosion resistance is determined. The examinations showed a decrease of thermodynamic stability of austenite together with decreasing nickel equivalent value, in cast iron solidifying according to both the stable and the metastable systems. As a result of increasing degree of austenite transformation, the created martensite caused a significant hardness increase, accompanied by small decline of corrosion resistance. It was found at the same time that solidification way of the alloy and its matrix structure affect corrosion resista
Go to article

Abstract

Within the presented work, the effect of austenite transformation on abrasive wear as well as on rate and nature of corrosive destruction of spheroidal Ni-Mn-Cu cast iron was determined. Cast iron contained: 3.1÷3.4 %C, 2.1÷2.3 %Si, 2.3÷3.3 %Mn, 2.3÷2.5 %Cu and 4.8÷9.3 %Ni. At a higher degree of austenite transformation in the alloys with nickel equivalent below 16.0%, abrasive wear resistance was significantly higher. Examinations of the corrosion resistance were carried out with the use of gravimetric and potentiodynamic method. It was shown that higher degree of austenite transformation results in significantly higher abrasive wear resistance and slightly higher corrosion rate, as determined by the gravimetric method. However, results of potentiodynamic examinations showed creation of a smaller number of deep pinholes, which is a favourable phenomenon from the viewpoint of corrosion resistance.
Go to article

Abstract

This study discloses the characteristic features of the modified low-cycle fatigue test used for the determination of the mechanical properties of two types of cast iron, i.e. EN-GJL-250 and EN-GJS-600-3. For selected materials, metallographic studies were also conducted in the range of light microscopy and scanning microscopy.
Go to article

Abstract

In the family of iron-based alloys, ductile iron enjoys the highest rate of development, finding application in various industries. Ductile iron or the cast iron with spheroidal graphite can be manufactured by various methods. One of them is the Inmold spheroidization process characterized by different technological solutions, developed mainly to increase the process efficiency. So far, however, none of the solutions has been based on the use of a reactor made outside the casting mould cavity. The method of spheroidization inside the casting mould using a reaction chamber developed at the Foundry Research Institute is an innovative way of cast iron treatment. The innovative character of this method consists in the use of properly designed and manufactured reactor placed in the casting mould cavity. Owing to this solution, the Inmold process can be carried out in moulds with both horizontal and vertical parting plane. The study presents the results of examinations of the microstructure of graphite precipitates and metal matrix of castings after spheroidization carried out by the Inmold process using a reactor and mould with vertical parting plane. Special pattern assembly was made for the tests to reproduce plates with wall thicknesses of 3; 5; 7; 10; 20 and 30 mm. The content of residual magnesium was determined for all tested castings, while for castings of plates with a wall thickness equal to or larger than 10 mm, testing of mechanical properties was additionally performed.
Go to article

Abstract

Determined were direction and intensity of influence of alloying additions on the number of eutectic graphite colonies in austenitic cast iron Ni-Mn-Cu. Chemical composition of the cast iron was 1.7 to 3.3% C, 1.4 to 3.1% Si, 2.8 to 9.9% Ni, 0.4 to 7.7% Mn, 0 to 4.6% Cu, 0.14 to 0.16% P and 0.03 to 0.04% S. Analysed were structures of mottled (20 castings) and grey (20 castings) cast iron. Obtained were regression equations determining influence intensity of individual components on the number of graphite colonies per 1 cm2 (LK). It was found that, in spite of high total content of alloying elements in the examined cast iron, the element that mainly decides the LK value is carbon, like in a plain cast iron.
Go to article

Abstract

Metal alloys with matrix based on an Fe-Al system are generally considered materials for high-temperature applications. Their main advantages are compact crystallographic structure, long-range ordering and structural stability at high temperatures. These materials are based on an intermetallic phase of FeAl or Fe3Al, which is stable in the range from room temperature up to the melting point of 1240°C. Their application at high temperatures is also beneficial because of the low cost of production, very good resistance to oxidation and corrosion, and high mechanical strength. The casting alloy the structure of which includes the FeAl phase is, among others, highaluminium cast iron. This study has been devoted to the determination of the effect of vanadium and titanium on the transformation of the high-aluminium cast iron structure into an in-situ FeAl-VC composite.
Go to article

Abstract

The paper presents influence of soaking parameters (temperature and time) on structure and mechanical properties of spheroidal graphite nickel-manganese-copper cast iron, containing: 7.2% Ni, 2.6% Mn and 2.4% Cu. Raw castings showed austenitic structure and relatively low hardness (150 HBW) guaranteeing their good machinability. Heat treatment consisted in soaking the castings within 400 to 600°C for 2 to 10 hours followed by air-cooling. In most cases, soaking caused changes in structure and, in consequence, an increase of hardness in comparison to raw castings. The highest hardness and tensile strength was obtained after soaking at 550°C for 6 hours. At the same time, decrease of the parameters related to plasticity of cast iron (elongation and impact strength) was observed. This resulted from the fact that, in these conditions, the largest fraction of fine-acicular ferrite with relatively high hardness (490 HV0.1) was created in the matrix. At lower temperatures and after shorter soaking times, hardness and tensile strength were lower because of smaller degree of austenite transformation. At higher temperatures and after longer soaking times, fine-dispersive ferrite was produced. That resulted in slightly lower material hardness.
Go to article

Abstract

Production of spheroidal graphite cast iron is today quite mastered technology. There are many methods achieving the nodular graphite morphology. Each of these methods have specific characteristics and requirements to technical support, properties and the type of applied modifier. Selection of the spheroidization method is dependent on foundry disposition, production character, economic balance, quality requirements, etc. In case of centrifugally casting the core, which fills body and neck of the roll, is created by ductile iron. Considering the sophisticated production of centrifugally cast rolls for hot rolling mills it is necessary to ensure a high reproducibility and reliability of ductile cast iron production quality in the bulk range of 9-18 t per tapping. These conditions are in the Roll Foundry in Vítkovicke Slevarny, spol. s r.o. provided and verified mastered overpour method and the newly injection of cored wire in the melt.
Go to article

Abstract

This paper deals with influence on segregation of iron based phases on the secondary alloy AlSi7Mg0.3 microstructure by nickel. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich intermetallic phases. It is impossible to remove iron from melt by standard operations. Some elements eliminates iron by changing iron intermetallic phase morphology, decreasing its extent and by improving alloy properties. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of nickel as iron corrector of iron based phases.
Go to article