Abstract

In Al-Si alloy the iron is the most common impurity and with presence of other elements in alloy creates the intermetallic compounds, which decreases mechanical properties and increases of porosity. The cause of the negative effect of intermetallic particles on the mechanical properties is that it is more easily break off the tension load as the aluminium matrix or small particles of silicon. By adding suitable alloying elements, also known as iron correctors, is possible to reduce this harmful effect. In the article is evaluated influence of manganese on microstructure with performed EDX analysis selected intermetallic phases and tensile test and measurement of length of Al5FeSi phase. For realization experiments was used AlSi7Mg0.3 alloy with increased iron content. Manganese was added in the amount 0.3 wt. %, 0.6 wt. %, 0.8 wt.% and 1,2 wt. %. From performed measurements it has been concluded, that increased amount of manganese, i.e. Mn/Fe ratio, does not have significant influence on mechanical properties AlSi7Mg0.3 alloy in the melted state.
Go to article

Abstract

In this paper, the effect of changes the parameters of heat treatment on the structure and the degree of elements segregation was determined, in the context of corrosion resistance of ductile iron Ni-Mn-Cu, containing 7.2% Ni, 2.6% Mn and 2.4% Cu. In the condition after casting, castings of austenitic matrix and 160HBW hardness were obtained. The achieved castings were soaked at 450, 550 and 650°C for 4, 8 and 12 hours, then cooled down at the ambient air. In most cases, the heat treatment resulted in a change in the castings matrix, had the consequence of increasing their hardness in comparison to raw castings. Increasing the temperature and prolonging soaking time resulted in increasing the degree of transformation of austenite, while reducing the degree of elements segregation. This led to the formation of slightly bigger number of pitting due to corrosion, but not so deep and more evenly distributed in comparison to raw castings. Wherein the results of corrosion tests show that heat treatment of castings did not significantly change their corrosion resistance in comparison to raw castings, in contrast to the significant increase in mechanical properties.
Go to article

Abstract

The aim of this study is to design and implement a computer system, which will allow the semantic cataloging and data retrieval in the field of cast iron processing. The intention is to let the system architecture allow for consideration of data on various processing techniques based on the information available or searched by a potential user. This is achieved by separating the system code from the knowledge of the processing operations or from the chemical composition of the material being processed. This is made possible by the creation and subsequent use of formal knowledge representation in the form of ontology. So, any use of the system is associated with the use of ontologies, either as an aid for the cataloging of new data, or as an indication of restrictions imposed on the data which draw user attention. The use of formal knowledge representation also allows consideration of semantic meaning, a consequence of which may be, for example, returning all elements in subclasses of the searched process class or material grade.
Go to article

Abstract

The current work presents the research results of abrasion wear and adhesive wear at rubbing and liquid friction of new austenitic, austenitic-ferritic (“duplex”) cast steel and gray cast iron EN-GJL-250, spheroidal graphite iron EN-GJS-600-3, pearlitic with ledeburitic carbides and spheroidal graphite iron with ledeburitic carbides with a microstructure of the metal matrix: pearlitic, upper bainite, mixture of upper and lower bainite, martensitic with austenite, pearlitic-martensitic-bainitic-ausferritic obtained in the raw state. The wearing quality test was carried out on a specially designed and made bench. Resistance to abrasion wear was tested using sand paper P40. Resistance to adhesive wear was tested in interaction with steel C55 normalized, hardened and sulfonitrided. The liquid friction was obtained using CASTROL oil. It was stated that austenitic cast steel and “duplex” are characterized by a similar value of abrasion wear and adhesive wear at rubbing friction. The smallest decrease in mass was shown by the cast steel in interaction with the sulfonitrided steel C55. Austenitic cast steel and “duplex” in different combinations of friction pairs have a higher wear quality than gray cast iron EN-GJL250 and spheroidal graphite iron EN-GJS-600-3. Austenitic cast steel and “duplex” are characterized by a lower wearing quality than the spheroidal graphite iron with bainitic-martensitic microstructure. In the adhesive wear test using CASTROL oil the tested cast steels and cast irons showed a small mass decrease within the range of 1÷2 mg.
Go to article

Abstract

The paper presents the results of abrasive wear resistance tests carried out on high-vanadium cast iron with spheroidal VC carbides. The cast iron of eutectic composition was subjected to spheroidising treatment using magnesium master alloy. The tribological properties were examined for the base cast iron (W), for the cast iron subjected to spheroidising treatment (S) and for the abrasion-resistant steel (SH). Studies have shown that high-vanadium cast iron with both eutectic carbides and spheroidal carbides has the abrasion resistance twice as high as the abrasion-resistant cast steel. The spheroidisation of VC carbides did not change the abrasion resistance compared to the base high-vanadium grade.
Go to article

Abstract

The validation of each simulation code used in foundry domain requires individual approach due to its specificity. This validation can by elaborated on the basis of experimental results or in particular cases by comparison the simulation results from different codes. The article concerns the influence of grey cast iron density curve and different forms of solid fraction curve Fs=f(T) on the formation of shrinkage discontinuities. Solid fraction curves applying Newtonian Thermal Analysis (NTA) were estimated. The experimental and numerical simulation tests were performed on the castings, which were made with Derivative Thermal Analysis (DerTA) standard cups. The numerical tests were realized using NovaFlow&Solid (NF&S), ProCast and Vulcan codes. In this work, the coupled influence of both curves on the dynamics of the shrinkage-expansion phenomena and on shrinkage defects prognosis in grey cast iron castings has been revealed. The final evaluation of the simulation systems usefulness should be based on validation experiment, preceded by comparing the simulation results of available systems which are proposed in given technology.
Go to article

Abstract

Increasing demands on the utility properties of materials used for castings have led to the production of cast iron with a modified shape of graphite, where the required properties are achieved by a change in graphite shape, its size and layout, and a change in the basic structure of the metal. This paper is focused on the continuous method of producing spheroidal graphite FLOTRET. In the introductory section is summarized the theoretical foundations of the secondary treatment of cast irons, especially the FLOTRET flow method, describes the advantages and disadvantages of the method. The practical part is divided into laboratory and operational tests. Laboratory experiments were conducted on a laboratory-type modifier FLOTRET chamber, which was designed and hydraulically optimized. Experiments were focused on the effects of pressure altitude and amount of modifier on the residual values of magnesium, as conditions for a successful modification. The method was tested in two foundries under operating conditions and in one of them was observed a long-term modification process.
Go to article

Abstract

Reason for and risks of using of cast iron with vermicular graphite for typical construction parts. Ultrasound checking of graphite shape. Factors influencing plausibility of result. Difference between laboratory and operation application. Roughness, parallelism, stabilityand size dimension of walls. Conditions, proposals for simplification and productivity enhancement of castings checking. Recommendation.
Go to article

Abstract

The article contains the results of tests performed under the target project in Hardtop Foundry Charsznica. The objective of the tests and studies was to develop a technology of making high-quality ductile iron castings, combined with effective means of environmental protection. The studies presented in this article related to castings weighing from 1 to 300 kg made from ductile iron of grades 400-15 and 500-7, using two-layer moulds, where the facing and core sand was the sand with an alkaline organic binder, while backing sand was the sand with an inorganic geopolymer binder. A simplified method of sand reclamation was applied with possible reuse of the reclaim as an addition to the backing sand. The cast iron spheroidising treatment and inoculation were selected taking into account the specific conditions of Hardtop Foundry. A pilot batch of castings was made, testing the gating and feeding systems and using exothermic sleeves on risers. The study confirmed the validity of the adopted concept of making ductile iron castings in layer moulds, while maintaining the content of sand with an organic binder at a level of maximum 15%.
Go to article

Abstract

The paper presents data concerning the total production of castings over the 2000-2014 period, both on a global scale, and in Poland. The basic types of casting alloys were taken into account. Changes in the production volume and structure over the period of the analysed 15 years were pointed out with respect to countries leading in foundry production. The topmost position in the world foundry industry is held by China for several years (with almost 45% share in the foundry market), the second place is taken by India (with almost 9% share). A distinct reduction in the shares of the once significant producers of castings, such as USA, Japan, Germany, Russia, Italy, or France, was observed over the 2000-2014 period. Poland had a share of 1.16% in 2000, and of 1.02% in 2014. Comparing the detailed data concerning the years 2000 and 2014, one can see that the fractions of castings made of ductile iron, cast steel, aluminium alloys, or magnesium alloys increase on a global scale, while such alloys as grey cast iron or malleable are in decline.
Go to article

Abstract

The paper presents the results of tests on the spheroidising treatment of vanadium carbides VC done with magnesium master alloy and mischmetal. It has been proved that the introduction of magnesium master alloy to an Fe-C-V system of eutectic composition made 34% of carbides crystallise in the form of spheroids. Adding mischmetal to the base alloy melt caused 28% of the vanadium carbides crystallise as dendrites. In base alloy without the microstructure-modifying additives, vanadium carbides crystallised in the form of a branched fibrous eutectic skeleton. Testing of mechanical properties has proved that the spheroidising treatment of VC carbides in high-vanadium cast iron increases the tensile strength by about 60% and elongation 14 - 21 times, depending on the type of the spheroidising agent used. Tribological studies have shown that high-vanadium cast iron with eutectic, dendritic and spheroidal carbides has the abrasive wear resistance more than twice as high as the abrasion-resistant cast steel.
Go to article

Abstract

A research of wear resistance of an austenitic cast iron with higher resistance to abrasive-wear and maintained corrosion resistance characteristic for Ni-Resist cast iron is presented. For the examination, structure of raw castings was first formed by proper selection of chemical composition (to make machining possible). Next, a heat treatment was applied (annealing at 550 °C for 4 hours followed by air cooling) in order to increase abrasive-wear resistance. One of the factors deciding intensity of wear appeared to be the chilling degree of castings. However, with respect to unfavourable influence of chilling on machining properties, an important factor increasing abrasivewear resistance is transformation of austenite to acicular ferrite as a result of annealing non-chilled castings. Heat treatment of non-chilled austenitic cast iron (EquNi > 16%) resulted in much higher abrasive-wear resistance in comparison to the alloy having pearlitic matrix at ambient temperature (EquNi 5.4÷6.8%).
Go to article

Abstract

The study reported in this paper was aimed at establishing the effect of values of parameters characterizing the process of superficial remelting of a nodular iron casting on the quantity of introduced heat, geometry of remeltings as well as parameter λ and hardness of cementite eutectic. The remelting process was carried out using GTAW method, at electric arc length of 3 mm in argon atmosphere, welding current intensities I = 50, 130, 210, and 300 A, and electric arc scanning speeds vs = 200, 400, and 800 mm/min. The measurements included estimation of the quantity of heat introduced to the casting in the electric arc-induced remelting process with the use of flow calorimeter. Widths and depths of remetlings were assessed with the use of metallographic method. As a result of fast solidification, cementite eutectic was obtained in remelted material in which, in the course of cooling down to ambient temperature, austenite was subject to partial transformation into martensite. To characterize the cementite eutectic, value of the structural parameter λ was assessed. Values of the parameter were similar for areas of occurrence of both fibrous and laminated eutectic. Remeltings were examined at half of their depths. Micro-hardness measurements were taken in the same areas. The established quantitative relationships may prove to be useful in practice for the purpose of predicting values of parameter λ and hardness of remeltings in studies aimed at improving resistance of cast-iron castings to abrasive wear.
Go to article

Abstract

High-vanadium cast iron is the white cast iron in which the regular fibrous γ + VC eutectic with the volume fraction of vanadium carbide amounting to about 20% crystallises. This paper presents the results of studies on high-vanadium cast iron subjected to the inoculation treatment with magnesium master alloy. The aim of this operation is to change the morphology of the crystallising VC carbides from the fibrous shape into a spheroidal one. The study also examines the effect of the amount of the introduced inoculant on changes in the morphology of the crystallising VC carbides. To achieve the goals once set, metallographic studies were performed on high-vanadium cast iron of eutectic composition in base state and after the introduction of a variable content of the inoculant. The introduction of magnesium-based master alloy resulted in the expected changes of microstructure. The most beneficial effect was obtained with the introduction of 1.5% of magnesium master alloy, since nearly half of the crystallised vanadium carbides have acquired a spheroidal shape.
Go to article

Abstract

The work presents results of investigations concerning the production of cast iron containing about 5-6% aluminium, with the ferritic matrix in the as-cast state and nodular or vermicular graphite precipitates. The examined cast iron came from six melts produced under the laboratory conditions. It contained aluminium in the amount of 5.15% to 6.02% (carbon in the amount of 2.41% to 2.87%, silicon in the amount of 4.50% to 5.30%, and manganese in the amount of 0.12% to 0.14%). After its treatment with cerium mixture and graphitization with ferrosilicon (75% Si), only nodular and vermicular graphite precipitates were achieved in the examined cast iron. Moreover, it is possible to achieve the alloy of pure ferritic matrix, even after the spheroidizing treatment, when both the aluminium and the silicon occur in cast iron in amounts of about 5.2÷5.3%.
Go to article

Abstract

The modification is a widespread method of improving the strength properties of cast iron. The impact in terms of increasing amounts of eutectic grains has been thoroughly studied while the issue of the impact on the mechanical properties of primary austenite grains has not been studied in depth yet. The paper presents the study of both aspects. The methodology was to conduct the melting cast iron with flake graphite, then modifying the alloy by two sets of modifiers: the commercial modifier, and a mixture of iron powder with a commercial inoculant. The DAAS test was carried out to identify the primary austenite grains. The degree of supercooling was determined and the UTS test was performed as well. Additionally carried out the metallographic specimen allowing for counting grains. It can be concluded that the introduction of the iron powder significantly improved the number of austenite primary grains which resulted in an increase in tensile strength UTS.
Go to article

Abstract

In highly developed countries, a significant progress in the use of alternative and clean energy sources has recently been observed. The European Union has implemented a programme to build wind turbines. It is estimated that in the coming years, thanks to the support in tax and credit, the global energy will develop very intensively. Many components of the wind turbines are castings. The basic material used for these castings is ductile iron, which in this particular case must meet high requirements imposed by the operating conditions of wind turbines. Anticipating an increase in customer demand for this type of castings, Krakodlew SA has decided to modernize its foundry using the ability to obtain external financing. The ductile iron manufacturing technology is now being developed and adapted to the specific conditions of the foundry plant, including the melting process yielding cast material with the required chemical composition, the technology of moulding, and the conditions for possible secondary metallurgy, spheroidizing treatment and graphitizing inoculation. The fulfilment of the imposed conditions for the casting production demands the use of advanced casting technologies introduced to the manufacturing process. The development of technology to launch the production of ductile iron castings for the wind power industry was supported by The National Centre for Research and Development (NCBiR). This article presents part of research on the binding kinetics of furan resin sands and choice of their composition for moulds and cores to make heavy castings used as components of equipment for the wind power industry.
Go to article

Abstract

The growth kinetics of the zinc coating formed on the surface of casting made from ductile iron grade EN-GJS-500-3 was investigated. To produce homogenous metal matrix in test samples, the normalising and ferritising annealing was carried out. Studies showed a heterogeneous structure of cast iron with varying content of the phases formed. This was followed by hot dip galvanising treatment at 450°C to capture the growth kinetics of the zinc coating (the time of the treatment ranged from 60 to 600 seconds). Nonlinear estimation of the determined growth kinetics of the alloyed layer of a zinc coating was made and an equation of the zinc coating growth was derived. Based on the results of the investigations it was concluded that thickness of the zinc coating formed on the surface of casting with a 100% pearlitic matrix makes 55% of the thickness of coating formed on the surface in 100% ferritic.
Go to article

Abstract

The effectiveness of cast iron spheroidization with FeSiMg master alloy by the traditional method and using a reaction chamber placed in the cavity of foundry mould was compared. The method of cast iron treatment in mould cavity using a reaction chamber is an innovative technology developed by the Foundry Research Institute in Krakow. The effectiveness of the spheroidization process carried out by both methods was checked on a series of test castings. The article also presents the results of metallographic examinations and mechanical testing, including the discussion of magnesium yield and its assimilation rate.
Go to article

Abstract

The paper presents the effect of pre-heat treatment on the mechanical properties of ductile cast iron with elevated content of Cu and Mo elements. Austempered Ductile Iron is a material with non-standard properties, combining high tensile strength and abrasion resistance with very good plasticity. In addition, it is prone to strain hardening and have good machining abilities. The study was conducted for five designed heat treatment cycles. The variables were the time and temperature of the pre-heat treatment, followed by one of two standard heat treatments for ADI cast iron. The aim of the authors was fragmentation of the grains of perlite during the initial heat treatment. It is presumed, that subsequent heat treatment will cause further refinement of the microstructure than would be the case without initial heat treatment. Diffusion is much faster than in case of ferritic matrix of cast iron. The results will be used to evaluate material for the production of parts of equipment that must operate under extreme load conditions.
Go to article

Abstract

In this paper results of microsegregation in the newly developed nodular cast iron with carbides are presented. To investigate the pearlitic and bainitic cast iron with carbides obtained by Inmold method were chosen. The distribution of linear elements on the eutectic cell radius was examined. To investigate the microsegregation pearlitic and bainitic cast iron with carbides obtained by Inmold method were chosen. The linear distribution of elements on the eutectic cell radius was examined. Testing of the chemical composition of cast iron metal matrix components, including carbides were carried out. The change of graphitizing and anti-graphitizing element concentrations within eutectic cell was determined. It was found, that in cast iron containing Mo carbides crystallizing after austenite + graphite eutectic are Si enriched.
Go to article

Abstract

The contribution summarises the results of oxygen activity determinations, which were measured and registered continuously in castings from cast irons with various types of graphite. The results were used to find the relationship between two variables: natural logarithm of oxygen activities and reverse value of thermodynamic temperature 1 /T. Obtained regression lines were used to calculate oxygen activity at different temperatures, to calculate Gibbs free energy ΔG at the different temperatures and to calculate the single ΔG value for significant temperature of the graphite solidification. The results were processed by a statistical analysis of data files for the different types of graphite with flake, vermicular and spheroidal graphite. Each material has its proper typical oxygen activities range and individual temperature function of Gibbs free energy for analysing and governing casting quality.
Go to article

Abstract

High-chromium cast irons are used as abrasion resistant materials. Their wear resistance depends on quantity of carbides and the matrix supporting these carbides. The paper presents the results of cast irons of chemical composition (in wt. %) 19–22 Cr and 2–4.5 C alloyed by 1.7 Mo + 5 Ni + 2 Mn to improve their toughness, which were tested in working conditions of ferroalloys crushing. Tests showed that these as-cast chromium cast irons with mostly austenitic matrix achieved the hardness of 38-45 HRC, but their relative abrasion resistance Ψ ranged from 1.3 to 4.6, was higher comparing to the tool made from the X210Cr12 steel heat treated on hardness 61 HRC. The transformation of austenite into martensite occurs not only at the worn strained areas (on a surface of scratch) but also in their neighbourhood. Due to the work hardening of relatively large volumes of transformed austenite the cast iron possesses high abrasion resistance also on the surfaces where low pressures are acting. The tough abrasion-resistant cast iron well proved for production of dynamic and wear stressed castings e.g., crusher hammers, cutting tools for ceramic etc.
Go to article

Abstract

Constantly developing production process and high requirements concerning the quality of glass determine the need for continuous improvement of tools and equipment needed for its production. Such tools like forms, most often made of cast-iron, are characterized by thick wall thickness compared to their overall dimensions and work in difficult conditions such as heating of the surface layer, increase of thermal stresses resulting from the temperature gradient on the wall thickness, occurrence of thermal shock effect, resulting from cyclically changing temperatures during filling and emptying of the mould. There is no best and universal method for assessing how samples subjected to cyclic temperature changes behave. Research on thermal fatigue is a difficult issue, mainly due to the instability of this parameter, which depends on many factors, such as the temperature gradient in which the element works, the type of treatment and the chemical composition of the material. Important parameters for these materials are at high temperature resistance to thermal shock and thermal fatigue what will be presented in this paper.
Go to article

Abstract

The purpose of this paper is to develop a dynamic thermal model of a permanent magnet excited synchronous motor (PMSM). The model estimates the temperature at specific points of the machine during operation. The model is implemented using thermal network theory, whose parameters are determined by means of analytical approaches. Usually thermal models are initialized and referenced to room temperature. However, this can lead to incorrect results, if the simulations are performed when the electrical machine operates under “warm” conditions. An approach is developed and discussed in this paper, which captures the model in critical states of the machine. The model gives feedback by online measured quantities to estimate the initial temperature. The paper provides an extended dynamic thermal model, which leads to a more accurate and more efficient thermal estimation.
Go to article