The Legnica deposit is one of the most prospective in the context of future lignite mining. Its extraction will be inseparable from the removal of the rocks of the overburden, the volume of which is very large. Due to the raw material properties, some of the rocks can be classified as accompanying minerals. The raw material identification of overburden sediments in the Legnica lignite deposit is insufficient. So far, they haven’t been the subject of detailed and comprehensive research to prove their usefulness. The article was a summary of the knowledge on this subject. The following should be included in the accompanying minerals: Quaternary sands and gravels, tertiary sands and clays (Poznan clays). They are present in two colour variants in the Legnica deposit - and fiery. The mineral composition of greenish-blue clays allows them to be included in illite-kaolinite- smectite varieties, in turn fiery clays as kaolinite-illite-smectite varieties. The tertiary clays are a very useful raw material for the production of building materials. In addition, they are potential mineral sorbents due to the nature of the association of clay minerals (occurrence of montmorillonite). They also show suitability for building waterproofing barriers. Quaternary gravels and sands, developed in the overburden Legnica deposit are differentiated raw materials. Some of them are raw materials for the construction industry. The glacial tills can be used as a component of ceramic mixtures. Tertiary sands can be used as a proppant material. The information on the raw material properties of these sediments will be one of the essential criteria for their treatment as accompanying minerals. Minerals accompanying those developed in the Legnica deposit should be exploited and deposited selectively. The creation of anthropogenic deposits accumulating these minerals will provide the possibility of their use for decades after the termination of operation.
Peat soils (FAO — Gelic Histosols) in the southern Bellsund coast area occur on slopes and terraces. They are formed in places favourable for plant growth, i.e. adequately moistened and fertilized largely with bird excrements. These formations belong to moss peats which are generally decomposed weakly and moderately to about 0.5 m depth. Their content of organic matter is equal to about 30-90%, but it is higher in terrace peats. The latter are more acidified than slope peats. The reaction both of slope and terrace peat soils is as a rule, slightly acid or neutral, and CaC03 content does not exceed 10%. As regards the content of macroelements, that of Al is the highest followed by Ca, Fe, Mg and P. Little K and Ti, and only traces of Na are found. Microelements occur in the following sequence: Mn, Zn, Cu, Cr, Ni, Pb, Co, Cd. Particularly Mn, Zn as well as Cu and Cd were found in a higher concentration. Slope peat soils are richer in macro- and microelements than terrace ones, e.g. 4 times in the case of Mg. Peat soils poor in ash parts (up to 25% ash), contain the fewest elements. Some regularities concern also a vertical distribution of the particular profiles but only with regard to terrace peat soils.
For the purpose of making of a solid body of an electric guitar the acoustic- and mechanical properties of walnut- (Juglans regia L.) and ash wood (Fraxinus excelsior L.) were researched. The acoustic properties were determined in a flexural vibration response of laboratory conditioned wood elements of 430 × 186 × 42.8 mm used for making of a solid body of an electric guitar. The velocity of shearand compression ultrasonic waves was additionally determined in parallel small oriented samples of 80 × 40 × 40 mm. The research confirmed better mechanical properties of ash wood, that is, the larger modulus of elasticity and shear modules in all anatomical directions and planes. The acoustic quality of ash wood was better only in the basic vibration mode. Walnut was, on the other hand, lighter and more homogenous and had lower acoustic- and mechanical anisotropy. Additionally, reduced damping of walnut at higher vibration modes is assumed to have a positive impact on the vibration response of future modelled and built solid bodies of electric guitars. When choosing walnut wood, better energy transfer is expected at a similar string playing frequency and a structure resonance of the electric guitar.
The article is a review of the current theoretical achievements in the context of the discussion on the shape and validity of the property tax reform in Poland, indicated in the endogenous development of municipalities. The conclusions contained in the article are an attempt to join in a scientifi c discussion on the subject of property taxation. They constitute a proposal of formulated recommendations necessary from the point of view of legitimacy of collecting property taxes and the implementation of the new system of ad valorem tax.
The author claims that Marx’s ideas have succeeded, the proletariat has been victorious in the class conflict but the victory is completely different from what Marx has expected. The vision of the proletariat state ended up in a total failure. The vestiges of Marx’s proposal testify to complete inapplicability of his main ideas to the circumstances of the contemporary world. The concept of a state managed by the proletariat class turned out to be defective. The ownership of the means of production has failed. The concept of private property defended itself and has even been strengthened. And where a public ownership won the upper hand, as in State Treasury, it turned out to be institutional and not collective. Moreover, the state interferes more and more vigorously in private businesses and their activities. On the other hand, however, the proletariat succeeded in the area of employment law where it won some durable legal guarantees. Thus Marx correctly perceived certain needs of the proletariat but proposed inapt solutions to them.
The article is a part of materials regarding current problems of Polish science and higher education. It provides an in-depth analysis of the Act on degrees and academic titles as well as several other laws which introduce the so-called Ph.D. implementation in Poland. These laws were adopted by the Sejm of the Republic of Poland in April 2017. The author focuses on several problems, discussing them in separate chapters. The article also tries to predict the far-reaching results of the new rules. At the same time, the author proposes specific solutions that should be included in the future in the Act on degrees and academic titles, or in the Act of industrial property. They should eliminate the negative effects of conflicts between the provisions of various legal acts.
The petrographic composition of coal has a significant impact on its technological and sorption properties. That composition is most frequently determined by means of microscope quantitative analyses. Thus, aside from the purely scientific aspect, such measurements have an important practical application in the industrial usage of coal, as well as in issues related to the safety in underground mining facilities. The article discusses research aiming at analyzing the usefulness of selected parameters of a digital image description in the process of automatic identification of macerals of the inertinite group using neural networks. The description of the investigated images was based on statistical parameters determined on the basis of a histogram and co-occurrence matrix (Haralick parameters). Each of the studied macerals was described by means of a 20-element feature vector. An analysis of its principal components (PCA) was conducted, along with establishing the relationship between the number of the applied components and the effectiveness of the MLP network. Based on that, the optimum number of input variables for the investigated classification task was chosen, which resulted in reduction of the size of the network’s hidden layer. As part of the discussed research, the authors also analyzed the process of classification of macerals of the inertinite group using an algorithm based on a group of MLP networks, where each network possessed one output. As a result, average recognition effectiveness of 80.9% was obtained for a single MLP network, and of 93.6% for a group of neural networks. The obtained results indicate that it is possible to use the proposed methodology as a tool supporting microscopic analyses of coal.
Magnesium alloys thanks to their high specific strength have an extensive potential of the use in a number of industrial applications. The most important of them is the automobile industry in particular. Here it is possible to use this group of materials for great numbers of parts from elements in the car interior (steering wheels, seats, etc.), through exterior parts (wheels particularly of sporting models), up to driving (engine blocks) and gearbox mechanisms themselves. But the use of these alloys in the engine structure has its limitations as these parts are highly thermally stressed. But the commonly used magnesium alloys show rather fast decrease of strength properties with growing temperature of stressing them. This work is aimed at studying this properties both of alloys commonly used (of the Mg-Al-Zn, Mn type), and of that ones used in industrial manufacture in a limited extent (Mg-Al-Sr). These thermomechanical properties are further on complemented with the microstructure analysis with the aim of checking the metallurgical interventions (an effect of inoculation). From the studied materials the test castings were made from which the test bars for the tensile test were subsequently prepared. This test took place within the temperature range of 20°C – 300°C. Achieved results are summarized in the concluding part of the contribution.
Superparamagnetic iron oxide nanoparticles (SPION) synthesised chemically usually need the modification of the particle surface. Other natural sources of magnetic particles are various magnetotactic bacteria. Magnetosomes isolated from magnetotactic bacteria are organelles consisting of magnetite (Fe3O4) or greigite (Fe3S4) crystals enclosed by a biological membrane. Magnetotactic bacteria produce their magnetic particles in chains. The process of isolation of magnetosome chains from the body of bacteria consists of a series of cycles of centrifugation and magnetic decantation. Using a high-energy ultrasound it is possible to break the magnetosome chains into individual nanoparticles – magnetosomes. This study presents the effect of sonication of magnetosome suspension on their acoustic properties, that is speed and attenuation of the sound. Acoustic propagation parameters are measured using ultrasonic spectroscopy based on FFT spectral analysis of the received pulses. The speed and attenuation of ultrasonic waves in magnetosome suspensions are analysed as a function of frequency, temperature, magnetic field intensity, and the angle between the direction of the wave and the direction of the field.
The results of investigations of moulding sands with an inorganic binder called GEOPOL, developed by the SAND TEAM Company are presented in the paper. Hardeners of various hardening rates are used for moulding sands with this binder. The main aim of investigations was determination of the influence of the hardening rate of moulding sands with the GEOPOL binder on technological properties of these sands (bending strength, tensile strength, permeability and grindability). In addition, the final strength of moulding sands of the selected compositions was determined by two methods: by splitting strength and shear strength measurements. No essential influence of the hardening rate on such parameters as: permeability, grindability and final strength was found. However, the sand in which the slowest hardener (SA 72) were used, after 1 hour of holding, had the tensile and bending strength practically zero. Thus, the time needed for taking to pieces the mould made of such moulding sand will be 1.5 - 2 hours.
The investigation results of the influence of the reclaim additions on the properties of moulding sands with the GEOPOL geopolymer binder developed by the SAND TEAM Company were presented. Two brands of hardeners were applied in the tested compositions, the first one was developed by the SAND TEAM Company, marked SA72 and the new hardener offered by the KRATOS Company, marked KR72. The main purpose of investigations was to determine the influence of reclaim fractions and the applied hardener on the basic moulding sands properties, such as: bending and tensile strength, permeability and grindability. The unfavourable influence of the reclaim additions into moulding sands on the tested properties as well as an increased hardening rate, were found. Moulding sands, in which the hardener KR72 of the KRATOS Company was used, were less sensitive to the reclaim additions.
Among the copper based alloys, Cu-Al-X bronzes are commonly used as mold materials due to their superior physical and chemical properties. Mold materials suffer from both wear and corrosion, thus, it is necessary to know which one of the competitive phenomenon is dominant during the service conditions. In this study, tribo-corrosion behavior of CuAl10Ni5Fe4 and CuAl14Fe4Mn2Co alloys were studied and electrochemical measurements were carried out using three electrode system in 3.5 % NaCl solution in order to evaluate their corrosion resistance. In tribo-corrosion tests, alloys were tested against zirconia ball in 3.5 % NaCl solution, under 10N load with 0.04 m/s sliding speed during 300 and 600 m. The results indicate that (i) CuAl10Ni5Fe4 alloy is more resistant to NaCl solution compared to CuAl14Fe4Mn2Co alloy that has major galvanic cells within its matrix, (ii) although CuAl10Ni5Fe4 alloy has lower coefficient of friction value, it suffers from wear under dry sliding conditions, (iii) as the sliding distance increases, corrosion products on CuAl14Fe4Mn2Co surface increase at a higher rate compared to CuAl10Ni5Fe4 leading to a decrease in volume loss due to the lubricant effect of copper oxides.
Studies were carried out to determine the effect of heat treatment parameters on the plastic properties of unalloyed ausferritic ductile iron, such as the elongation and toughness at ambient temperature and at – 60 °C. The effect of austenitizing temperature (850, 900 and 950°C) and ausferritizing time (5 - 180 min.) at a temperature of 360°C was also discussed. The next step covered investigations of a relationship that is believed to exist between the temperature (270, 300, 330, 360 and 390 °C) and time (5, 10, 30, 60, 90, 120, 150, 180, 240 min.) of the austempering treatment and the mechanical properties of unalloyed ausferritic ductile iron, when the austenitizing temperature is 950°C. The “process window” was calculated for the ADI characterized by high toughness corresponding to the EN-GJS800-10-RT and EN-GJS-900-8 grades according to EN-PN 1564 and to other high-strength grades included in this standard. Low-alloyed cast iron with the nodular graphite is an excellent starting material for the technological design of all the ausferritic ductile iron grades included in the PN-EN-1624 standard. The examined cast iron is characterized by high mechanical properties stable within the entire range of heat treatment parameters.
Lead-free ceramics of Na0.5K0.5Nb1-xSbxO3 (NKNS) and Na0.5K0.5Nb1-xSbxO3 + 0.5 mol%MnO2 (NKNS + 0.5 mol%MnO2) (0 < x < 0.06) ceramics were prepared by a conventional solid-state hot pressing method. The ceramics possess a single-phase perovskite structure with orthorhombic symmetry. Microstructural examination revealed that Mn doping of NKNS leads to improvement of densification. The cubic-tetragonal and tetragonal-orthorhombic phase transitions of NKNS shifted to higher and lower temperature, respectively after introduction of Mn ion. Besides, ferroelectric and piezoelectric properties were improved. The results were discussed in term of difference in both ionic size and electronegativity of Nb5+ and Sb5+ and improvement of densification after Mn ion doping.
The multiple direct remelting of composites based on the A359 alloy reinforced with 20% of Al2O3 particles was performed. The results of both gravity casting and squeeze casting were examined in terms of the obtained microstructure and mechanical characteristics. In microstructure examinations, the combinatorial method based on phase quanta theory was used. In mechanical tests, the modified low cycle fatigue method (MLCF) was applied. The effects obtained after both gravity casting and squeeze casting were compared. It was noted that both characteristics were gradually deteriorating up to the tenth remelting. The main cause was the occurrence of shrinkage porosity after the gravity casting. Much better results were obtained applying the squeeze casting process. The results of microstructure examinations and fatigue tests enabled drawing the conclusion that the A359 alloy reinforced with Al2O3 particles can confer a much better fatigue life behavior to the resulting composite than the A359 alloy without the reinforcement. At the same time, comparing these results with the results of the previous own research carried out on the composites based also on the A359 alloy but reinforced in the whole volume with SiC particles, it has been concluded that both types of the composites can be subjected to multiple remelting without any significant deterioration of the structural and mechanical characteristics. The concepts and advantages of using the combinatorial and MLCF methods in materials research were also presented
This study offers a new method to synthesize facilely willemite (Zn2SiO4) based phosphor at the temperature of 800 °C. The ZnO-SiO2 nanocomposite was calcined at different temperatures between 500 and 1000 °C. The structural, morphological and optical properties of the nanocomposite obtained at various calcination temperatures were studied using different techniques. The FT-IR, XRD and the UV-vis result confirmed the formation of willemite phase. The precursor was confirmed to be amorphous by XRD at room temperature, but upon calcination temperature at 500 °C, it was transformed into a crystalline structure. The crystallinity and the particle size of the nanocomposite increase as the calcination temperature were increased as revealed by XRD and TEM measurement. The sample exhibits a spherical morphology from 500 to 800 °C and dumbbell-like morphology above 800 °C as shown by the FESEM images. The absorption spectrum suffers intense in lower temperature and tends to shift to lower wavelength in the UV region as the calcination temperature increases. The band gap values were found to be increasing from 3.228-5.550 eV obtained between 500 to 1000 °C, and all the results confirm the formation of willemite phase at 800 °C.
The results of studies presented in this article are an example of the research activity of the authors related to lead-free alloys. The studies covered binary SnZn90 and SnZn95 lead-free alloys, including their microstructure and complex mechanical characteristics. The microstructure was examined by both light microscopy (LM) and scanning electron microscopy (SEM). The identification of alloy chemical composition in micro-areas was performed by SEM/EDS method. As regards light microscopy, the assessment was of both qualitative and quantitative character. The determination of the geometrical parameters of microstructure was based on an original combinatorial method using phase quantum theory. Comprehensive characterization of mechanical behavior with a focus on fatigue life of alloys was performed by means of the original modified low cycle fatigue method (MLCF) adapted to the actually available test machine. The article discusses the fatigue life of binary SnZn90 and SnZn95 alloys in terms of their microstructure. Additionally, the benefits resulting from the use of the combinatorial method in microstructure examinations and MLCF test in the quick estimation of several mechanical parameters have been underlined.
This paper deals with computer modelling of the retention of a synthetic diamond particle in a metallic matrix produced by powder metallurgy. The analyzed sintered powders can be used as matrices for diamond impregnated tools. First, the behaviour of sintered cobalt powder was analyzed. The model of a diamond particle embedded in a metallic matrix was created using Abaqus software. The preliminary analysis was performed to determine the mechanical parameters that are independent of the shape of the crystal. The calculation results were compared with the experimental data. Next, sintered specimens obtained from two commercially available powder mixtures were studied. The aim of the investigations was to determine the influence of the mechanical and thermal parameters of the matrix materials on their retentive properties. The analysis indicated the mechanical parameters that are responsible for the retention of diamond particles in a matrix. These mechanical variables have been: the elastic energy of particle, the elastic energy of matrix and the radius of plastic zone around particle.
High-tin bronzes are used for church bells and concert bells (carillons). Therefore, beside their decorative value, they should also offer other functional properties, including their permanence and good quality of sound. The latter is highly influenced by the structure of bell material, i.e. mostly by the presence of internal porosity which interferes with vibration of the bell waist and rim, and therefore should be eliminated. The presented investigations concerning the influence of tin content ranging from 20 to 24 wt% on mechanical properties of high-tin bronzes allowed to prove the increase in hardness of these alloys with simultaneous decrease in the tensile and the impact strengths (Rm and KV, respectively) for the increased tin content. Fractures of examined specimens, their porosity and microstructures were also assessed to explain the observed regularities. A reason of the change in the values of mechanical properties was revealed to be the change in the shape of α-phase crystals from dendritic to acicular one, and generation of grain structure related to the increased Sn content in the alloy.
This work presents an influence of cooling rate on crystallization process, structure and mechanical properties of MCMgAl12Zn1 cast magnesium alloy. The experiments were performed using the novel Universal Metallurgical Simulator and Analyzer Platform. The apparatus enabled recording the temperature during refrigerate magnesium alloy with three different cooling rates, i.e. 0.6, 1.2 and 2.4°C/s and calculate a first derivative. Based on first derivative results, nucleation temperature, beginning of nucleation of eutectic and solidus temperature were described. It was fund that the formation temperatures of various thermal parameters, mechanical properties (hardness and ultimate compressive strength) and grain size are shifting with an increasing cooling rate.
Impact of surface and volume modification and double filtration during pouring the moulds on basic mechanical properties and creep resistance of nickel superalloys IN-713C and MAR-247 in conditions of accelerated creep of castings made of post-production scrap of these alloys is evaluated in this paper. The conditions of initiation and propagation of cracks in the specimens were analysed with consideration of stereological properties of material macro- and microstructure. It has been proven that in the conditions of hightemperature creep at 980°C and at stress σ = 150 MPa, creep resistance of superalloy MAR-247 is more than 10 times higher than the creep resistance of IN-713C alloy. In case of IN-713C alloy, the creep resistance negligibly depends on macrograin sizes. But, the macrograin size considerably affects the time to failure of specimens made of alloy MAR-247. Creep resistance of specimens made of coarse grain material was 20% higher than the resistance of fine grain materials.