Stable dispersion of antimony-doped tin oxide nano-powder was prepared by wet attrition process by comminuting aggregated ATO nano-powder using the titanate coupling agent as a dispersant to form the chemisorbed layer on the particle surface. The feed solution of the ATO dispersion and PVP was prepared for electro-spun fibers on the glass substrate. The surface resistance of the fibrous ATO film after electrospinning for 30 minutes was in the order of 105 Ω/□, which is sufficient for anti-static coating. The optical transmittance of ATO fibers was confirmed by measuring the visible light transmittance.

This paper presents the findings of fatigue strength tests of 15CrNi6 steel following low-pressure carburizing and oil quenching, subjected to cycles of one-sided three-point bending. The fatigue fractures were compared with the results of fatigue strength studies of 16MnCr5 steel following low-pressure carburizing and nitrogen quenching. The fatigue tests for 16MnCr5 steel were conducted as part of a high-cycle resonance test, with a pendular bending load. The study also involved an analysis of the effects on non-metallic inclusions in the structure on the mechanism of fatigue destruction. The inclusions were found to initiate fatigue cracks. In both cases, a similar method of a fatigue fissure initiation was observed, independent of the study method or specimen material.