Multiferroic six-layer Aurivillius type Bi7Fe3Ti3O21 ceramics was obtained by conventional mixed oxides method. The final sintering process was taken in several different sintering times, which determined changes in properties of discussed ceramic material. The structure and dielectric properties of the material are reported. In order to examine the technological conditions on the crystal structure, XRD analysis was carried out. The microstructure, as well as the quantitative and qualitative analysis of the chemical composition were investigated by scanning electron microscope with an energy dispersion spectrometer. The main purpose of the paper is to present the effect of sintering time on the microstructure, crystallographic structure and dielectric properties of Bi7Fe3Ti3O21 ceramics.
Aurivillius Bi5-xHoxTi3FeO15 (BHTFO) multiferroic ceramics with different holmium doping contents were synthesized by conventional solid state reaction. The effect of holmium doping on the microstructure, structural and dielectric behaviors of BHTFO ceramics were investigated in details. Microstructure and crystalline structure studies of ceramics were carried out at room temperature while dielectric properties were investigated in a wide range of temperature (T = 25ºC-550ºC) and frequency (20Hz-1MHz).
The paper reports the consequences of lanthanum modifications of barium bismuth niobiate (BaBi2Nb2O9) ceramics. The discussed materials were prepared by solid state synthesis and a one-step sintering process. The investigations are focused on dielectric aspects of the modification. The presented results reveal that the trivalent lanthanum ions incorporate twovalent barium ions, which is connected with the creation of A-site cationic vacancies as well as oxygen vacancies. Such a scenario results in significant decreasing in grain boundaries resistivity. The activation energy of grain boundaries conductivity is significantly reduced in the case of lanthanum admixture.
La0,7Ca0,3MnO3 polycrystalline were synthesized from La2O3, CaO and MnO2 powder mixture using a solid state reaction technique. The compound powders were obtained through the free sintering method at different temperatures and sintering times in order to study the influence of technological conditions on Ca doped La manganites. The most important physical features as structure, microstructure and morphology were described after X-ray diffraction investigation. Photographs of the specimen fractures were taken with SEM (scanning electron microscope) and they revealed high porosity of the tested material and great tendency for its grains to create agglomerates. Influence of doping and technological conditions on lattice parameters were studied by means of Rietvield analysis. The XRD measurements reveal that La0,7Ca0,3MnO3 has orthorhombic symmetry with Pnma space group.