The paper deals with the issue of potential for improvement of resistance of wood chip fine grinders to abrasive wear by providing them with WCCoCr coating applied with the use of atmospheric plasma spraying (APS). The study focused on establishing parameters of the technological process of spraying a 250–270 μm thick coating onto surface of ductile cast iron castings used to date as grinder linings. The presented data include results of microstructure examination, chemical composition analysis, HV hardness measurements, and scratch tests for both previous and new variant of linings. The obtained scratch test results indicate that the material of the coating is characterized with definitely lower susceptibility to scratching. The scratch made on coating was 75–84 μm wide and 7.2–8.2 μm deep, while the scratch on cast iron was distinctly wider (200–220 μm) and deeper (8.5–12.8 μm). In case of cast iron, the range of variability in scratch width and depth was definitely larger. This can be explained with large difference in hardness of individual components of microstructure of cast iron and significantly larger plastic deformation of cast iron compared to the coating revealed in the course of indenter motion over surfaces of the two materials. It has been found that application of WCCoCr coating offered better resistance of lining surfaces to scratching which can be considered a rationale for undertaking in-service tests.
A common problem encountered in hydraulic valves is a progressing deterioration of tightness of their water flow cutting-off seats. The seats are provided usually with a copper-alloy insert joined mechanically with cast-iron valve housing. The problem of unreliability of such joints can be solved by providing surface of the seat with a coating, deposited with the use of HVOF method and resistant to abrasive and cavitation wear. The tests were carried out for a sealing-draining seat insert made of CuZn39Pb2Al brass used to date and a specimen taken from the cast-iron valve housing which was the substrate for a plasma-sprayed coating of powder containing 86.1% Cr, 7.2% Ni, and 6.7% C. The coating, 345 ± 15 μm thick, was characterized with good quality of bonding with cast-iron substrate and high compactness of the material. The cavitation wear test on materials used in the study were carried out with the use of Vibra-Cell ultrasonic liquid processor (Sonics) equipped with a piezoelectric probe operating at the frequency of 20 kHz. Based on profilograms taken along a line crossing centers of cavitation craters, measurements of the height parameter Rt, and microscopic observations of surfaces it has been found that the coating plasma-sprayed onto substrate of nodular cast iron demonstrated higher resistance to cavitation compared to copper-alloy inserts used so far in cast-iron hydraulic valves. Cavitation craters on the material used typically for valve seats to date were more distinctly outlined and deeper compared to craters observed on the coating. Larger were also sizes of local tear-outs which resulted in larger difference between the peaks line and the valleys line.
The paper deals with susceptibility of nodular cast iron with ferritic -pearlitic matrix on cavitation erosion . Cavitation tests were carried out with the use of a cavitation erosion vibratory apparatus employing a vibration exciter operated at frequency of 20 kHz. The study allowed to determine the sequence of subsequent stages in which microstr ucture of cast iron in superficial regions is subject to degradation. The first features to be damaged are graphite precipitates. The ferritic matrix of the alloy turned out to be definitely less resistant to cavitation erosion compared to the pearlitic matrix component.
The present paper is a presentation of results of a study on morphology, chemical composition, material properties (HVIT, HIT, EIT), and nanoindentation elastic and plastic work for carbide precipitates in chromium cast iron containing 24% Cr. It has been found that the carbides differ in chemical composition, as well as in morphology and values characterizing their material properties. The carbides containing the most chromium which had the shape of thick and long needles were characterized with highest values of the analyzed material properties.