The present work has the objective of studying the effect of shot peening with glass microspheres on SAE 1020 steel in its resistance to fatigue. Fatigue tests were carried out by rotary bending with load control and loading on balance in specimens with and without shot peening. A rotation speed of approximately 750 rpm (12.5 Hz) was employed in the fatigue tests. Vickers microhardness tests were performed in order to verify the surface hardening produced by shot peening with glass microspheres. Analysis of the steel surface and fatigue fractures was performed using scanning electron microscopy (SEM). Fatigue tests were performed in order to obtain S-N curves (Wöhler curves). It was observed that shot peening with glass microspheres improved the fatigue strength of the steel at high cycle.

This work aims to analyze the effects of niobium on the bioactivity of a titanium, nickel, aluminum, and niobium alloy obtained by the Plasma Skull Push Pull process (PSPP). Titanium alloys, such as NiTinol (NiTi), are metallic biomaterials that have wide application in health and surgical prostheses. In this work the microstructural and bioactivity characteristics of the alloys are evaluated. The addition of aluminum improves alloy ductility and reduces its cost. The addition of niobium favors the hydroxyapatite nucleation. Therefore, the addition of the combination of the two elements contributes to lower cost and better alloy bioactivity.