The effect of combination grain refinement with AlTi5B1 master (55 ppm) and Sr-modification with AlSr5 master (20, 30, 40, 50 and 60 ppm) on the microstructure, tensile and hardness properties of AlSi7MgTi cast alloy were systematically investigated. Eutectic silicon was studied by optical and scanning electron microscopy after standard (0.5% HF) and deep etching (HCl). Morphology of eutectic Si changes from compact plate-like (as-cast state) to fibbers (after modification). Si-fibbers in samples with 50 and 60 ppm Sr coarsen probably as a result of over-modification. The optimum mechanical properties has the experimental material which was grain refined and modified with 40 ppm of Sr (UTS = 220.6 MPa; ductility = 6.1%, and 82.3 HBW 5/250/15).

The paper describes modification to Fm3–m (space group no. 225) lattice of aluminium based α-solid solution observed in Zn-Al alloys required to properly correlate quantitative data from X-ray diffraction analysis with results obtained from quantitative scanning electron microscopy image analysis and those predicted from Zn-Al binary phase diagram. Results suggests that 14 at.% of Zn as a solute atom should be introduced in crystal lattice of aluminium to obtain correct estimation of phase quantities determined by quantitative X-ray diffraction analysis. It was shown that this modification holds for Cu mould cast as well as annealed and water-cooled samples of Zn-3wt.%. Al and Zn-5wt.% Al.

The secondary aluminium alloys are very important material in actual industry from economic and ecological point of view. The secondary aluminium used for production of casts, however, contains some elements, i.e. iron, – affecting physical, chemical and mechanical behaviour. The subject of our investigation has been corrosion behaviour in natural atmosphere of the hypoeutectic AlSi7Mg0.3 cast alloys with various content of iron, because the Fe content affects not only mechanical properties but corrosion resistance, as well. Three types of the AlSi7Mg0.3 cast alloys were exposed for 9 months in natural atmosphere and the measure of their degradation by corrosion was found by determination of the weight loss and the light microscopy. In addition, a scanning electron microscopy (SEM) analyses and evaluation of surface changes were used. The corrosion behaviour in natural atmosphere was compared to results of the carried out electrochemical and exposure laboratory experiments in chloride solutions.