The work presents the results of examinations concerning the influence of various amounts of home scrap additions on the properties of

castings made of MgAl9Zn1 alloy. The fraction of home scrap in the metal charge ranged from 0 to 100%. Castings were pressure cast by

means of the hot-chamber pressure die casting machine under the industrial conditions in one of the domestic foundries. The examinations

consisted in the determination of the following properties: tensile strength Rm, yield strength Rp0.2, and the unit elongation A5, all being

measured during the static tensile test. Also, the hardness measurements were taken by the Brinell method. It was found that the

mechanical properties (mainly the strength properties) are being improved up to the home scrap fraction of 50%. Their values were

increased by about 30% over this range. Further rise in the home scrap content, however, brought a definite decrease in these properties.

The unit elongation A5 exhibited continual decrease with an increase in the home scrap fraction in the metal charge. A large growth of

hardness was noticed for the home scrap fraction increasing up to the value of 50%. Further increasing the home scrap percentage,

however, did not result in a significant rise of the hardness value any more.