In this research work, the Ti-6Al-4V material was used for the investigation of machining parameters by means of hybrid micro electrical discharge machining to improve the machining process and reduce the negative effects of debris accumulation in the drilled hole. L9 orthogonal array was used in the Taguchi based grey relational analysis to optimize the parameters such as material removal rate and diametrical accuracy of the machining process for Ti-6Al-4V. This work encompasses the design, development, and calibration of the work piece vibration platform and experimental analysis of the process parameters by means of the hybrid micro electrical discharge machining process. The maximum material removal rate and minimum surface roughness was observed at the current value of 2.5 A, pulse on time is 2 µs and pulse off time is 14.5 µs. The maximum material removal rate was observed for the increase in pulse on time with 14.4  µs and 4 A current level. The diametrical accuracy of the microholes was increased while increasing the pulse off time and decreasing the pulse on time. The fluid flow simulation has been conducted to find out the pressure drop and to know the velocity of the flow inside the hole for the effective flushing of the debris during machining.

Go to article

Authors and Affiliations

T. Mugilan
M.S. Aezhisai Vallavi
S. Santhosh
D. Sugumar
S. Christopher Ezhil Singh
Download PDF Download RIS Download Bibtex

Abstract

This research paper discusses the friction and wear behaviour of Al-12Si alloy reinforced with B4C prepared through Powder Metallurgy (P/M) method by varying the weight percentage of reinforcement (x = 2, 4, 6, 8, and 10) content. The samples were prepared by using die and punch assembly and the lubricant used to eject the sample from the die was molybdenum disulfide. The compaction was done by using a compression testing machine by applying a pressure of 800 MPa. The dry sliding friction and wear behaviour of the sample was conducted on a Pin-on-Disc machine and the experimental values of friction and wear were calibrated. The Taguchi design experiment was done by applying an L25 orthogonal array for 3 factors at 5 levels for the response parameter Coefficient of Friction (CoF) and wear loss. The SEM images show the shape, size and EDX confirm the existence of Al, Si, B4C particles in the composites. Analysis of Variance (ANOVA) for CoF of S/N ratio, shows that the reinforcement having 34.92% influence towards the S/N ratio of CoF, ANOVA for wear loss of S/N ratio shows that the sliding distance having 46.76% influence towards the S/N ratio of wear loss, when compared to that of the other two input parameters. The interaction line plot and the 2Dsurface plot for CoF and wear loss show that the increase in B4C content decreases the wear loss and CoF. The worn surface shows that the B4C addition will increase the wear resistance.

Go to article

Authors and Affiliations

R. Jeya Raj
W.A Lenin Anselm
M. Jinnah Sheik Mohamed
S. Christopher Ezhil Singh
T.D John
D. Rajeev
G. Glan Devadhas
K.G. Jaya Christyan
R. Malkiya Rasalin Prince
R.B. Jeen Robert

This page uses 'cookies'. Learn more