Abstract

The paper refers to pulverization and sintering of the (Fe80Nb6B14)0.88Tb0.12 high coercive alloy. The powder was sintered using the ultra-fast current aided method. It turned out that too long discharge time leads to appearing of a soft magnetic phase and simultaneously, decrease in coercivity of the compacted powder. Nevertheless, it was possible to establish preference technology parameters, preserving magnetic hardness of the alloy. As a final test, an impact of Co-powder addition on magnetic properties was studied. The introduced soft magnetic phase (about 20 wt. %) caused about 30% increase of magnetic remanence, which is a result of direct exchange interactions between the two phases.

Go to article

Authors and Affiliations

K. Granek
G. Ziółkowski
A. Chrobak
J. Klimontko
J. Rak
O. Zivotsky
L. Gembalova

This page uses 'cookies'. Learn more