This study manufactured a SiC coating layer using the vacuum kinetic spray process and investigated its microstructure and wear properties. SiC powder feedstock with a angular shape and average particle size of 37.4 μm was used to manufacture an SiC coating layer at room temperature in two different process conditions (with different degrees of vacuum). The thickness of the manufactured coating layers were approximately 82.4 μm and 129.4 μm, forming a very thick coating layers. The SiC coating layers consisted of α-SiC and β-SiC phases, which are identical to the feedstock. Cross-sectional observation confirmed that the SiC coating layer formed a dense structure. In order to investigate the wear properties, ball crater tests were performed. The wear test results confirmed that the SiC coating layer with the best wear resistance achieved approximately 4.16 times greater wear resistance compared to the Zr alloy. This study observed the wear surface of the vacuum kinetic sprayed SiC coating layer and identified its wear mechanism. In addition, the potential applications of the SiC coating layer manufactured using the new process were also discussed.

The microstructure and macroscopic properties of WC-50Ni+stellite 1(Co-Cr-W, ST1) coating layer fabricated by HVOF spray have been investigated. WC-50Ni powder and ST1 powders were mixed in the ratio of 1:0 and 5:5 wt.%, respectively. Argon heat treatment (Ar) and high-frequency heat treatment (H.F.) were conducted on the coating materials. WC was decomposed in the Ar heat treatment specimen, but decomposition of WC was not observed in the H.F. heat treatment specimen. Hardness was measured for as-sprayed WC-50Ni (821.5Hv) and as-sprayed WC-50Ni+ST1 (668.1 Hv). Hardness of Ar heat treatment specimen was reduced by about 14~18% than that of the as-sprayed coating layers. However, when the H.F. heat treatment was performed, the hardness inversely increased by about 6~10% than the as-sprayed coating layer. Based on these results, the method to improve the mechanical property of HVOF sprayed WC-50Ni+ST1 coating layer has also been also discussed.

Fe-Cr-B-based metamorphic alloy coating layers were manufactured by plasma spray with a Fe-Cr-B-Mo-Nb composition (hereinafter, M+) powder. The microstructure and wear properties of the coating layers were investigated and compared with a metamorphic alloy coating layer fabricated with commercial M material. XRD analysis revealed that the M and M+ coating layers were composed of α-Fe, (Cr, Fe)2B, and some metallic glass phases. Wear test results showed that M+ coating layers had a superior wear resistance which had 1.48 times lower wear volume than M coating layers. Observations of the worn-out surfaces and cross-sections of the coating layers showed that M+ coating layer had relatively low oxides along the particle boundaries and it suppress a delamination behavior by the oxides.