Increasing demands on the utility properties of materials used for castings have led to the production of cast iron with a modified shape of graphite, where the required properties are achieved by a change in graphite shape, its size and layout, and a change in the basic structure of the metal. This paper is focused on the continuous method of producing spheroidal graphite FLOTRET. In the introductory section is summarized the theoretical foundations of the secondary treatment of cast irons, especially the FLOTRET flow method, describes the advantages and disadvantages of the method. The practical part is divided into laboratory and operational tests. Laboratory experiments were conducted on a laboratory-type modifier FLOTRET chamber, which was designed and hydraulically optimized. Experiments were focused on the effects of pressure altitude and amount of modifier on the residual values of magnesium, as conditions for a successful modification. The method was tested in two foundries under operating conditions and in one of them was observed a long-term modification process.

The article will be focused on analysis of properties of aluminum alloy for the casting of type Al-Mg. As an experimental material was used aluminum alloy EN AC 51200, supplied in a cast state without a heat treatment. It was produced by the continuous casting method. Experiments deal with microstructural material analysis, fractographic analysis, mechanical and fatigue tests. The microstructure of the testing sample was examined using an optical microscope Neophot 32. Fatigue properties of aluminum alloy was tested by three-point bending cyclic loading. The fracture surface of the testing sample was examined using scanning electron microscopy (SEM), where sample was observed on various stages of the fatigue process, its characteristics and differences of fracture surfaces.