One of the elements of the Polish Energy Policy program is the development of renewable energy, including energy from biomass combustion. In Poland, the Green Block was built at the Połaniec Power Station fired with 100% biomass fuel. This solution is conducive not only to obtaining energy but also to improving environmental protection. During the combustion of biomass in a fluidized bed boiler, about 50 thousand tons of fly ash per year being a source of nutrients for plants, for example potassium salts, phosphorus, calcium, boron compounds, etc. was derived. The subject of the research were three types of ashes from biomass combustion containing 80% dendromass and 20% agromass. Agromas was made of straw, dried material or sliced palm nuts. The physical characteristics and chemical composition of three basic fly ash samples are presented. Due to the high fineness and thus dusting during spreading, it was found that there is no possibility of the direct use of fly ash from biomass combustion as an alkalizing agent for acidic soils. The lowest bulk density was demonstrated by samples of fly ash originating from the combustion of biomass containing 20% straw as agromass, while the poorest in potassium and phosphorus were ash samples obtained from the combustion of biomass containing 20% agromass in the form of palm kernel slate. As additional components, mineral acids as well as inorganic compounds, including industrial waste, were used to correct the chemical composition and to mineral fertilizer granulation. The number of introduced components was related to the postulated composition of the produced fertilizer. Examples of mineral fertilizers obtained, both simple and multicomponent fertilizers, are presented.

Due to the occurrence of zinc and lead ore deposits in dolomite rocks, the sphalerite concentrates obtained from these ores contain an admixture of dolomite. In practice, a substantial amount of magnesium included in zinc ores passes to the last production stage, i.e. zinc electrolysis. The magnesium present in electrolyte impairs electrical conductance and appears in the technical and economical indexes. This paper deals the attempts to remove magnesium removal from initial sphalerite concentrates by means of chemical flotation using spent electrolyte derived from zinc electrolysis. The authors attempt to substantiate the existing relationships, as well as to derermine the optimum conditions for the procedure suggested. The leaching efficiency of magnesium amounted to about 80%, and is dependent upon the stage of the leaching. Losses of zinc were below 2%, and the magnesium concentration in solution amounted to about 20%. These solution can produce magnesium and zinc, which will be presented in the following paper.

The aim of the work was to draw attention to the usefulness of the alkaline thermal activation process with sodium hydroxide in the process of rare earth metal leaching (REE), from fly ash with hydrochloric acid and nitric acid(V). The work is a part of the authors’ own research aimed at optimizing the REE recovery process coming from fly ash from hard coal combustion.

The article contains an assessment of the possibility of leaching rare earth metals (REE) from fly ash originating from the combustion of hard coal in one of the Polish power plants. The process was carried out for various samples consisting of fly ash and sodium hydroxide and for different temperatures and reaction times. The process was carried out for samples consisting of fly ash and sodium hydroxide containing respectively 10, 20 and 30% on NaOH by weight in relation to the weight of fly ash. Homogenization of these mixtures was carried out wet, and then they were baked at 408K, 433K and 473K, for a period of three hours. The mixture thus obtained was ground to a particle size of less than 0.1 mm and washed with hot water to remove excessive NaOH. The solid post-reaction residue was digested in concentrated HCl at 373K for 1 hour at a weight ratio fs/fc of 1:10. The results of chemical analysis and scanning microscopic analysis along with EDS analysis and X-ray analysis were used to characterize the physicochemical properties of the tested material.

The results indicated that REE recovery from fly ash strictly depends on heat treatment temperature with NaOH, and an increase in REE recovery from alkaline-activated fly ash along with increasing the amount of NaOH in relation to fly ash mass.