Neodymium-Iron-Boron (Nd-Fe-B) magnets are considered to have the highest energy density, and their applications include electric motors, generators, hard disc drives, and MRI. It is well known that a fiber structure with a high aspect ratio and the large specific surface area has the potential to overcome the limitations, such as inhomogeneous structures and the difficulty in alignment of easy axis, associated with such magnets obtained by conventional methods. In this work, a suitable heat-treatment procedure based on single-step and multistep treatments to synthesize sound electrospun Nd-Fe-B-O nanofibers of Φ572 nm was investigated. The single-step heat-treated (directly heat-treated at 800°C for 2 h in air) samples disintegrated along with the residual organic compounds, whereas the multistep heat-treated (sequential three-step heat-treated including three steps;: dehydration (250°C for 30 min in an inert atmosphere), debinding (650°C for 30 min in air), and calcination (800°C for 1 h in air)) fibers maintained sound fibrous morphology without any organic impurities. They could maintain such fibrous morphologies during the dehydration and debinding steps because of the relatively low internal pressures of water vapor and polymer, respectively. In addition, the NdFeO3 alloying phase was dominant in the multistep heat-treated fibers due to the removal of barriers to mass transfer in the interparticles.

In this study, precisely controlled large scale gas atomization process was applied to produce spherical and uniform shaped high entropy alloy powder. The gas atomization process was carried out to fabricate CoCrFeNiMn alloy, which was studied for high ductility and mechanical properties at low temperatures. It was confirmed that the mass scale, single phase, equiatomic, and high purity spherical high entropy alloy powder was produced by gas atomization process. The powder was sintered by spark plasma sintering process with various sintering conditions, and mechanical properties were characterized. Through this research, we have developed a mass production process of high quality and spherical high entropy alloy powder, and it is expected to expand applications of this high entropy alloy into fields such as powder injection molding and 3D printing for complex shaped components.

In this study, we demonstrate a facile and cost-effective way to synthesize Nd-Fe-B of various shapes such as powders, rods and fibers using electrospinning, heat-treatment and washing procedures. Initially Nd-Fe-B fibers were fabricated using electrospinning. The as-spun Nd-Fe-B fibers had diameters ranging 489 to 630 nm depending on the PVP concentration in reaction solutions. The different morphologies of the Nd2Fe14B magnetic materials were related to the difference in thickness of the as-spun fibers. The relationships between the as-spun fiber thickness, the final morphology, and magnetic properties were briefly elucidated. The intrinsic coercivity of Nd2Fe14B changed with the change in morphology from powder (3908 Oe) to fiber (4622 Oe). This work demonstrates the effect of the Nd-Fe-B magnetic properties with morphology and can be extended to the experimental design of other magnetic materials.