The properties of expansive concretes made of two types of cement: Portland cement CEM I and blast furnace slag cement CEM III were tested. The expansion of the concrete was caused by using an expansive admixture containing aluminium powder added in an amount of 0.5; 1 and 1.5% of cement mass. It was found that the compressive strength of concrete with CEM I decreased after using an expansive admixture in the amount of more than 0.5% of the cement mass. The compressive strength of concrete with CEM III decrease after addition of admixture in the entire range of dosages used. On the basis of electrochemical measurements, it was found no influence of an expansive admixture on corrosion of reinforcing steel. The use of an expansive admixture causes a slight increase in the effective diffusion coefficient of chloride ions in concrete.

The subject of the article is a comparison of two types of concrete carbonation models: self-limited carbonation and infinite carbonation. The results of the research on the progress of carbonation during six years of sample exposure in natural atmospheric conditions were used to determine the detailed models for a set of concretes with different w/c and different types of cement, and two scenarios of initial curing. It has been established that the model of self-limiting carbonation (i.e. hyperbolic) is more adequate for describing laboratory tests results in natural conditions.