The paper describes the influence of graphite shape, size and amount to electrical properties of different cast irons. Experiments of electrical resistivity measurements were conducted during solidification of four different melts in different time intervals from melt treatment by inoculation and nodularization. Metallographic analyses were made in order to determine the shape, size, distribution and amount of graphite and correlate results with electrical resistivity measurements. It was found out that nodular graphite is giving the lowest electrical resistivity and is decreased during solidification. Electrical resistivity of lamellar cast iron is increased during solidification since lamellas interrupt metal matrix severely There is no significant difference in resistivity of vermicular cast iron from nodular cast iron. Smaller size of graphite and lower amount of graphite and higher amount of metal matrix also decrease resistivity.

Chunky graphite has been recognized for a long time as one of the major problems in production of heavy section nodular cast iron. A great number of studies have been conducted to describe the chunky graphite formation, but a clear understanding of its appearance and a safe mastering of the melt preparation to avoid chunky graphite are not yet available. In the present work the cooling curves were recorded in large cone blocks and standard TA cup. According to measured data from the cone block, melt characteristics and heat transfer coefficient between casting and mould were adjusted in the ProCAST® simulation software. For a near-eutectic nodular cast iron test melt with 0.7 wt. % Ni, relationship between the area of the cone block affected by chunky graphite and simulation software results has been observed, i.e., thermal modulus and time to solidus.