In this study, we investigate the mechanical behavior of each skin layer, in terms of the nominal stress-strain curve by uniaxial tensile tests using specimens of porcine skin in two forms: dermis containing epidermis, and all three layers. All tests were performed under cyclic loading at the constant strain rate of 10–3 s–1 at ambient temperature. To measure the precise initial cross-sectional areas of each layer, the thickness of each skin layer was quantified by counting the number of pixels on the photo-image using image-processing software. In the tensile test, force-strain curves of the total skin and dermis with epidermis were obtained. Subsequently, a rule of mixtures was applied to determine the nonlinear mechanical properties of the hypodermis layer. In conclusion, we could define the uniaxial tensile behavior of the hypodermis, and additionally predict the weight effect of the dermis and hypodermis layers in the tensile test.

439L stainless steel composites blended with fifteen micron SiC particles were prepared by uniaxial pressing of raw powders at 100 MPa and conventional sintering at 1350oC for 2 h. Based on the results of X-ray diffraction analysis, dissolution of SiC particles were apparent. The 5 vol% SiC specimen demonstrated maximal densification (91.5%) among prepared specimens ­(0-10 vol% SiC); the relative density was higher than the specimens in the literature (80-84%) prepared by a similar process but at a higher forming pressure (700 MPa). The stress-strain curve and yield strength were also maximal at the 5 vol% of SiC, indicating that densification is the most important parameter determining the mechanical property. The added SiC particles in this study did not serve as the reinforcement phase for the 439L steel matrix but as a liquid-phase-sintering agent for facilitating densification, which eventually improved the mechanical property of the sintered product.