Foundry technologists use their own style of gating system designing. Most of their patterns are caused by experience. The designs differ from plant to plant and give better or worse results. This shows that the theory of gating systems is not brought into general use sufficiently and therefore not applied in practise very often. Hence, this paper describes the theory and practical development of one part of gating systems - sprue base for automated horizontal moulding lines used for iron castings. Different geometries of sprue bases with gating system and casting were drawn in Solid Edge ST9. The metal flow through the gating systems was then simulated with use of MAGMA Express 5.3.1.0, and the results were achieved. The quality of flow was considered in a few categories: splashes, air entrapment, vortex generation and air contact. The economical aspect (weight of runner) was also taken under consideration. After quantitative evaluation, the best shape was chosen and optimised in other simulations with special attention on its impact on filling velocity and mould erosion. This design (a sprue base with notch placed in drag and cope) is recommended to be used in mass production iron foundries to reduce oxide creation in liquid metal and especially to still metal stream to improve filtration.

The subject of this paper was to compare the influence of selected coatings on bending strength of moulds and cores manufactured in a furan technology. In a range of study, there were used three kinds of coatings - water based coating and two kind of alcohol based coating manufactured by FOSECO. Coating were applicated by brush, overpouring/flow and spraying. For each application method, there were realized different kind of drying- at ambient temperature, in a furnace and by burning. Physicochemical properties of coatings were such selected to accommodate them to the application method and type of coating. Based on the conducted studies it was observed that for water based coating application method doesn’t have an important influence on bending strength and it is necessary to optimize the time and temperature of drying to achieve better results of bending strength. For alcohol based coatings, drying by burning causes significant deterioration of bending strength of the mould and core and drying process at ambient allows to obtain high bending strength of mould/cores in regard to time of drying.