Steel slag stone can be used as a substitute for coarse aggregate in concrete. In this study, the performance of steel slag concrete (SSC) in the wall brick structure was analyzed. The specimens with a steel slag replacement rate of 0%, 20%, 25%, 30%, 35%, 40%, 45%, and 50% were designed, and the slump, stability, and carbonation resistance were tested. The results showed that the slump decreased with the increase of the replacement rate of steel slag stone. At the 60th min, the slump of SSC50 was 74 mm, which was 25.25% smaller than SSC00. When the replacement rate was more than 30%, cracks or fractures appeared, and the stability was destroyed. Twenty-eight days after the carbonation experiment, with the increase of the replacement rate, the carbonation resistance of the specimen decreased, and the performance was best when the replacement rate was 25%. The experimental results show that the performance of SSC is the best when the replacement rate of steel slag stone is 25%, which can be further promoted and applied in practice.

The strength of recycled aggregate (RA) is low, which makes the performance of recycled aggregate concrete (RAC) poor, and the addition of fiber can make up for the shortcoming of RAC. In this paper, the mechanical properties of RAC which was added with steel fiber were studied. The specimens with RA content of 0%, 40%, 70% 100% and steel fiber content of 0%, 0.5% and 1% were prepared, and their mechanical properties were tested. The results showed that the slump reduced 73.75% after the addition of 100% RA and 37.5% after the addition of 1% steel fiber compared to R0S0; from the perspective of mechanical properties, the larger the content of steel fiber, the better the mechanical properties of the specimen; the improvement of the tensile strength was the most obvious after the addition of steel fiber. The experimental results show that steel fiber can improve the performance of RAC and make it perform better in practical application.