The aim of this paper is to evaluate the fatigue resistance of austenitic nodular cast iron and to compare it with other types of nodular cast irons. The austenitic nodular cast iron, used for the experiments, was alloyed by 13% nickel and 7% manganese (EN-GJSA-XNiMn13-7) to obtain an austenitic matrix. The microstructure was studied using light metallographic microscopy. Mechanical properties were investigated by tensile test, impact bending test and Brinell hardness test. Fatigue tests were carried out at sinusoidal cyclic push-pull loading at ambient temperature. The results of fatigue tests were compared with the fatigue properties of ferrite-pearlitic nodular cast iron and pearlite-ferritic nodular cast iron. Experimental results show that NiMn-type of austenitic nodular cast iron has lower tensile strength and hardness, but higher elongation and absorbed energy than the compared types of nodular cast iron. However, austenitic nodular cast iron has lower fatigue limit.

The article will be focused on analysis of properties of aluminum alloy for the casting of type Al-Mg. As an experimental material was used aluminum alloy EN AC 51200, supplied in a cast state without a heat treatment. It was produced by the continuous casting method. Experiments deal with microstructural material analysis, fractographic analysis, mechanical and fatigue tests. The microstructure of the testing sample was examined using an optical microscope Neophot 32. Fatigue properties of aluminum alloy was tested by three-point bending cyclic loading. The fracture surface of the testing sample was examined using scanning electron microscopy (SEM), where sample was observed on various stages of the fatigue process, its characteristics and differences of fracture surfaces.