Removal of mercury(II) (Hg(II)) from aqueous media by a new biosorbent was carried out. Natural Polyporus squamosus fungus, which according to the literature has not been used for the purpose of Hg(II) biosorption before, was utilized as a low-cost biosorbent, and the biosorption conditions were analyzed by response surface methodology (RSM). Medium parameters which were expected to affect the biosorption of Hg(II) were determined to be initial pH, initial Hg(II) concentration (Co), temperature (T (°C)), and contact time (min). All experiments were carried out in a batch system using 250 mL fl asks containing 100 mL solution with a magnetic stirrer. The Hg(II) concentrations remaining in fi ltration solutions after biosorption were analyzed using Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES). Based on the RSM results, the optimal conditions were found to be 5.30, 47.39 mg/L, 20°C and 254.9 min for pH, Co, T (°C), and contact time, respectively. Under these optimal conditions, the maximum biosorbed amount and the biosorption yield were calculated to be 3.54 mg/g and 35.37%, respectively. This result was confi rmed by experiments. This result shows that Polyporus squamosus has a specifi c affi nity for Hg ions. Under optimal conditions, by increasing the amount of Polyporus squamosus used, it can be concluded that all Hg ions will be removed
In the present paper, elemental Fe, Cr and Ni powders were used to fabricate nano-structured duplex and ferritic stainless steel powders by using high energy planetary ball milling. We have studied the effect of milling atmosphere like wet (toluene) and dry (argon) milling of elemental Fe-18Cr-13Ni (duplex) and Fe-17Cr-1Ni (ferritic) powders for 10 h in a dual drive planetary mill. Stearic acid of 1wt. % was added during milling to avoid agglomeration. The dry and wet milled duplex and ferritic stainless steel powders were characterized by XRD, SEM and particle size analysis techniques. We have found that both the milling atmospheres have great influence in controlling the final particle morphology, size and phase evolution during milling. It was reported that dry milling is more effective in reducing particle size than the wet milling. The Nelson-Riley method of extrapolation was used to calculate the precise lattice parameter and Williamson-Hall method was used to calculate the crystallite size and lattice strain of both the stainless steel milled in argon atmosphere. Dry milled duplex and ferritic stainless steel were then consolidated by conventional sintering method at 1100, 1200 and 1300°C temperatures under argon atmosphere for 1 hour.